Abstract
Coatings were prepared by mixing MeTMS and an aqueous colloidal silica. Mixing of an MeTMS hydrolysis mixture with the aqueous colloidal silica is only possible, without flocculation of the colloidal silica particles, within a certain time window. 29Si NMR was used to follow the hydrolysis/condensation reactions of MeTMS, whereas 1H NMR was used to monitor the reaction of the MeTMS monomers and oligomers with the silica surface in the coating liquid. The reaction of MeTMS with the surface of the SiO2 particles is determined by the oligomer size. Typical SiO2 surface coverage is less than 3 molecules/nm2 (approximately one monolayer). Large MeTMS oligomers and/or cyclic species do not react with the SiO2 surface. These species are probably too apolar to react or absorb at the SiO2 surface. Flocculation of the aqueous colloidal silica occurs due to the low polarity of the hydrolysis mixture. The water content and the degree of condensation of the MeTMS determine the width of the time window.
Similar content being viewed by others
References
L. Chu, M.W. Daniels, and L.F. Francis, in Better Ceramics Through Chemistry VII: Organic/Inorganic Hybrid Materials, edited by B.K. Coltrain, C. Sanchez, D.W. Schaeffer, and G.L. Wilkes (Materials Research Society, Pittsburg PA, 1996), p. 421.
M.W. Daniels, L. Chu, and L.F. Francis, in Better Ceramics Through Chemistry VII: Organic/Inorganic Hybrid Materials, edited by B.K. Coltrain, C. Sanchez, D.W. Schaeffer, and G.L. Wilkes (Materials Research Society, Pittsburg PA, 1996), p. 215.
M.P.J. Peeters, W.J.J. Wakelkamp, and A.P.M. Kentgens, Journal of Non Crystalline Solids 189, 77 (1995).
S.E. Rankin, C.W. Macosko, and A.V. McCormick, Chemistry of Materials 10, 2037 (1998).
M.W. Daniels and L.F. Francis, Journal of Colloid and Interface Science 205, 191 (1998).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Peeters, M.P. An NMR Study of MeTMS Based Coatings Filled with Colloidal Silica. Journal of Sol-Gel Science and Technology 19, 131–135 (2000). https://doi.org/10.1023/A:1008795113990
Issue Date:
DOI: https://doi.org/10.1023/A:1008795113990