Abstract
The closed porosity of polyacrylonitrile fibres wet-spun from dimethyl acetamide solutions was investigated in raising the spinning bath temperature from 2 to 20°C. The dependence of the porosity of the fibre on the conditions of plasticization treatment is established. The fibre treated in saturated vapor medium has higher porosity values (narrow transmission factors in chlorobenzene) than the fibre treated with a hot aqueous solution of dimethyl acetamide. The dependence of the fibre porosity on the drying and repeated washing and subsequent drying temperatures is demonstrated. The mobility of the structural elements increases and the porosity of the fibre decreases with an increase in the drying temperature.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
REFERENCES
A. T. Serkov, Khim. Volokna, No. 2, 41–45 (2001).
Qian Baojun, Qin Jian, and Zhou Lhanlong, Textile Asia, 20,No. 4, 40, 49–56 (1989).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zlatoustova, L.A., Smirnova, V.N., Medvedev, V.A. et al. The Macroporosity of Polyacrylonitrile Fibre. Fibre Chemistry 34, 200–202 (2002). https://doi.org/10.1023/A:1020571131832
Issue Date:
DOI: https://doi.org/10.1023/A:1020571131832