Abstract
Three different coating conditions influencing the quality of a silicon polyester galvanized steel system were investigated by means of EIS. The first aim was to investigate the influence of different types of pores or discontinuities on the corrosion resistance of the above-mentioned coating system. A second aim was to study the influence of mechanical deformation and damage of the coating on the corrosion behaviour of the coating system. Finally, degradation due to ultraviolet exposure was investigated. In each of these investigations it was possible to distinguish different time constants for different electrochemical events in the Bode phase diagram. Since the difference in magnitude of the values of the resistances was large, they could not be distinguished in the Nyquist plots. Therefore, this type of plot was not used in this work. From the build-up of the coating system and the number of time constants deduced from the EIS measurements, it was possible to model the system. From the model, the physical and electrochemical phenomena occurring during the service life of an imperfect organic coating system was explained.
Similar content being viewed by others
References
R. Macdonald and W.B. Johnson, in 'Impedance Spectroscopy, Emphasizing Solid Materials and Systems' (J. Wiley & Sons, New York, 1987) p. 15.
A.K. Jonscher, in 'Dielectric Relaxation in Solids', (Chelsea Dielectrics Press, London, 1983) pp. 96–100.
F. Geenen, PhD thesis, TU Delft (1991).
V. Lavaert, P. Praet, M. Moors, E. Wettinck and B. Verhegghe, Progr. Org. Coat. 39 (2000) 157–165.
V. Lavaert, M. De Cock, M. Moors and E. Wettinck, Progr. Org. Coat. 38 (2000) 213–221.
B.A. Boukamp, 'EquivalentCircuitUser's Manual', University of Twente (1989).
B. Yeum, ZsimpWin 2.00, Electrochemical Impedance Software, Data Analysis Software (2001).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lavaert, V., Moors, M. & Wettinck, E. An EIS study of the influence of imperfections on the corrosion behaviour of an organic coated steel system. Journal of Applied Electrochemistry 32, 853–857 (2002). https://doi.org/10.1023/A:1020543407413
Issue Date:
DOI: https://doi.org/10.1023/A:1020543407413