Abstract
Unidirectional carbon fibre reinforced SiC composites were prepared from four types of carbon fibres, PAN-based HSCF, pitch-based HMCF, CF50 and CF70, through nine cycles or twelve cycles of impregnation of polycarbosilane and subsequent pyrolysis at 1200°C. The polycarbosilane-derived matrix was found to be β-SiC with a crystallite size of 1.95 nm. The mechanical properties of the composites were evaluated by four-point bending tests. The fracture behavior of each composite was investigated based on load-displacement curves and scanning electron microscope (SEM) observation of fracture surfaces of the specimens after tests. It was found that CF50/SiC and CF70/SiC exhibited high strength and non-brittle fracture mode with multiple matrix cracking and extensive fibre pullout, whereas HSCF/SiC and HMCF/SiC exhibited low strength and brittle fracture mode with almost no fibre pullout. The differences in the fracture modes of these carbon fibre/SiC composites were thought to be due to differences in interfacial bonding between carbon fibres and matrix. Values of flexural strengths of CF70/SiC and CF50/SiC were 967 MPa and 624 MPa, respectively, which were approximately 75% and 38% of the predicted values. The relatively lower strength of CF50/SiC, compared with CF70/SiC, was mainly attributed to the shear failure of CF50/SiC during bending tests.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
J. M. Yang, W. Lin, C. J. Shin, W. Kai, S. M. Jeng and C. V. Burkland, J. Mater. Sci. 26 (1991) 2954.
H. Yoshida, N. Miyata, K. Naito, S. Ishikawa and C. Yamagishi, J. Ceram. Soc. of Japan 102 (1994) 1016.
A. G. Evans and F. W. Zok, J. Mater. Sci. 29 (1994) 3857.
W. Liu, Y. Wei and J. Deng, Carbon 33 (1995) 441.
F. Lamouroux, X. Bourrat, R. Nasalain and J. Sevely, Carbon 33 (1993) 1273.
K. Nakano, A. Kamiya, H. Ogawa, and Y. Nishino, J. Ceram. Soc. of Japan 100 (1992) 472.
A. Kamiya, K. Nakano, N. Terazawa, Y. Nishino and H. Ichikawa, J. Ceram. Soc. of Japan 103 (1995) 191.
H. Yoshida, N. Miyata, M. Sagawa, S. Ishikawa, K. Naito, N. Enomoto and C. Yamagishi, ibid. 100 (1992) 454.
D. W. Shin and H. Tanaka, J. Am. Ceram. Soc. 77 (1994) 97.
T. Tanaka, N. Tamari, I. Kondoh and M. Iwasa, J. Ceram. Soc. of Japan 103 (1995) 1.
S. Hikuchi, Y. Yasutomi and H. Arakawa, J. Ceram. Soc. of Japan 102 (1994) 456.
Y. Hasegawa, J. Mater. Sci. 24 (1989) 1177.
M. R. Mucalo, N. B. Milestone, I. C. Vickridge and M. V. Swan, J. Mater. Sci. 29 (1994) 4487.
M. D. Thouless, O. Sbaizero, L. S. Sigl, and A. G. Evans, J. Am. Ceram. Soc. 72 (1989) 525.
A. G. Evans and D. B. Marshall, Acta. Metall. 37 (1989) 2567.
J.-K. Kim and Y.-W. Mai, in "Materials Science and Technology: vol. 13 Structure and Properties of Composites" (VCH, Germany, 1993) p. 239.
E. Y. Sun, S. R. Nutt and J. J. Brennan, J. Am. Ceram. Soc. 79 (1996) 1521.
Y. Hasegawa and K. Okamura, J. Mater. Sci. 18 (1983) 3633.
E. Bouillon, F. Langlais, R. Pailler, R. Naslain, F. Cruege, P. V. Huong, J. C. Sarthou, A. Delpuech, C. Laffon, P. Lagarde, M. Monthioux and A. Oberlin, J. Mater. Sci. 26 (1991) 1333.
J. Aveston, G. A. Cooper and A. Kelly, in "The Properties of Fiber Composites" (Conf. Proc. National Physical Laboratory, IPC Science and Technology Press, 1971) p. 15.
D. B. Marshall, B. N. Cox and A. G. Evans, Acta Metall. 33 (1985) 2013.
W. A. Curtin, J. Am. Ceram. Soc. 74 (1991) 2837.
P. S. Steif and A. Trojnacki, J. Am. Ceram. Soc.ibid. 77 (1994) 221.
S. Otani, K. Okuda and S. Matsuda, in "Tanso Seni" (Kindai Hensyu Sya, Japan, 1983) p. 701.
S. Otani, K. Okuda and S. Matsuda, in "Tanso Seni" (Kindai Hensyu Sya, Japan, 1983) p. 173.
G.-B. Zeng, H. Sano, Y. Uchiyama, K. Kobayashi, K. Suzuki and H.-M. Cheng, J. Ceram. Soc. of Japan, 106 (1998) in press.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zheng, G.B., Sano, H., Uchiyama, Y. et al. The properties of carbon fibre/SiC composites fabricated through impregnation and pyrolysis of polycarbosilane. Journal of Materials Science 34, 827–834 (1999). https://doi.org/10.1023/A:1004589316992
Issue Date:
DOI: https://doi.org/10.1023/A:1004589316992