Abstract
Zinc alloy castings are usually assembled together or mounted by screwed steel fasteners, and are tightened to a predetermined torque to develop the required tensile preload in the fastener. Due to relaxation processes in the castings, creep may cause a partial preload loss at an elevated temperature. The equipment used for load relaxation tests consists of a load-monitoring device, an oil bath, and a data-acquisition system. A load cell monitoring device is used to monitor the load loss in an ISO-metric M6×1 steel screw set into sand castings made from alloys No. 3, No. 5 and No. 2 and tightened to produce an initial preload of 6 kN. The castings were held at constant temperature in the range 80–120°C in an oil bath. The oil bath maintains the desired test temperature throughout the experiment. All tests were conducted for periods of upto 160 h. For all alloys, the initial load loss was high, decreasing gradually with time, but not ceasing. The load loss increased rapidly with test temperature, and almost all of the relaxation curves approximated to a logrithmic decay of load with time. Alloy No. 2 had the best resistance to load loss, with No. 5 next and No. 3 worst at all temperatures. The lower resistance to relaxation of alloy No. 3 was mainly due to the lower relaxation strength of copper-free primary dendrites, whereas in alloys No. 5 and No. 2, the higher copper contents contribute greatly to their relaxation strength in the form of second-phase particles. © 1998 Kluwer Academic Publishers
Similar content being viewed by others
References
A. Fox (ed.), Stress Relaxation Testing. ASTM Special Technical Publication 676, Kansas City, MO, 24-25 May 1979 p. 1.
F. Garofalo, in “Fundamentals of Creep and Creep-Rupture in Metals” (MacMillan, New York, 1965) p. 20.
J. K. Solberg and H. Thon, Mater. Sci. Engng. 75 (1985) 105.
S. Murphy and F. E. Goodwin, in International Congress and Exposition, Detroit, MI, 26-29 February 1996, SAE Technical Paper Series (SAE, 1996) p. 1.
S. Murphy and C. W. Haines, in Proceedings of Advances in Science, Technology and Applications of Zn-Al Alloys, Mexico, 1994, edited by G. T. Villasenor, Y. H. Zhu and C. Pina, p. 3.
D. G. Sopwith, Proc. Inst. Mech. Engng Lond. 159 (1948) p. 373.
M. P. Markovets, Thermal Engng 17 (1970) 77.
“Engineering Properties of Zinc Alloys” (International Lead Zinc Research Organisation Inc., New York, 1989) pp. 41 and 64.
A. A. Mir, PhD thesis, The University of Aston in Birmingham (1998).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mir, A.A., Murphy, S. Preload relaxation of threaded fasteners in sand-castings of zinc-based alloys. Journal of Materials Science 33, 4327–4332 (1998). https://doi.org/10.1023/A:1004472512660
Issue Date:
DOI: https://doi.org/10.1023/A:1004472512660