Containerless solidification of germanium by electromagnetic levitation and in a drop-tube

  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

Containerless solidification of germanium has been realized by electromagnetic levitation and drop-tube processing, respectively. The effect of undercooling in the range of 40–426 K on the as-solidified structures of levitation melted Ge drops (∼8.4 mm diameter) was investigated. For undercoolings less than 300 K, the lamellar twins were grown, whereas a microstructural transition to equiaxed grains was observed at undercoolings ≥300 K. Further increasing the undercooling to 400 K, a significant reduction in grain size was achieved. In addition to a similar microstructural development among the particles solidified during free fall in a 8.5 m drop-tube, high-undercooling-induced single crystals were found for some droplets less than 200 μm in diameter. The results on the transition from twins to fine equiaxed grains are accounted for by theories of solidification kinetics and a dendrite break-up model.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. J. W. CAHN, W. B. HILLIG and G. W. SEARS,Acta Metall. 12 (1964) 1421.

    Article  CAS  Google Scholar 

  2. S. N. OJHA and R. K. MANDAL,J. Mater. Sci. Lett. 15 (1996) 326.

    Article  CAS  Google Scholar 

  3. M. E. GLICKSMAN and R. J. SCHAEFFER,J. Crystal Growth 67 (1967) 297.

    Article  Google Scholar 

  4. S. D. PETEVES and R. ABBASCHIAN,Met. Trans. 22A (1991) 1259.

    Article  CAS  Google Scholar 

  5. W. A. TILLER, “The science of crystallization: macroscopic phenomena and defect generation” (Cambridge University Press, Cambridge, 1991).

    Book  Google Scholar 

  6. H. A. DAVIS and J. B. HULL,Scripta Metall. 7 (1973) 637.

    Article  Google Scholar 

  7. S. R. STIFFLER, M. O. THOMPSON and P. S. PEERCY,Appl. Phys. Lett. 56 (1990) 1025.

    Article  CAS  Google Scholar 

  8. G. DEVAUD and D. TURNBULL,Acta Metall. 35 (1987) 765.

    Article  CAS  Google Scholar 

  9. C. F. LAU and H. W. KUI,Acta Metall. Mater. 42 (1994) 3811.

    Article  CAS  Google Scholar 

  10. R. F. COCHRANE, P. V. EVANS and A. L. GREER,Mater. Sci. Engng. 98 (1988) 99.

    Article  CAS  Google Scholar 

  11. F. ZHANG and W. WANG,Appl. Phys. Lett. 67 (1995) 617.

    Article  CAS  Google Scholar 

  12. D. LI, T. VOLKMANN, K. ECKLER and D. M. HERLACH,J. Crystal Growth 152 (1995) 101.

    Article  CAS  Google Scholar 

  13. D. M. HERLACH,Mater. Sci. Engng. R12 (1994) 117.

    Google Scholar 

  14. W. SOELLNER, “Diplomarbeit in Physik” (Institut für Raumsimulation, DLR, Küln, 1995).

    Google Scholar 

  15. R. J. BAYUZICK, W. H. HOFMEISTER and M. B. ROBINSON, in Proceedings of the Hume-Rothery Memorial Symposium: Undercooled Alloy Phases, New Orleans, March 1986, edited by E. W. Collings and C. C. Koch (American Institute of Mining, Metallurgical and Petroleum Engineers, Warrendale, PA, 1987) p. 207.

    Google Scholar 

  16. A. LUDWIG, I. WAGNER, J. LAAKMANN and P. R. SAHM,Mater. Sci. Engng. A178 (1994) 299.

    Article  CAS  Google Scholar 

  17. R. S. WAGNER,Acta Metall. 8 (1960) 57.

    Article  Google Scholar 

  18. D. R. HAMILTON and R. G. SEIDENSTICKER,J. Appl. Phys. 31 (1960) 1165.

    Article  CAS  Google Scholar 

  19. P. V. EVANS, S. VITTA, R. G. HAMERTON, A. L. GREER and D. TURNBULL,Acta Metall. 38 (1990) 233.

    Article  CAS  Google Scholar 

  20. R. TRIVEDI and W. KURZ,Int. Mater. Rev. 39 (1994) 49.

    Article  CAS  Google Scholar 

  21. M. SCHWARZ, A. KARMA, K. ECKLER and D. M. HERLACH,Phys. Rev. Lett. 73 (1994) 1380.

    Article  CAS  Google Scholar 

  22. D. LI, The Alexander von Humboldt-Stiftung: Report No. 2, 1996 (unpublished).

Download references

Author information

Authors and Affiliations

  1. Institut fur Raumsimulation, Deutsche Forschungsanstalt fur Luft- und Raumfahrt, D-51140, Koln, Germany

    D LI & D. M HERLACH

Authors
  1. D LI
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. D. M HERLACH
    View author publications

    You can also search for this author in PubMed Google Scholar

Rights and permissions

Reprints and permissions

About this article

Cite this article

LI, D., HERLACH, D.M. Containerless solidification of germanium by electromagnetic levitation and in a drop-tube. Journal of Materials Science 32, 1437–1442 (1997). https://doi.org/10.1023/A:1018593615171

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1023/A:1018593615171

Keywords

Search

Navigation