Abstract
Sol-gel zirconia-silica oxides were synthesized with two zirconium precursors, zirconium n-butoxide and zirconium acetylacetonate, and two different hydrolysis catalysts, HCl and H2SO4. The samples prepared with HCl were additionally sulfated with a 1 M solution of H2SO4. Characterization was performed with FTIR and 29Si-MAS-NMR spectroscopy, as well as with nitrogen adsorption. Because zirconium and silicon alkoxides have different hydrolysis rates, it was necessary to perform a pre-hydrolysis of the silicon alkoxide before mixing. The atom distribution in the ZrO2-SiO2 system depended on the zirconium precursor, which also determined the zirconium incorporation in the silica lattice, which was greater for zirconium acetylacetonate. The zirconium precursor also was responsible for the silanol concentration, which increases when samples were sulfated. Sulfating stabilizes the specific surface area. On sulfate samples calcined at 800°C BET areas larger than 500 m2/g were obtained.
Similar content being viewed by others
References
K. Morikawa, T. Shirasaki, and M. Okada, Adv. Catal. 20, 97 (1980).
R.J. Peglar, F.H. Hambleton, and J.A. Hockey, J. Catal. 20, 309 (1971).
J.R. Sohn and D.J. Ir, J. Korean Inst. Chem. Lett. 21, 305 (1983).
G.W. Wang, H. Hattori, and K. Tanabe, Chem. Lett. 277, 75 (1983).
M. Hino and K. Arata, J. Chem. Soc. Chem. Comm. 1148, 1045 (1979).
B.H. Davis, R.A. Keogh, and R. Srivasan, Catal. Today 20, 219 (1994).
K. Tanabe, H. Hattori, and T. Yamaguchi. Crit. Rev. Surf. Chem. 1, 1 (1990).
T. López, M. Asomoza, and R. Gómez, Thermochim. Acta, 219, 279 (1993).
S. Soled and G.B. McVicker, Catal. Today 14, 189 (1992).
M. Padallino, F. Pirini, M. Begui, P. Chirulo, G. Cogliati, and L. Costa, J. Non-Cryst. Solids 147, 340 (1992).
H.J.M. Bosman, E.C. Kruissin, J. van der Spoel, and F. var der Brink, J. Catal. 148, 660 (1994).
D.R. Acosta, T. López, R. Gómez, and O. Novaro, J. Mat. Res. 10, 1397 (1995).
M. Niwa, N. Katada, and Y. Murakami, J. Catal. 134, 340 (1992).
T. López, R. Gómez, F. Tzompantzi, E. Garcia-Figueroa, D.R. Acosta, and O. Novaro, Langmuir 13, 970 (1997).
M.Y. Wen, I. Wender, and J.W. Tierney, Energy and Fuel. 4, 372 (1990).
F.R. Chen, G. Coudurier, J.F. Joly, and J.C. Vedrine, J. Catal. 143, 616 (1993).
H.A. Kung, J. Solid State Chem. 52, 191 (1984).
J.C. Yory, M.D. Amato, J. Costa, and P. Parera, J. Catal. 153, 218 (1995).
T. López, J. Navarrete, R. Gómez, O. Novaro, F. Figueras, and H. Armendaris, Appl. Catal. A. 125, 217 (1995).
F. Del Monte, V. Larsen, and J.D. Mackenzie, J. Am. Ceram. Soc. 83, 628 (2000).
F. Del Monte, V. Larsen, and J.D. Mackenzie, Am. Ceram. Soc. 83, 1506 (2000).
J.A. Andersen, C. Fergusson, I. Rodríguez-Ramos, and I. Guerrero-Ruiz, J. Catal. 192, 344 (2000).
E. Sanchez, T. López, R. Gómez, J.L. Boldu, E. Muñoz, and O. Novaro, J. Sol-Gel Sci. and Technol. 5, 391 (1993).
T. Yamaguchi, T. Tanabe, and Y.C. Kung, Nat. Chem. and Phys. 16, 67 (1986).
D.A. Ward and E.I. Ko, J. Catal. 157, 333 (1995).
D.A. Ward and E.I. Ko, Langmuir 11, 369 (1995).
D.A. Ward and E.I. Ko, J. Catal. 150, 18 (1995).
C. Monterra, G. Cerrato, F. Pinna, M. Signoretto, and G.J. Strukul, J. Catal. 149, 181 (1994).
C. Monterra, G. Cerrato, C. Emanuel, and V. Bolis, J. Catal. 142, 142 (1993). Effect of Zirconia Precursor 219
T. López and R. Gómez, in Sol-Gel Optics, Processing and Activation, edited by L.C. Klein (Kluwer Academic Publishers, Boston, MA, 1993), ch. 16, p. 345.
A.D. Makarov, G. Boreskov, and K. Dzis'ko, Kinet. Katal. 20, 799 (1961).
J.R. Sohn and H.W. Kim, J. Mol. Catal. 52, 361 (1989).
C. Monterra, L. Orio, and C. Emanuel, Chem. Soc. Faraday Trans. 86, 3003 (1990).
E. López-Salinas, J.G. Hernandez-Cortez, M.A. Cortes-Jacome, J. Navarrete, M.E. Llanos, A. Vazquez, H. Armendáriz, and T. Lopez. Appl. Catal. 175, 43 (1998).
K. Tanabe, T. Sumiyoshi, K. Shibata, T. Kigoura, and T. Kitagawa, J. Bull. Chem. Soc. Jpn. 47, 1064 (1974).
X. Bokhimi, E. Muñoz, J.L. Boldu, E. Adem, O. Novaro, T. Lopez, F. Rojas, R. Gomez, and A. Garacia-Ruiz, J. Sol-Gel Sci. Technol. 17, 219 (2000).
T. López, F. Tzompantzi, J. Navarrete, R. Gómez, J.L. Boldú, E. Muñoza, and O. Novaro, J Catal. 181, 285 (1999).
J.R. John and H.W. Kim, J. Mol. Catal. 52, 36 (1989).
R.D. Gonzales, Actas V Congreso de America del norte Cancún, Mexico (1997).
F. Boccuzzi, S. Coluccia, G. Ghiotti, C. Monterra, and A. Zecchina, J. Phys. Chem. 82, 1298 (1978).
K. Nakamoto, Infrared and Raman Spectra of Inorganic and Coordination Compounds (John Wiley & Sons, NY, 1992), p. 335.
J. Casanovas, F. Illas, and G. Pacchioni, Chem. Phys. Lett. 326, 523 (2000).
F. Gaboriaud, A. Nonat, D. Chaumont, A. Craievich, and B. Hanquet, B. J. Phys. Chem. B 103, 2091 (1999).
B. Civalleri, E. Garrone, and P. Ugliengo, Chem. Phys. Lett. 299, 443 (1999).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
López, T., Tzompantzi, F., Hernández-Ventura, J. et al. Effect of Zirconia Precursor on the Properties of ZrO2-SiO2 Sol-Gel Oxides. Journal of Sol-Gel Science and Technology 24, 207–219 (2002). https://doi.org/10.1023/A:1015380523481
Issue Date:
DOI: https://doi.org/10.1023/A:1015380523481