The mechanical and interfacial properties of the mullite matrix and alumina–silica matrix composites reported in a previous publication [1], are related to the processing parameters. The flexural strengths were in the range of 428–737 MPa, flexural moduli from 82–214 GPa, work of fracture values from 293–482 KJ m-2 and ultimate failure strains from 0.16–0.45%. The interfacial strengths were determined by the fibre push-in test and compared with fracture behaviour. The formation of different interfaces in the composites and the influence of the density of thermally-induced cracks and porosity on flexural modulus is discussed.
Similar content being viewed by others
References
Wu, F. R. Jones and P. F. James, J. Mater. Sci. (in press).
R. W. Rice, Ceram. Engng Sci. Proc. 7–8 (1985) 589.
R. J. Kerans, R. S. Hay and N. J. Pagano, Amer. Ceram. Soc. Bull. 8 (1989) 429.
M. D. Thouless, O. Sbaizero, L. S. Sigl and A. G. Evans, J. Amer. Ceram. Soc. 72 (1989) 525.
L. A. Bonney and R. F. Cooper, ibid. 73 (1990) 2916.
E. Mouchon and PH. Colomban, Composites 26 (1995) 175.
L. M. Sheppard, Amer. Ceram. Soc. Bull. 71 (1992) 617.
British standard methods of testing, “Method 1005, determination of flexural properties-three point method”, BS 2782: Part 10: Method 1005, EN63 (British Standards Institution, 1977).
A. Kelly, “Strong solids,” 2nd Edn (Clarendon Press, Oxford, 1973).
D. J. Hannant, “Fibre cement and fibre concretes”, (Wiley, Chichester, 1978).
J. Aveston, R. A. Mercer and J. M. Sillwood, in Proc. Conf. on Composites, Standards, Testings and Design, April 1974, National Physical Laboratory (1974) pp. 93-103.
J. Wu, M. Chen, F. R. Jones and P. F. James, J. Non-Cryst. Solids 162 (1993) 197.
J. Wu, PhD thesis, University of Sheffield (1995).
D.B. Marshall, J. Amer. Ceram. Soc. (1984) C-259.
G. Simon and A. R. Bunsell, J. Mater. Sci. 19 (1984) 3658.
B. A. Bender, B. S. Wallace and D. J. Schrodt, ibid. 26 (1991) 970.
T. J. Clark, R. M. Arons, J. B. Stamatoff and J. Rabe, Ceram. Engng Sci. Proc. 6 (1985) 576.
G. Ervin, Jr., J. Amer. Ceram. Soc. 41 (1958) 347.
D. W. Shin, K. H. Auh and K. M. Knowles, J. Ceram. Soc. Jpn 103 (1995) 311.
E. Bischoff, M. RÜhle, O. Sbaizero and A. G. Evans, J. Amer. Ceram. Soc. 72 (1989) 741.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wu, J., Jones, F.R. & James, P.F. Continuous fiber reinforced mullite matrix composites by sol–gel processing: Part II Properties and fracture behaviour. Journal of Materials Science 32, 3629–3635 (1997). https://doi.org/10.1023/A:1018630429960
Issue Date:
DOI: https://doi.org/10.1023/A:1018630429960