Abstract
Hydrated calcium zincate was synthesized by mechanical ball milling of ZnO and Ca(OH)2 in water at room temperature. The structural and electrochemical properties of this material used as rechargeable anodic material were examined by microelectrode voltammetry, charge–discharge measurements and structural analysis. The results showed that during mechanical milling, ZnO, Ca(OH)2 and H2O reacted rapidly to form Ca[Zn(OH)3]2 · 2H2O which was subsequently transformed to a stable structure CaZn2(OH)6 · 2H2O. Since this composite oxide has lower solubility in KOH solution (<35 wt %) and better electrochemical reversibility than ZnO-based negative materials, the zinc anodes using this material can overcome the problems of shape changes and dendritc formation, and therefore exhibit improved cycling life.
Similar content being viewed by others
References
C. Biegler, R.L. Deutscher, S. Fletcher, S. Hua and R. Woods, J. Electrochem. Soc. 130 (1983) 2303.
R. Jain, T.C. Adler, F.R. Mclarnon and E.J. Cairns, J. Appl. Electrochem. 22 (1992) 1039.
R. Renuka, L. Srinivasan and S. Ramamurthy, J. Appl. Electrochem. 31 (2001) 655.
J. McBreen and E. Gannon, J. Electrochem. Soc. 130 (1983) 1980.
R. Shivkumar, G.P. Kalaignan and T. Vasudevan, J. Power Sources 75 (1998) 90.
R.F. Thornton and Eric J. Carlson, J. Electrochem. Soc. 127 (1980) 1448.
G.D. Wilcox and P.J. Mitchell, J. Power Sources 32 (1990) 31.
G.D. Wilcox and P.J. Mitchell, J. Power Sources 28 (1989) 345.
J-M. Wang, L. Zhang, C. Zhang and J-Q. Zhang, J. Power Sources 102 (2001) 139.
F. Mansfeld and S. Gilman, J. Electrochem. Soc. 117 (1970) 588.
E.D. Woumfo and O. Vittori, J. Appl. Electrochem. 21 (1991) 77.
K. Bass, P.J. Mitchell and G.D. Wilcox, J. Power Sources 35 (1991) 333.
M.B. Liu, G.M. Cook and N.P. Yao, J. Electrochem. Soc. 129 (1982) 913.
J-X. Yu, H-X. Yang, X-P. Ai and X-M. Zhu, J. Power Sources 103 (2001) 93.
C-S. Cha, C-M. Li, H-X. Yang and P-F. Liu, J. Electroanal. Chem. 368 (1994) 368.
Joint Committee on Powder Diffraction Standards, 4-0733, 4-0831 and 21-1486 (1980).
Joint Committee [16], 25-1449 and 24-221 (1980).
Y.C. Chang and G. Prentice, J. Electrochem. Soc. 136 (1989) 3398.
H.J. Park and S.I. Mho, ‘Analytical Sciences’, 13supplement (1997) 311.
M.C.H. Mckubre and D.D. Macdonald, J. Electrochem. Soc. 128 (1981) 524.
M. Cai and S.M. Park, J. Electrochem. Soc. 143 (1996) 2125.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhu, XM., Yang, HX., Ai, XP. et al. Structural and electrochemical characterization of mechanochemically synthesized calcium zincate as rechargeable anodic materials. Journal of Applied Electrochemistry 33, 607–612 (2003). https://doi.org/10.1023/A:1024999207178
Issue Date:
DOI: https://doi.org/10.1023/A:1024999207178