Abstract
In order to solve the difficult problem of heterogeneity of different components in the procedure of ceramic preparation, a novel processing (heterogeneous nucleation-and-growth processing) was used to prepare homogeneous distribution powders. Composite coating particles consisting of alpha aluminum hydroxide (α-Al(OH)3) cores (average particle size 0.42 μm) with outer homogeneous amorphous silica layer are prepared by heterogeneous nucleation-and-growth processing. Effects of silica content in composite coating particles versus concentration of silicon tetraethoxide (TEOS), pH value, time and temperature are studied. The homogeneous amorphous silica layer on cores is confirmed by X-ray diffraction, transmission electron microscopy and zeta potential measurement.
Similar content being viewed by others
References
V.V. Hardikar and E. Matijevic, J. Colloid Interface Sci. 221, 133 (2000).
M. Ohmori and E. Matijevic, J. Colloid Interface Sci. 150, 594 (1992).
L.M. Liz-Marzan, M. Giersig, and A.P. Philipse, J. Colloid Interface Sci. 176, 459 (1995).
M. Ohmori and E. Matijevic, J. Colloid Interface Sci. 160, 288 (1993).
L.M. Liz-Marzan, M. Giersig, and P. Mulvaney, Langmuir 12, 4329 (1996).
Y.F. Tang, Z.D. Ling, Y.N. Lu, A.D. Li, H.Q. Ling, Y.J. Wang, and Q.Y. Shao, Mater. Chem. & Phy. 75, 301 (2002).
A.P. Philipse, M.P.B. Van Bruggen, and C. Pathmamanoharan, Langmuir 10, 92 (1994).
T. Ung, L.M. Liz-Marzan, and P. Mulvaney, Langmuir 14, 3740 (1998).
Q. Liu, Z. Xu, J.A. Finch, and R. Egerton, Chem. Mater. 10, 3936 (1998).
J.H. Adair, T. Li, T. Kido, et al., Mater. Sci. Eng. R 23, 139 (1998).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Tang, Y., Li, A., Lü, Y. et al. Preparation of Core/Shell Structure of α-Al(OH)3-SiO2 by Heterogeneous Nucleation-and-Growth Processing. Journal of Sol-Gel Science and Technology 27, 263–265 (2003). https://doi.org/10.1023/A:1024056617029
Issue Date:
DOI: https://doi.org/10.1023/A:1024056617029