Model films of cellulose ID – improved preparation method and characterization of the cellulose film

  • S. Fält
  • L. Wågberg
  • E.-L. Vesterlind
  • P.T. Larsson
Article

Abstract

An optimization study of the preparation of spin-coated cellulose model films from the NMMO/DMSO system on silicon wafers has been made. The study shows that the cellulose concentration ID the solution determines the cellulose film thickness and that the temperature of the solution affects the surface roughness. A lower solution temperature results ID a lower surface roughness at cellulose concentrations below 0.8%. Using the described method, ID ID possible to prepare films with thicknesses of 30–90 nm with a constant surface roughness by changing the cellulose concentration, i.e. by dilution with DMSO. On these films, water has a contact angle less than 20° and about 50% of the material can, according to CP/MAS 13C-NMR spectroscopy on corresponding fibrous material, be considered to consist of crystalline cellulose ID type material. ID has further been shown that AFM can be used to determine the thickness of cellulose films, ID both dry and wet states. ID this method, the difference ID height between the top surface and the underlying wafer has been measured at an incision made into the cellulose film. The cellulose films have also been spin-coated with the same technique as on the silicon oxide wafer onto the crystal ID a quartz crystal microbalance (QCM). These model films were found to be suitable for swelling measurements with the QCM. The films were very stable during this type of measurement and films with different amounts of charges gave different swelling responses depending on their charges. As expected, films with a higher charge showed a higher swelling.

AFM Coating Contact angle Dissolving pulp Microbalance Microscopy NMR Spectroscopy Spinning Surfaces Swelling 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. Arndt K.-F., Morgenstern B. and Röder T. 2000. Scattering function of non-substituted cellulose dissolved ID β-methylmorpholine-β-oxide-monohydrate. Macromol. Symp. 162: 109-119.Google Scholar
  2. Dijt J.C., Cohen-Stuart M.A., Hofman J.E. and Fleer G.J. 1990. Kinetics of polymer adsorption ID stagnation point flow. Colloids Surf. 51: 141-158.Google Scholar
  3. Edgar C. and Gray D. 2002. Creating model cellulose I surfaces from nanocrystal suspensions. Abstracts of papers, 223rd ACS National meeting, Orlando, FL, April 7-11.Google Scholar
  4. Flory P.J. 1953. Principles of Polymer Chemistry. Cornell University Press, Ithaca, NY.Google Scholar
  5. Gunnars S., Waġberg L. and Cohen-Stuart M.A. 2002. Model films of cellulose ID Method development and initial results. Cellulose 9: 239-249.Google Scholar
  6. Hearle J.W.S. 2001. ID: Woodings C. (ed.), Regenerated Cellulose Fibres. CRC Press, Woodhead Publishing Ltd, Cambridge, UK, pp. 199-234.Google Scholar
  7. Holmberg M., Wigren R., Erlandson R. and Claesson P.M. 1997a. Interactions between cellulose and colloidal silica ID the presence of polyelectrolytes. Colloids Surf. 129-130: 175-183.Google Scholar
  8. Holmberg M., Berg J., Stemme S., Ödberg L., Rasmusson J. and Cleasson P. 1997b. Surface force studies of Langmuir-Blodgett cellulose films. J. Colloid Interface Sci. 186: 369-381.Google Scholar
  9. Höök F., Rodahl M., Brzezinski P. and Kasemo B. 1998. Energy dissipation kinetics for protein and antibody-antigen adsorption under shear oscillation on a quartz crystal microbalance. Langmuir 14: 729-734.Google Scholar
  10. Huang Y., Gardner D., Chen M. and Biermann C. 1995. Surface energetics and acid-base character of sized and unsized paper handsheets. J. Adhesion Sci. Technol. 9(11): 1403-1411.Google Scholar
  11. Israelachvili J.N. and Adams G.E. 1978. Measurement of forces betweentwomica surfaces I aqueouselectrolyte solution ID the range 0-100 nm. J. Chem. Soc. Faraday Trans. I 74: 975-1001.Google Scholar
  12. Jayme G. 1958. Properties of wood celluloses ID Determination and significance of water retention value. Tappi 41(11): 180A-183A.Google Scholar
  13. Katz S., Beatson R.P. and Scallan A.M. 1984. The determination of strong and weak acid groups ID sulfite pulps. Svensk Papperstidn. 87(6): R48-R53.Google Scholar
  14. Lennholm H. and Iversen T. 1995. Estimation of cellulose I and ID ID cellulosic samples by principal component analysis of 13C-CP/MAS-NMR-spectra. Holzforschung 49: 119-126.Google Scholar
  15. Lennholm H., Larsson T. and Iversen T. 1994. Determination of cellulose ID and ID#x03B2; ID lignocellulosic materials. Carbohydr. Res. 261: 119-131.Google Scholar
  16. Lindström T. and Carlsson G. 1982. The effect of carboxyl groups and their ionic form during drying on the hornification of cellulose fibres. Svensk Papperstidn. 85(15): R146-151.Google Scholar
  17. Nelson P.F. and Kalkipsakis C.G. 1964. The behavior of salts of a carboxymethylated eucalypt kraft pulp. Tappi 47(3): 170-176.Google Scholar
  18. Neuman R.D., Berg J.M. and Cleasson P.M. 1993. Direct measurement of surface forces ID papermaking and paper coating systems. Nord Pulp Pap. Res. J. 8: 96-104.Google Scholar
  19. Pettersson B. and Eriksson K.-E.L. 2000. A standardized spectrophotometric assay of endoglucanase activity using dyed amorphous polysaccharides. Anal. Biochem. 285: 220-224.Google Scholar
  20. Poptoshev E. 2001. Polyelectrolyte moderated interactions between glass and cellulose surfaces. PhD thesis, Royal Institute of Technology (KTH), Stockholm, Sweden.Google Scholar
  21. Revol J.-F., Godbout L. and Gray D.G. 1998. Solid self-assembled films of cellulose with chiral nematic order and optically variable properties. J. Pulp Paper Sci. 24(5): 146-149.Google Scholar
  22. Rodahl M., Höök F., Krozer A., Brzezinski P. and Kasemo B. 1995. Quartz crystal microbalance setup for frequency and Q-factor measurements ID gaseous and liquid environments. Rev. Sci. Instrum. 66(7): 3924.Google Scholar
  23. Rodahl M. and Kasemo B. 1996. A simple setup to simultaneously measure the resonant frequency and the absolute dissipation factor of a quartz crystal microbalance. Rev. Sci. Instrum. 67(9): 3238-3241.Google Scholar
  24. Rodahl M., Höök F., Fredriksson C., Keller C.A., Krozer A., Brzezinski P., Voinova M. and Kasemo B. 1997. Simultaneous frequency and dissipation factor QCM measurements of biomolecular adsorption and cell adhesion. Faraday Discuss. 107: 229-246.Google Scholar
  25. Röder T. and Morgenstern B. 1999. The influence of activation on the solution state of cellulose dissolved ID N-methylmorpholine-N-oxide-monohydrate. Polymer 40: 4143-4147.Google Scholar
  26. Röder T., Morgenstern B. and Glatter O. 2000. Polarized and depolarized light scattering on solutions of cellulose ID N,N-dimethylacetamide/lithium chloride. Macromol. Symp. 162: 87-93.Google Scholar
  27. Röder T., Morgenstern B., Schelosky N. and Glatter O. 2001. Solutions of cellulose ID N,N-dimethylacetamide/lithium chloride studied by light scattering methods. Polymer 42: 6765-6773.Google Scholar
  28. Torn L.H. 2000. Polymers and surfactants ID solution and at interfaces. PhD thesis, Wageningen University, The Netherlands.Google Scholar
  29. Wågberg L. and Westerlind C. 2001. Spreading of droplets of different liquids on specially structured papers. Nord. Pulp Pap. Res. J. 5: 598-606.Google Scholar
  30. Walecka J.A. 1956. An investigation of low degree of substitution carboxymethylcelluloses. Tappi 39(7): 458-463.Google Scholar
  31. Westman L. and Lindström T. 1981. Swelling and mechanical properties of cellulose hydrogels. 1. Preparation, characterization and swelling bahavior. J. Appl. Polym. Sci. 26(8): 2519-2532.Google Scholar
  32. Woodings C. 2001. Regenerated Cellulose Fibres. CRC Press, Woodhead Publishing Ltd, Cambridge, UK, pp. 1-21.Google Scholar

Copyright information

© Kluwer Academic Publishers 2004

Authors and Affiliations

  • S. Fält
    • 1
  • L. Wågberg
    • 2
  • E.-L. Vesterlind
    • 1
  • P.T. Larsson
    • 3
  1. 1.Department of Natural and Environmental SciencesMidSweden UniversitySundsvallSweden
  2. 2.Department of Fibre and Polymer Technology, Fibre Technology DivisionKTHStockholmSweden
  3. 3.STFI ABStockholmSweden

Personalised recommendations