Abstract
Pure aluminum nitride (AIN) has been successfully sintered to highly translucent form by microwave sintering at 1850°C with a dwelling time of 30–60 minutes. The results showed that the sintering temperature should be at least 1850°C or higher to get reasonable translucency in the AIN sample by the microwave sintering process. On the other hand, the conventional sintering method requires much longer sintering time to obtain a translucent AIN ceramics.
Similar content being viewed by others
References
L.M. Sheppard, Am. Ceram. Soc. Bull., 69, 1801 (1990).
R. Lee, J. Am. Ceram. Soc., 74(9), 2242 (1991).
A.W. Weimer, ed., Carbide, Nitride and Boride Materials Synthesis and Processing (Chapman and Hall, 1997).
D.C. Harris, Infrared Window and Dome Materials, Vol. TT10, (SPIE Optical Engineering Press, 1992).
N. Kuramoto and H. Taniguchi, J. Mater. Sci. Lett., 3, 471 (1984).
N. Kuramoto, H. Taniguchi, and I. Aso, Am. Ceram. Soc. Bull., 68, 883 (1989).
W.H. Sutton, Am. Ceram. Soc. Bull., 68, 376 (1989).
D. Clark and W.H. Sutton, Annu. Rev. Mater. Sci., 26, 229 (1996).
J. Cheng, Study on the microwave processing of ceramics, Ph.D. Thesis, Wuhan University of Technology, Wuhan, China, 1991.
N. Hashimoto, H. Yoden, and S. Deki, J. Am. Ceram. Soc., 75, 2098 (1992).
J. Cheng, J. Qiu, J. Zhou, and N. Ye, in Microwave Processing of Materials III, edited by R. Beatty, et al., Mater. Res. Soc. Symp. Proc., 269, 323 (1992).
M.A. Janney and H.D. Kimrey, in Microwave Processing of Materials II, edited by W.B. Snyder, et al., Mater. Res. Soc. Symp. Proc., 189, 215 (1990).
J.G.P. Binner, N.A. Hassine, and T.E. Cross, in Microwaves: Theory and Application in Materials Processing III, edited by D.E. Clark, et al., Ceram. Trans., 59, 565 (1995).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Cheng, J., Agrawal, D., Zhang, Y. et al. Development of Translucent Aluminum Nitride (AIN) Using Microwave Sintering Process. Journal of Electroceramics 9, 67–71 (2002). https://doi.org/10.1023/A:1021646219797
Issue Date:
DOI: https://doi.org/10.1023/A:1021646219797