Abstract
The corrosion behaviour of Zn–Co compositionally modulated multilayers (CMM) was studied using corrosion potential measurement and the neutral salt spray (NSS) method. It was established that the corrosion potentials of the CMM, deposited from a single bath, are significantly more positive than those deposited from a dual bath. The best corrosion resistance was found for multilayers consisting of four sublayers, each 3.0 μm thick, deposited both from a dual bath and from a single bath (with an oversublayer of Zn–Co 1%).
Similar content being viewed by others
References
M. Kalantary, G. Wilcox and D. Gabe, Electrochim. Acta 40 (1995) 1609.
G. Barral and S. Maximovich, Colloq. Phys., Colloque C4 51 (1990) 291.
D. Simunovich and M. Schlesinger, J. Electrochem. Soc. 141 (1994) L10.
J. Celis, A. Haseeb and J. Roos, Trans. Inst. Metal. Finish. 70 (1992) 123.
A. Haseeb, J. Celis and J. Roos, J. Electrochem. Soc. 141 (1994) 230.
C.-C. Yang and H. Cheh, J. Electrochem. Soc. 142 (1995) 3034.
C.-C. Yang and H. Cheh, J. Electrochem. Soc. 142 (1995) 3040.
A. Stankeviciute, K. Leinartas, G. Bikulcius, D. Virbaye, A. Sudavicius and E. Juzeliunas, J. Appl. Electrochem. 28 (1998) 89.
N. Short, A. Abibsi and J. Dennis, Trans. Inst. Metal. Finish. 67 (1989) 73.
G. Loar, K. Romer and T. Aoe, Plat. Surf. Finish. 78 (1991) 74.
M. Kalantary, Plat. Surf. Finish. 81 (1994) 80.
D. Crotty and R. Griffin, Plat. Surf. Finish. 86 (1997) 57.
I. Kirilova and I. Ivanov, J. Appl. Electrochem. 28 (1998) 1359.
I. Kirilova and I. Ivanov, Bul. Chem. Commun. 29(2) (1996/97) 355.
I. Kirilova and I. Ivanov, Bul. Chem. Commun. 29(2) (1996/97) 204.
I. Kirilova and I. Ivanov, J. Appl. Electrochem. 27 (1997) 1380.
I. Kirilova and I. Ivanov, J. Appl. Electrochem. 28 (1998) 637.
Bulg. Patent 39 402 (1978).
SU Patent. 181 3808A1 (1990).
Bulg. Patent. 29 959 (1981).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kirilova, I., Ivanov, I. Corrosion behaviour of Zn–Co compositionally modulated multilayers electrodeposited from single and dual baths. Journal of Applied Electrochemistry 29, 1133–1137 (1999). https://doi.org/10.1023/A:1003675216529
Issue Date:
DOI: https://doi.org/10.1023/A:1003675216529