Effects of alloying elements on the electrochemical characteristics of iron aluminides

  • H. C CHOE
  • H. S KIM
  • D. C CHOI
  • K. H KIM
Article

Abstract

Effects of alloying elements on the electrochemical characteristics of iron aluminides in the H2SO4, H2SO4+KSCN and HCl solutions were investigated using electrochemical tests. The corrosion morphologies in iron aluminides were analysed by utilising optical microscopy. It was found that the addition of Cr and Mo to iron aluminides increased the corrosion potential, pitting potential and repassivation potential. The active current density, passive current density and reactivation current density decreased as Cr and Mo were added. In the case of Mo addition, the passive current density was slightly higher in the H2SO4 solution than in solutions containing SCN- and Cl-. When B was added to samples, the corrosion potential and repassivation potential decreased, whereas the active current density, passive current density, reactivation current density and pitting potential increased. Iron aluminides containing Mo and Cr showed remarkably improved intergranular and pitting corrosion resistance to SCN- and Cl- solution. On the other hand, B addition accelerated granular and intergranular corrosion by precipitation of borides.

Keywords

Saturated Calomel Electrode Corrosion Potential Corrosion Test Intergranular Corrosion KSCN 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    B. Schmidt, P. N. Nagpal and I. Baker, in High Temperature Ordered Intermetallic Alloys III, Mat. Res. Soc. Symposia Proceedings, Vol. 133 (MRS, 1989) p. 755.CrossRefGoogle Scholar
  2. 2.
    P. F. Tortorelli and J. H. Devan, Mater. Sci. Eng. A153 (1992) 573.CrossRefGoogle Scholar
  3. 3.
    C. G. Mckamey, J. A. Horton and C. T. Liu, J. Mater. Res. 4 (1989) 1156.CrossRefGoogle Scholar
  4. 4.
    J. R. Knibole and R.N. Wright, Mater. Sci Eng. A153 (1992) 382.CrossRefGoogle Scholar
  5. 5.
    N. S. Stoloff and C.T. Liu, Intermetallic 2 (1994) 875.CrossRefGoogle Scholar
  6. 6.
    J. G. Kim and R. A. Buchanan, Corrosion 50 (1994) 658.CrossRefGoogle Scholar
  7. 7.
    ASTM Wear and Erosion, Metal Corrosion, section 3, Vol. 03.02, (American Society for Testing and Materials, Philadelphia, PA, 1988) p. 97.Google Scholar
  8. 8.
    M. Pourbaix, “Atlas of Electrochemical Equilibria in Aqueous Solutions” (Pergamon Press, London, 1966) p. 168.Google Scholar
  9. 9.
    Z. Szklaska-Smialowska, “Pitting Corrosion of Metals” (NACE, Houston, 1986) pp. 218, 147.Google Scholar
  10. 10.
    C. R. Claton and Y. C. Yu, J. Electrochem. Soc. 133 (1986) 2465.CrossRefGoogle Scholar
  11. 11.
    Goldschmidt, H. J., J. Iron Steel Inst. Lond. 209 (1971) 900.Google Scholar
  12. 12.
    W. L. Clarke, R. L. Cowan and W. L. Walker ASTM STP 656 (American Society for Testing and Materials, Philadelphia, PA, 1978) pp. 99.Google Scholar
  13. 13.
    D. A. Jones, “Principles and Prevention of Corrosion” (Maxwell MacMillan Eds., New York, 1992) p. 302.Google Scholar
  14. 14.
    M. Skashita and N. Sato, Corros. Sci. 17 (1977) 473.CrossRefGoogle Scholar
  15. 15.
    C. L. Rollinson, “The Chemistry of Chromim, Molybdenum and Tungsten” (Pergamon Press, Oxford, 1975).Google Scholar
  16. 16.
    I. L. Rozenfeld, “Corrosion Inhibitors” (McGraw-Hill, New York, 1981) p. 174.Google Scholar
  17. 17.
    A. P. Majidi and M. A. Streicher, Corrosion 40 (1984) 393.CrossRefGoogle Scholar
  18. 18.
    R. C. Newman, H. S. Isaacs and B. Alman, ibid. 38 (1980) 261.CrossRefGoogle Scholar

Copyright information

© Chapman and Hall 1997

Authors and Affiliations

  • H. C CHOE
    • 1
  • H. S KIM
    • 2
  • D. C CHOI
    • 3
  • K. H KIM
  1. 1.Department of Iron Manufacture and Metallurgical EngineeringKwang Yang CollegeKwang YangKorea
  2. 2.Department of Materials Science and Metallurgical EngineeringSunchoen National UniversitySunchoenKorea
  3. 3.Department of Metallurgical EngineeringChonnam National UniversityKwangjuKorea

Personalised recommendations