Antibacterial effect of nanosized silver colloidal solution on textile fabrics

Abstract

This paper deals with the antibacterial efficacy of nanosized silver colloidal solution on the cellulosic and synthetic fabrics. Two kinds of Bacteria; Gram-positive and Gram-negative, were used. TEM observation of silver nanoparticles showed their shape, and size distribution. The particles were very small (2–5 nm) and had narrow distribution. SEM images of treated fabrics indicated silver nanoparticles were well dispersed on the surfaces of specimens. WAXS patterns did not show any peak of silver as the fabric had very small quantity of silver particles. However, ICP-MS informed the residual concentration of silver particles on fabrics before/after laundering. The antibacterial treatment of the textile fabrics was easily achieved by padding them with nanosized silver colloidal solution. The antibacterial efficacy of the fabrics was maintained after many times laundering.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    E. R. Trotman, “Dyeing and Chemical Technology of Textile Fibers” (John Wiley & Sons Inc., NY, 1984) p. 252.

    Google Scholar 

  2. 2.

    B. F. Smith and I. Block, “Textiles in Perspective” (Prentice-Hall, Inc., NJ, 1982) p. 326.

    Google Scholar 

  3. 3.

    C. E. Morris and C. M. Welch, Textile Research Journal 53 (1983) 725.

    Google Scholar 

  4. 4.

    T. Nakashima, Y. Sakagami, H. Ito and M. Matsuo, ibid. 71 (2001) 688.

    Google Scholar 

  5. 5.

    Z. L. Wang, “Characterization of Nanophase Material” (Wiley-VCH Verlag GmbH, Weinheim, 2000) p. 1.

    Google Scholar 

  6. 6.

    H. Craighead and K. Leong, “Nanotechnology Research Direction: Biotechnology, Medicine, and Healthcare” edited by M. C. Roco, R. S. Williams and P. Alivisatos (Kluwer Academic Publishers, Netherlands, 2000) p. 164.

    Google Scholar 

  7. 7.

    S. N. Khanna, “Handbook of Nanophase Materials: Effect on Properties of Reduced Size and Dimensions” edited by A. N. Goldstein (Marcel Dekker, Inc., NY, 1997) p. 2.

    Google Scholar 

  8. 8.

    D. M. Cox, “Nanostructure Science and Technology: High Surface Area Materials” edited by R. W. Siegel, E. Hu and M. C. Roco (International Technology Research Institute, VA, 1999) p. 49.

    Google Scholar 

  9. 9.

    D. P. E. Dickson, Journal Magn. Mater. 203 (1999) 46.

    Google Scholar 

  10. 10.

    R. Crawford, I. H. Harding and D. E. Mainwaring, “Surfaces of Nanoparticles and Porous Materials: Hydrous Metal Oxides as Adsorbents for Aqueous Heavy 2203 Metals” edited by J. A. Schwarz and C. I. Contescu (Marcel Dekker, Inc., NY, 1999) p. 676.

    Google Scholar 

  11. 11.

    I. E. Alcamo, “Fundamentals of Microbiology” (The Benjamin/Cummings Publishing Company, Inc., CA, 1991) p. 61,748.

    Google Scholar 

  12. 12.

    G. J. Tortora, B. R. Funke and C. L. Case, “Microbiology” (The Benjamin/Cummings Publishing Company, Inc., CA, 1992) p. 174,273

    Google Scholar 

  13. 13.

    T. K. Joeger, R. Joeger, E. Olsson and C. G. Granqvist, Trades in Biotechnology 19 (2001) 15.

    Google Scholar 

  14. 14.

    J. J. Bozzola and L. D. Russell, “Electron Microscopy” (Jones and Bartlett Publishers, Boston, 1995) p. 186.

    Google Scholar 

Download references

Author information

Affiliations

Authors

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Lee, H.J., Yeo, S.Y. & Jeong, S.H. Antibacterial effect of nanosized silver colloidal solution on textile fabrics. Journal of Materials Science 38, 2199–2204 (2003). https://doi.org/10.1023/A:1023736416361

Download citation

Keywords

  • Polymer
  • Silver Nanoparticles
  • Colloidal Solution
  • Antibacterial Effect
  • Silver Particle