Abstract
As2Se3.4glass samples with controlled oxygen content in the range (1.4–7.9) × 10–2wt % were used to assess the effect of oxygen impurity on the IR absorption spectrum of the glass. The spectral dependence of the extinction coefficient for oxygen impurity was determined in the range 600–1400 cm–1. It was shown that the presence of 10–5wt % O gives rise to additional losses comparable to the intrinsic losses in the CO2lasing range.
Similar content being viewed by others
REFERENCES
Dianov, E.M., Petrov, M.Yu., Plotnichenko, V.G., and Sysoev, V.K., Evaluation of Minimal Transmission Losses in Chalcogenide Glasses, Kvant. Elektron. (Moscow), 1982, vol. 9, no. 4, pp. 798–800.
Plotnichenko, V.G., Current and Potential Application Areas of IR Optical Fibers, Vysokochist. Veshchestva, 1994, no. 4, pp. 34–42.
Moynihan, C.T., Macedo, P.B., Maklad, M.S., et al., Intrinsic and Impurity Infrared Absorption in As2Se3 Glass, J. Non-Cryst. Solids, 1975, vol. 17, pp. 369–385.
Ma, D.S., Danielson, P.S., and Moynihan, C.T., Bulk and Impurity Infrared Absorption in 0.5As2Se3-0.5GeSe2, J. Non-Cryst. Solids, 1980, vol. 37, no. 4, pp. 181–190.
Demokritova, N.V., Vinogradova, G.Z., Bel'skii, N.K., and Lopatto, Yu.S., Removal of Oxygen from Selenium, Izv. Akad. Nauk SSSR, Neorg. Mater., 1984, vol. 20, no. 3, pp. 511–514.
Le žal, D. and Srb, I., Synthesis of Chalcogenide Glasses of the Se-Ge and Se-As Systems without Traces of Oxygen, Collect. Czech. Chem. Commun., 1973, vol. 36, pp. 2091–2097.
Bychkova, T.I., Vinogradova, G.Z., Voitsekhovskii, V.V., and Plotnichenko, V.G., Impurity Absorption of As2O3 in Glassy Selenium, Vysokochist. Veshchestva, 1990, no. 4, pp. 203–207.
Voight, B. and Dresler, G., Bestimmung und Abtrennung von Sauerstoffverunreinigungen in Reinst-Selen, Anal. Chim. Acta, 1981, vol. 127, pp. 87–92.
Malyshev, A.Yu., Pimenov, V.G., and Zaitseva, E.A., Determination of Arsenic, Antimony, and Selenium Impurities in High-Purity Sulfur, Anal. Kontrol, 2000, vol. 4, no. 4, pp. 329–333.
Kovalev, I.D., Malyshev, K.N., and Shmonin, P.A., Tandem Laser Mass Reflectron for Determination of Gas Forming Impurities in Solids: Design and Concept, Zh. Anal. Khim., 1998, vol. 53, no. 1, pp. 38–42.
Gorbov, S.I. and Krestovnikov, A.N., Vapor Pressure of Arsenic Selenide, Zh. Neorg. Khim., 1968, vol. 13, no. 6, pp. 1482–1487.
Vedeneev, V.I., Gurvich, L.V., Kondrat'ev, V.N., et al., Energiya razryva khimicheskikh svyazei: Spravochnik (Energy of Bond Breaking: A Handbook), Moscow: Akad. Nauk SSSR, 1961.
Behrens, R.G. and Rosenblatt, G.M., Vapor Pressure and Thermodynamics of Octahedral Arsenic Trioxide (Arsenolite), J. Chem. Thermodyn., 1972, no. 4, pp. 175–190.
Papatheodorou, G.N. and Solin, S.A., Vibrational Excitations of As2O3: I. Disordered Phases, Phys. Rev. B: Solid State, 1976, vol. 13, no. 4, pp. 1741–1751.
Edmond, J.T. and Redfearn, M.W., Infra-Red Study of As2Se3-Type Glasses in the Wavelength Range 1.25 to 25 μm, Proc. Phys. Soc. (London), 1963, vol. 81, pp. 378–382.
Ležal, D. and Srb, I., Studium der Ultrarotspektren verschiedener Modifikationen der Arsen(III)-Oxids, Chem. Zv., 1971, vol. 25, pp. 32–43.
Ležal, D. and Koňák, K., The Characterization of the Infrared Absorption Spectra of the Vitreous, Cubic, and Monoclinic Modifications of As2O3, J. Non-Cryst. Solids, 1995, vol. 192/193, pp. 187–190.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Churbanov, M.F., Shiryaev, V.S., Smetanin, S.V. et al. Effect of Oxygen Impurity on the Optical Transmission of As2Se3.4Glass. Inorganic Materials 37, 1188–1194 (2001). https://doi.org/10.1023/A:1012513629483
Issue Date:
DOI: https://doi.org/10.1023/A:1012513629483