Abstract
Stress–strain behaviour in tension and in torsion was studied in ferrite–pearlite and ferrite–bainite microstructures of C–Mn steel. The fatigue tests were performed under reverse torsional loading on hour-glass shape specimens. The cyclic plasticity in torsion was found at about 37% of the monotonic yield stress in both ferrite–pearlite and ferrite–bainite microstructures. The ferrite phase in the direction of maximum shear stress was the preferable site for crack nucleation. The ferrite–bainite microstructure showed better fatigue properties than the ferrite–pearlite microstructure.
Similar content being viewed by others
References
C. E. FELTNER and P. BEARDMORE, ASTM/STP 467, 1970, p. 77.
J. C. GROSSKREUTZ, ASTM/STP 495, 1971, p. 5.
C. LAIRD, “Alloy microstructural design”, (Academic Press, New York, 1976) p. 175.
M. R. MITCHELL, “Fatigue and Microstructure” (ASM, Metals Park, OH, 1979).
F. BORIK and R. D. CHAPMAN,Trans. Am. Soc. Met. 53 (1961) 447.
M. GENSAMER, E. PEARSALL, W. S. PELLINI and J. R. LOW,ibid. 30 (1942) 983.
Y. TOMITA,Mater. Sci. Technol. 7 (1991) 299.
K. HUSSAIN, E. R. DE LOS RIOS and A. NAVARRO,Engng. Fract. Mech. 44 (1993) 425.
K. HUSSAIN and E. R. DE LOS RIOS,Scripta Metall. Mater. 28 (1993) 757.
M. F. F. IBRAHIM and K. J. MILLER,Fatigue Engng. Mater. Struct. 2 (1980) 351.
K. HUSSAIN, Ph.D. Thesis, Sheffeld University, UK, 1990.
L. F. COFFIN,Trans. ASME 76 (1954) 931.
S. S. MANSON, NACA, Research Memo TN. (1954) 2933.
H. O. BASQUIN,Proc. Amer. Soc. Testing Mater. 10 (1910) 625.
K. J. MILLER,Fatigue Fract. Engng. Mater. Struct. 10 (1987) 93.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
HUSSAIN, K., DE LOS RIOS, R.R. Microstructural effect on tensile and fatigue behaviour of C–Mn steel. Journal of Materials Science 32, 3565–3569 (1997). https://doi.org/10.1023/A:1018661809487
Issue Date:
DOI: https://doi.org/10.1023/A:1018661809487