Abstract
Alternating current (AC) impedance was used to evaluate the degradation of a high solids alkyd primer paint coating in a 3% NaCl solution, a 100% relative humidity (RH) environment after immersion in a 3% NaCl solution, and a 95% RH environment after immersion in a 3% NaCl solution. The results indicate AC impedance measures the amount of water absorbed into the coating through resistance results. A significant increase in capacitance may indicate a build up of corrosion products which causes blistering or debonding at the coating/metal interface, which may also be determined by diffusion tail analysis.
Similar content being viewed by others
References
H. Xiao and F. Mansfeld, J. Electrochem. Soc. 141 (1994) 2332.
A. S. M. Rautenbach, P. C. Pistorius and J. E. Leitch, Poly. Mater. Sci. Eng. 74 (1996) 14.
A. Amirudin and D. Thierry, Prog. Org. Coat. 26 (1995) 1.
F. Mansfeld, Corrosion 52 (1996) 417.
C. Compère, È. Frechette and E. Ghali, Corrosion Sci. 34 (1993) 1259.
C-T Chen and B. S. Skerry, Corrosion 47 (1991) 598.
N. Pebere, T. picaud, M. Duprat and F. Dabosi, Corrosion Sci. 29 (1989) 1073.
R. D. Armstrong and D. Wright, Electrochimica Acta 38 (1993) 1799.
F. Defloian, L. Fedrizzi, A. Locaspi and P. L. Bonora, Electrochimica Acta 38 (1993) 1945.
R. Hirayama and S. Haruyama, Corrosion 47 (1991) 952.
T. C. Simpson, P. J. Moran, H. Hampel, G. D. Davis, B. A. Shaw, C. O. Arah, T. L. Fritz and K. Zankel, Corrosion 46 (1990) 331.
J. Titz, G. H. Wagner, H. SpÄhn, M. Ebert, K. JÑttner and W. J. Lorenz, Corrosion 46 (1990) 221.
S. A. Mccluney, S. N. Popova, B. N. Popov, R. E. White and R. B. Griffin, J. Electrochem. Soc. 139 (1992) 1556.
J. N. Murray and H. P. Hack, Corrosion 47 (1991) 480.
R. C. Bacon, J. J. Smith and F. M. Rugg, Ind. Eng. Chem. 40 (1948) 161.
F. Wormwell and D. M. Brasher, Industrie Chim. Belge. 19 (1954) 813.
D. M. Brasher and A. H. Kingsbury, J. Appl Chem. 4 (1954) 62.
R. E. Touhsaent and H. Leidheiser, Corrosion 28 (1972) 435.
L. Beaunier, I. Epeiboin, J. C. Lestrade and H. Takenouti, Surf. Tech. 4 (1976) 237.
M. Kendig and H. Leidheiser, J. Electrochem Soc. 123 (1976) 982.
H. Leidheiser and M. Kendig, Corrosion 32 (1976) 69.
F. Mansfeld, M. Kendig and S. Tsai, Corrosion 38 (1982) 478.
D. F. Wei, I. Chatterjee and D. A. JOnes, Corrosion 51 (1995) 97.
S. FeliuJr., R. Barajas, J. M. Bastidas, M. Morcillo and S. Feliu, “Electrochemical Impedance: Analysis and Interpretation,” edited by J. R. Scully et al., ASTM special technical publication #1188, (Philadelphia, PA, 1993) p. 438.
F. Mansfeld, M. Kendig and S. Tsai, Corrosion Sci. 23 (1983) 317.
F. Mansfeld and M. Kendig, “Laboratory Corrosion Tests and Standards,” edited by G. S. Haynes and R. Baboian, ASTM special technical publication #866, (Philadelphia, PA, 1985) p. 122.
Z60 Inpedance/Gain-Phase Analysis Software Operating Manual, Scribner Assoc. ver 1.3 (1991).
E. K. Tan, F. Bellucci, M. J. Kloppers and R. M. Latanision, Mat. Sci. Forum 111-112 (1992) 177.
“Handbook of Chemistry and Physics,” edited by C. D. HODGMAN, R. C. WEAST and S. M. SHELBY, 41st ed. (Chemical Rubber Pub. Co., Cleveland, OH, 1959-60) p. 2525.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Senkevich, J.J. Degradation of an alkyd polymer coating characterized by AC impedance. Journal of Materials Science 35, 1359–1364 (2000). https://doi.org/10.1023/A:1004730006941
Issue Date:
DOI: https://doi.org/10.1023/A:1004730006941