Abstract
Two distinguishable hardening mechanisms, depending on the temperature, were found by isothermal ageing in a commercial dental low-carat Au–Ag–Cu–Pd alloy. Age-hardening was attributed to the precipitation of the metastable AuCu I′ and equilibrium AuCu I ordered phases and spinodal decomposition depending on the ageing temperature. It was clearly visible, by using the direct-ageing method, that the XRD peaks of the parent phases showed a shift during transformation.
Similar content being viewed by others
References
K. F. LEINFELDER and D. F. TAYLOR, J. Dent. Res. 56(1977) 335.
K. YASUDA and M. OHTA, in Proceedings of the 3rd International Precious Metals Conference, Chicago, IL (IPMI, 1979) p. 137.
K. YASUDA and M. OHTA, J. Dent. Res. 61 (1982) 473.
M. OHTA, T. SHIRAISHI, M. YAMANE and K. YASUDA, Dent. Mater. J. 2 (1983) 10.
M. NAKAGAWA and K. YASUDA, J. Mater. Sci. 23 (1988) 2975.
K. HISATSUNE, K-I. UDOH, B. I. SOSROSOEDIRDJO, T. TANI and K. YASUDA, J. Alloys Compds. 176 (1991) 269.
K-I. UDOH, H. FUJIYAMA, K. HISATSUNE, M. HASAKA and K. YASUDA, J. Mater. Sci. 27 (1992) 504.
K. YASUDA and Y. KANZAWA, Trans. Jpn. Inst. Met. 18 (1977) 46.
K. YASUDA, K. UDOH, K. HISATSUNE and M. OHTA, Dent. Mater. J. 2 (1983) 48.
K. UDOH, K. HISATSUNE, K. YASUDA and M. OHTA, ibid. 3 (1984) 253.
D. A. PORTER and K. E. EASTERLING, in ‘‘Phase Transformations in Metals and Alloys’’, 2nd edn (Chapman & Hall, London, 1992) p. 271.
A. K. JENA and M. C. CHATURVEDI, Phase transformations in materials (Prentice Hall, New Jersey, 1992) p. 390.
D. J. EYRE, SIAM J. Appl. Math. 53 (1993) 1686.
B. DITCHEK and L. H. SCHWARTZ, Acta Metall. 28 (1980) 807.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
KIM , H.I., JANG , M.I. & JEON , B.J. Age-hardening associated with precipitation reaction and spinodal decomposition in a commercial dental low-carat Au–Ag–Cu–Pd alloy. Journal of Materials Science: Materials in Medicine 8, 333–339 (1997). https://doi.org/10.1023/A:1018572614570
Issue Date:
DOI: https://doi.org/10.1023/A:1018572614570