, Volume 32, Issue 15, pp 3951–3959 | Cite as

Non-destructive evaluation of porous MgO ceramics using acoustic techniques

  • T Kathrina
  • R. D Rawlings
Article

Abstract

Two acoustic techniques, ultrasonics (US) and acousto-ultrasonics (AU), were used to evaluate MgO extrudate in both the green and sintered states. In US, the velocity was measured and in AU ringdown counts, pulse amplitude, pulse width and spectrum were used to quantify the output signal. The acoustic measurements showed good reproducibility, especially velocity. Under some sintering conditions the ultrasonic velocity and the porosity were lower than in the green state: this was attributed to pore growth in the early stages of sintering. It was found that as the temperature and time of sintering increased, the density, compressive strength and ultrasonic velocity increased. However, the response of the AU parameters to changes in sintering conditions was more complex, for example, the peak amplitude increased whereas pulse width and ringdown counts decreased with increasing temperature of sintering. The US and AU data on the sintered MgO extrudate were correlated with the structure and properties. Empirical relationships between the acoustic parameters and porosity and compressive strength were obtained which gave better coefficients of regression for the ultrasonic velocity than for acousto-ultrasonic parameters. It was concluded that US, and in some instances AU, are feasible as quality control techniques/non-destructive evaluation for ceramics.

Keywords

Compressive Strength Acoustic Emission Pulse Width Peak Amplitude Ultrasonic Velocity 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    A. VARY, “Materials Analysis by ultrasonics” (Noyes Data Corporation, Park Ridge, New Jersey, USA, 1987).Google Scholar
  2. 2.
    T. KATHRINA and R. D. RAWLINGS, Br. Ceram. Trans. 95(6) (1996) 233.Google Scholar
  3. 3.
    Idem, J. Eur. Ceram. Soc., in press.Google Scholar
  4. 4.
    R. A. ROBERTS, Mater. Eva. 46 (1988) 758.Google Scholar
  5. 5.
    K. YAMANAKA, S. K. JEN, C. NERON and J. F. BUSSIERE, ibid. 47 (1989) 828.Google Scholar
  6. 6.
    M. ARNOULD, F. DUVANT, J. DU MOUZA and R. STRUILLOU, “Use of ultrasonic waves for the continuous control of microcracking in hot ceramics during drying, firing and cooling”, Proceedings of the Final Contractor Meeting of EEC Research Development Programme in the Raw Material Sector in the area of Technical Ceramics (Elsevier, 1988) 281.Google Scholar
  7. 7.
    S. J. KLIMA and G. Y. BAAKLINI, in “Materials Analysis by Ultrasonics”, edited by A. Vary (Noyes Data Corporation, Park Ridge, New Jersey, USA, 1987).Google Scholar
  8. 8.
    A. VARY, Mater. Eva. 40 (1982) 650.Google Scholar
  9. 9.
    K. K. PHANI, S. K. NIYOGI, A. K. MAITRA and R. ROYCHAUDHURY, J. Mater. Sci. 21 (1986) 4335.CrossRefGoogle Scholar
  10. 10.
    A. O. B. ADUDA and R. D. RAWLINGS, “Acousto-ultrasonic testing of inorganic composites”, presented at the 7th CIMTEC World ceramic congress, Montecaniti Terme, Italy (1990); Proceedings to be published by Elsevier.Google Scholar
  11. 11.
    A. C. DAS, S. K. NIYOGI and S. MUKHERJEE, J. Mater. Sci. Lett. 10 (1991) 173.CrossRefGoogle Scholar
  12. 12.
    I. THOMPSON and R.D. RAWLINGS, J. Mater. Sci. 26 (1991) 4534.CrossRefGoogle Scholar
  13. 13.
    S. SOMIYA, “Advanced Technical Ceramics” Powder Technol. (Academic Press, Japan, 1984).Google Scholar
  14. 14.
    O. J. WHITTEMORE, Powder Technol. 29 (1981) 167.CrossRefGoogle Scholar
  15. 15.
    A. O. B. ADUDA and R. D. RAWLINGS, J. Mater. Sci. 29 (1994) 2297.CrossRefGoogle Scholar
  16. 16.
    Idem, Br. Ceram. Trans. 95 (1996) 10.Google Scholar
  17. 17.
    J. SUMMERSCALES, “Non-destructive testing of fibre-reinforced plastics composites” (Elsevier Applied Science, London, New York, 1990).Google Scholar
  18. 18.
    A. VARY, in “Non-destructive Testing on fibre-reinforced plastics composites”, edited by J. Summerscales (Elsevier Applied Science, London, New York, 1990) pp. 1–54.Google Scholar
  19. 19.
    C. B. SCRUBY and R. COLBROOK, Br. J. NDT 34(3) (1992) 109.Google Scholar
  20. 20.
    R. HALMSHAW, “Non-destructive Testing” (Edward Arnold, London, 1987).Google Scholar

Copyright information

© Chapman and Hall 1997

Authors and Affiliations

  • T Kathrina
    • 1
  • R. D Rawlings
    • 1
  1. 1.Department of MaterialsImperial College of Science, Technology and MedicineLondonUK

Personalised recommendations