Abstract
A surface-morphology change has been observed for an aluminide coating on the Co-base superalloy DZ40M during oxidation at 1100°C in air. The oxide formed on the coating remained an even grayish-white color during the stable oxidation stage, whereas, dark-colored corrosion nodules were observed when oxidation of the coating accelerated. The number of nodules increased with time, along with growth of the nodules, eventually covering the entire surface which signified failure.
Similar content being viewed by others
REFERENCES
H. Y. Lou, J. Chinese Soc. Corros. Protect. Suppl. 17, 464 (1997).
J. G. Li and G. Y. Zhao, in Corrosion and Corrosion Control Handbook (National Defence Industry Press, Beijing, 1988), p. 1.
R. Z. Zhu, Y. D. He, and H. B. Qi, in High-Temperature Corrosion and High-Temperature Resistance Materials (Shanghai Science and Technology Press, Shanghai, 1995), pp. 77, 115, 339-351.
B. W. Sun, H. R. Guan, X. F. Sun, and T. F. Li, Acta Metall. Sinica, 27, B100 (1991).
H. Y. Lou, F. H. Wang, B. J. Xia, and L. X. Zhang, Oxid. Met. 38, 299 (1992).
P. S. Liu, X. F. Sun, and H. R. Guan, Mater. Sci. Technol. 6, 25 (1998).
H. Fang, Acta Metall. Sinica 11, 89 (1975).
P. S. Liu, X. F. Sun, T. Jin, H. R. Guan, and Z. Q. Hu, Trans. Nonferrous Met. Soc. China 8, 582 (1998).
P. S. Liu and K. M. Liang, Oxid. Met. 53, 351 (2000).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Liu, P.S., Liang, K.M. & Gu, S.R. Failure Behavior of an Aluminide Coating on a Co-Base Superalloy during High-Temperature Oxidation in Air. Oxidation of Metals 54, 277–283 (2000). https://doi.org/10.1023/A:1004650328779
Issue Date:
DOI: https://doi.org/10.1023/A:1004650328779