Abstract
Photoluminescence (PL) from alkyl-terminated silicon nanocrystallites as a function of size has been studied. Ultraviolet–blue luminescence (390–410 nm) is observed from as-prepared silicon nanoclusters with diameters from 3 to 8 nm. After 1 h of annealing at 162°C in 2-methoxyethyl ether (diglyme), the λ max of PL shifts from 360 to 420 nm. High-resolution transmission electron microscopy (HRTEM) images show that individual silicon nanoparticles are fused to form pairs of nanoparticles. FTIR spectra show that the alkyl groups remain on the surface of silicon nanoparticles. As the temperature is raised to 250°C for 1 h, the PL no longer shows any peak in the visible light region. TEM images show that the silicon nanoparticles are aggregated and fused uniformly in one single dimension, to form a strip, and these strips parallel each other. When the temperature is raised to 350°C these silicon nanoparticles form a large piece of silicon textile network, showing that functionalized alkyl surface does not persist above this temperature. A strong Si–O–Si asymmetric stretching vibration appears between 1000 and 1100 cm−1 at the expense of the C–H vibrational modes and there is no more change after 3 h of annealing at 250 or 350°C. These results provide strong evidence that the PL originates from quantum confinement.
Similar content being viewed by others
REFERENCES
A. Shimizu et al. (1996). Jpn. J. Appl. Phys. 35, L276.
E. Bustarret et al. (1996). Thin Solid Films 276, 134.
See, e.g., (1998). MRS Bull. 23, 16.
L. T. Canham (1990). Appl. Phys. Lett. 57, 1046.
D. Zhang et al. (1992). Mater. Res. Soc. Symp. Proc. 256, 35.
H. Koyama, Y. Matsushita, and N. Koshida (1998). J. Appl. Phys. 83, 1776.
H. W. H. Lee et al. (1994). Mater. Res. Soc. Symp. Proc. 351, 129.
X. Zhao et al. (1994). Phys. Rev. B 50, 18654.
C.-S. Yang et al. (1999). J. Am. Chem. Soc. 121, 5191.
T. Ito, T. Ohta, and A. Hiraki (1992). Japan J. Appl. Phys. 31, L1.
F. Koch, V. Petrova-Koch, and T. Muschik (1993). J. Luminesc. 57:271.
A. O. Konstantinov et al. (1995). Appl. Phys. Lett. 66, 2250.
R. A. Bley and S. M. Kauzlarich, in J. H. Fendler (ed.), Nanoparticles and Nanostructures Films (Wiley-VCH, Weinheim, 1998), p. 101.
R. A. Bley and S. M. Kauzlarich (1996). J. Am. Chem. Soc. 118, 12461.
R. A. Bley et al. (1996). Chem. Mater. 8, 1881.
R. A. Bley and S. M. Kauzlarich, in J. H. Fendler and I. Dékány (eds.), Nanoparticles in Solids and Solutions (Kluwer Academic Press, Dordrecht, 1996), p. 467.
J. P. Wilcoxon, G. A. Samara, and P. N. Provencio (1999). Phys. Rev. B 60, 2704.
H. W. H. Lee et al. (in preparation).
A. P. Alivisatos (1996). Science 271, 933.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Yang, CS., Kauzlarich, S.M., Wang, Y.C. et al. Photoluminescence as a Function of Aggregated Size from n-Butyl-Terminated Silicon Nanoclusters. Journal of Cluster Science 11, 423–431 (2000). https://doi.org/10.1023/A:1009099416195
Issue Date:
DOI: https://doi.org/10.1023/A:1009099416195