Abstract
Cyclic voltammetry (CV) has been used to investigate molten salt mixtures in the temperature range of 820–840 °C between the initial and anticipated final compositions for the proposed electrolytic recausticizing process of inorganic pulping chemicals. A mixture simulating the initial conditions for the proposed process (sodium carbonate, sodium sulfide/polysulfide and sodium sulfate) exhibited carbonate oxidation and sulfate reduction at the limits of the potential window. Additional oxidation of sulfide to sulfur occurs at potentials inside the positive limit of the potential window with subsequent chemical reaction to form polysulfide. To simulate the final composition sodium oxide and peroxide were added to the mixtures; the resulting CVs had an additional oxidation peak attributed to oxide and peroxide oxidation. We conclude the electrolytic recycle process is feasible, producing sulfide and oxide from carbonate and sulfate of sodium in the molten state, yet separation is necessary between the anolyte and catholyte so the reduction products are not consumed by oxidation.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
American Forest and Paper Association, ‘Statistics of Paper, Paperboard and Wood Pulp’, Technical Report, American Forest and Paper Association, Washington, DC (1994).
T.M. Grace, B. Leopold and E.W. Malcolm, Alkaline Pulping, in M.J. Kocurek and F. Stevens (Eds), ‘Pulp and Paper Manufacture’ Vol. 5, Joint Textbook Committee of the Paper Industry of the United States and Canada, Atlanta (1991), p. 367.
R. Wartena, J. Winnick and P.H. Pfromm, J. Appl. Electrochem., 32 (2002) 415–424.
D.R. Jr. Lide, Editor, ‘Journal of Physical and Chemical Reference Data, JANAF Thermochemical Tables’ (American Institute of Physics, New York, 1986).
K.K. Kelley and C.T. Anderson, ‘Contributions to the Data on Theoretical Metallurgy: IV. Metal Carbonates – Correlations and Applications of Thermodynamic Properties’ Bulletin 384 (US Department of the Interior, Bureau of Mines, Washington, DC 1935).
R.P. Tischer, ‘The Sulfur Electrode: Fused Salts and Solid Electrolytes’ (Academic Press, New York, 1983) p. 375.
B.K. Andersen, ‘Thermodynamic Properties of Molten Alkali Carbonates', Dissertation (Technical University of Denmark, Lyngby, 1975).
R.A. Rapp and K.S. Goto, in J. Braunstein and J.R. Selman (Eds),'Hot Corrosion of Metals by Molten Salts', Proceedings of the Second International Symposium on Molten Salts, Pittsburgh, PA, Oct. (1978), p. 159–177.
C.A.C. Sequeira and M.G. Hocking, Electrochim. Acta 23 (1978) 381–388.
G.J. Janz, ‘Molten Salts Handbook’ (Academic Press, New York, 1967) p. 588.
L.W. Tilton, J. Am. Ceram. Soc. 43 (1) (1960) 9–17.
A.J. Bard and L.R. Faulkner, ‘Electrochemical Methods: Fundamentals and Applications’, (J. Wiley & Sons, New York, 1980), p. 718.
N.Q. Minh and N-P. Yao, J. Electrochem. Soc. 130 (5) (1983) 1025–1029.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wartena, R., Winnick, J. & Pfromm, P. Recycling kraft pulping chemicals: cyclic voltammetry of molten salt mixtures containing Na2CO3, Na2SO4, Na2S/Na2S x and Na2O/Na2O2 . Journal of Applied Electrochemistry 32, 725–733 (2002). https://doi.org/10.1023/A:1020182322704
Issue Date:
DOI: https://doi.org/10.1023/A:1020182322704