Abstract
Assessment of long-term stability of an aluminium alloy exposed to elevated temperatures is important in the design of lightweight aerospace structures. The manner in which differential scanning calorimetry (DSC) and transmission electron microscopy (TEM) are used together in monitoring microstructural evolution, and thereby assess phase stabilities in an Al–5.1Cu–0.8 Mg–0.5 Ag–0.7 Mn–0.13 Zr (wt%) alloy, are described. DSC thermograms of the alloy, spanning room temperature to 400°C, revealed the presence of two endotherms and an exotherm. TEM investigation has identified these thermal events to be associated with Ω, S′, and θ′ precipitates. Quantitative TEM was used to measure diameter, thickness, number density, and volume fraction of the precipitates in the alloy exposed at 135°C for times as long as 3000 h. The quantitative TEM results are correlated with the DSC signatures relating to precipitation, dissolution, and coarsening reactions affecting the Ω, S′, and θ′ precipitates in the exposed alloy.
Similar content being viewed by others
References
I. J. POLMEAR,Trans. Metall. Soc. AIME 230 (1964) 1331.
Idem,Metall. Trans. 19A (1988) 1027.
B. C. MUDDLE and I. J. POLMEAR,Acta Metall. Mater. 24 (1989) 777.
K. M. KNOWLES and W. M. STOBBS,Acta. Crystallogr B44 (1988) 207.
Y. C. CHANG and J. M. HOWE,Metall. Trans. 24A (1993) 1461.
V. D. SCOTT, S. KERRY and R. L. TRUMPER,Mater. Sci. Technol. 3 (1987) 827.
R. N. SHENOY and QIONG LI, manuscript in preparation.
R. SCHUELLER, A. K. SACHDEV and F. E. WAWNER,Scripta Metall. 27 (1992) 1289.
S. P. RINGER, B. C. MUDDLE and I. J. POLMEAR,Metall Trans. 26A (1995) 1659.
S. P. RINGER, W. YEUNG, B. C. MUDDLE and I. J. POLMEAR,Acta Metall. Mater. 42 (1994) 1715.
QIONG LI and R. N. SHENOY, sent for publication.
J. E. HILLIARD,Trans. Metall. Soc. AIME 224 (1962) 906.
E. A. STARKE Jr, NASA Contractor Report 4517, Grant NAG1-745 (1993)
R. N. SHENOY and J.M. HOWE,Scripta Metall. Mater. 30 (1995) 651.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
LI, Q., SHENOY, R.N. DSC and TEM characterizations of thermal stability of an Al–Cu–Mg–Ag alloy. Journal of Materials Science 32, 3401–3406 (1997). https://doi.org/10.1023/A:1018664515422
Issue Date:
DOI: https://doi.org/10.1023/A:1018664515422