Abstract
The role of silicon in the precipitation of the σ phase (Al5Cu6Mg2) has been investigated through comparative studies on Al-3.63Cu-1.67Mg (wt%) and Al-3.63Cu-1.67Mg-0.5Si alloys. Both alloys were extensively examined after solution treating at 525°C for 2.5 h followed by ageing at 265°C for times up to 650 h. Limited studies were also undertaken on both alloys after ageing at 200 and 305°C. Precipitation of σ was observed in Al-3.62%Cu-1.66%Mg-0.5%Si for all ageing conditions studied but was absent in Si-free Al-3.62%Cu-1.66%Mg. In addition, S′ and θ′ phases were observed in both alloys. The volume fraction of σ phase in the Si containing alloy was substantially reduced by a pre-age stretch followed by ageing for 24 h at 265°C with S′ being the dominant precipitate type. The volume fraction of σ phase in the Si containing alloy was lower after ageing 24 h at 200°C than after 24 h at 265 and 305°C. Peak hardness was higher for the Si free alloy on ageing at 200 and 265°C, but the Si free alloy softened more rapidly, reflecting the more rapid coarsening kinetics of S′ compared with σ.
Similar content being viewed by others
References
A. K. Gupta, M. C. Chaturvedi and A. K. Jena, Mater. Sci. Tech. 5 (1989) 52.
W. M. Rainforth and H. Jones, J. Mater. Sci. Lett. 16 (1997) 420.
G. C. Weatherly, PhD thesis, University of Cambridge, 1966.
R. N. Wilson, D. M. Moore and P. J. E. Forsyth, J. Inst. Metals 95 (1967) 177.
H. Suzuki, I. Araki, M. Kanno and K. Kazuhiro, J. Japan Inst. Light Metals 27 (1977) 239.
R. D. Schueller, F. E. Wawner and A. K. Sachdev, J. Mater. Sci. 29 (1994) 424.
F. E. Wawner and A. K. Sachdev Idem., ibid. 29 (1994) 239.
F. E. Wawner and A. K. Sachdev Idem., Scripta Met. Mater. 27 (1992) 617.
F. E. Wawner and A. K. Sachdev Idem., ibid. 27 (1992) 1289.
Q. Li and F. E. Wawner, J. Mater. Sci. 32 (1997) 5363.
S. C. Barr, L. M. Rylands, H. Jones and W. M. Rainforth, Mater. Sci. Tech. 13 (1997) 655.
X. Gao, J. F. Nie and B. C. Muddle, Mater. Sci. Forum 217-222 (1996) 1251.
L. M. Rylands, H. Jones and W. M. Rainforth, in “Light Weight Alloys for Aerospace Application III” edited by E.W. Lee, N. J. Kim, K.V. Jata and W. E. Frazier (TMS, Warrendale, USA, 1995) p. 129.
L. M. Rylands, W. M. Rainforth and H. Jones, Philos. Mag. Lett. 76 (1997) 63.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Barlow, I.C., Rainforth, W.M. & Jones, H. The role of silicon in the formation of the (Al5Cu6Mg2) σ phase in Al-Cu-Mg alloys. Journal of Materials Science 35, 1413–1418 (2000). https://doi.org/10.1023/A:1004767131956
Issue Date:
DOI: https://doi.org/10.1023/A:1004767131956