Abstract
Direct nitridation of aluminum compacts (relative density 65%)consisting of commercial atomized powder was examined at temperaturesfrom 500 to 700°C, near or below the melting point ofaluminum, and under a pressured nitrogen atmosphere between0.5–7 MPa. Complete nitridation was achieved at a temperature as lowas 540°C by controlling the nitrogen pressure. Thenitridation process and the structures of generated aluminum nitride(AIN) were drastically influenced by nitrogen pressure. Consideringthe relations between the reaction conditions and the reactionprocesses, it is suggested that low nitridation temperature andpre-heating in vacuum have a good effect on the nitridation ratio.
Similar content being viewed by others
References
T. B. Barrett, A. V. Virkar, K. L. More, R. B. Dinwiddie,Jr. and R. A. Cutler,J. Amer. Ceram. Soc. 80 (1997) 1421.
L. M. Shepard, Ceram. Bull. 69 (1990) 1801.
K. Watari, H. J. Hwang, M. Toriyama and S. Kanzaki, J. Amer. Ceram. Soc. 79 (1996) 1979.
A. W. Weimer, G. A. Cocharn, G. A. Eisman, J. P. Hook and L. K. Mills, ibid. 77 (1994) 3.
G. Selvaduray and L. Sheet, Mater. Sci. Tech. 9 (1993) 463.
K. Nickel, R. Riedel and G. Petzow, J. Amer. Ceram. Soc. 72 (1989) 1804.
N. Hashimoto, H. Yoden and S. Shigehito, ibid. 75 (1992) 2098.
A. C. Da cruz, R. J. Munz and H. Vali, J. Mater. Sci. lett. 17 (1998) 1255.
L. Maya, Adv. Ceram. Mater. 1 (1986) 150.
B. P. Sthapitanonda and J. L. Margrave, J. Phys. Chem. 60 (1956) 1628.
T. Okada, M. Obata, M. Toriyama and S. Kanzaki, in Proceedings of the 2nd International Symposium on the Science of Engineering Ceramics, September 1998, edited by K. Niihara, T. Sekino, E. Yasuda and T. Sasa (Trans Tech Publications, 1999) p. 129.
M. Obata, M. E. Brito, M. Toriyama and S. Kanzaki, J. Amer. Ceram. Soc. to be published.
H. Scholz and P. Greil, J. Mater. Sci. 26 (1991) 669.
D. W. Yuan, V. S. Chengn, R. F. Yan and G. Simkovich, Ceram. Eng. Sci. Proc. 15 (1994) 85.
K. Komeya, N. Matukaze and T. Meguro, J. Ceram. Soc. Jpn. 101 (1993) 1319.
Z. A. Munir, Ceram. Bull. 67 (1988) 342.
M. Costantino and C. Fipro,J. Mater. Res. 6 (1991) 2397.
R. M. Marin-ayral, J. C. Tedenac, M. Bockowski and M. C. Dumez, Ann. Chim. Fr. 20 (1995) 169.
F. Ueno, J. Mater. Sci. Soc. Jpn. 31 (1994) 150.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Okada, T., Toriyama, M. & Kanzaki, S. Direct nitridation of aluminum compacts at low temperature. Journal of Materials Science 35, 3105–3111 (2000). https://doi.org/10.1023/A:1004867919183
Issue Date:
DOI: https://doi.org/10.1023/A:1004867919183