Poly(methyl methacrylate)–titania hybrid materials by sol–gel processing

  • JUN ZHANG
  • SHENGCHENG LUO
  • LINLIN GUI
Article

Abstract

Sol–gel derived poly(methyl methacrylate)–titania hybrid materials were synthesized by using acrylic acid or allyl acetylacetone (3-allyl-2,4-pentanedione) as coupling agent. Titanium butoxide modified with acrylic acid (or titanium isopropoxide modified with allyl acetylacetone) was hydrolysed to produce a titania network, and then poly(methyl methacrylate) (PMMA) chains, formed in situ through a radical polymerization, were chemically bonded to the forming titania network to synthesize a hybrid material. Transparent hybrid materials with different contents of titania were achieved. With increase of the titania content, the colours of the products changed from yellow to dark red. The synthesis process was investigated step by step by using Fourier transform–infrared spectroscopy, and the experimental results demonstrated that acrylate or acetylacetonato groups bound to titanium remain in the final hybrid materials. The thermal stability of the hybrid materials was considerably improved relative to pure PMMA. Field emission scanning electron microscopy analyses showed the hybrid materials are porous and pore diameters vary from 10–100 nm. The hybrid materials using allyl acetylacetone as coupling agent exhibited a thermochromic effect that neither pure PMMA nor titania exhibit.

Keywords

PMMA Field Emission Scanning Electron Microscopy Acrylic Acid Hybrid Material Methyl Methacrylate 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    H. K. SCHMIDT, in “Inorganic and Organometallic Polymers with Special Properties”, edited by R. M. Laine (Kluwer Academic, New York, 1992) p. 297.CrossRefGoogle Scholar
  2. 2.
    H. SCHMIDT and G. PHILIPP,J. Non-Cryst. Solids 63 (1984) 283.CrossRefGoogle Scholar
  3. 3.
    J. HU and J. D. MACKENZIE, in “Better Ceramics Through Chemistry”, MRS Symposium Proceedings, Vol. 271, editors M. J. Hampden-Smith, W. G. Klemperer and C. Jeffrey Brinker (Materials Research Society, Pittsburgh, PA, 1992) p. 681.Google Scholar
  4. 4.
    H. HUANG, B. ORLER and G. L. WILKES,Polym. Bull. 14 (1985) 557.CrossRefGoogle Scholar
  5. 5.
    Idem,Macromolecules 20 (1987) 1322.CrossRefGoogle Scholar
  6. 6.
    B. WANG, G. L. WILKES, C. D. SMITH and J. E. McGRATH,Polym. Commun. 32 (1991) 400.Google Scholar
  7. 7.
    M. NANDI, JEANINE A. CUNKLIN, LAWRENCE SALVATI JR and AYUSMAN SEN,Chem. Mater. 3 (1991) 2021.CrossRefGoogle Scholar
  8. 8.
    R. H. GLASTER and G. L. WILKES,Polym. Bull. 22 (1989) 527.CrossRefGoogle Scholar
  9. 9.
    G. PHILIPP and H. SCHMIDT,J. Non-Cryst. Solids 82 (1986) 31.CrossRefGoogle Scholar
  10. 10.
    B. M. NOVAK,Adv. Mater. 5 (1993) 422.CrossRefGoogle Scholar
  11. 11.
    R. B. DAVIS and P. HURD,J. Am. Chem. Soc. 77 (1955) 3284.CrossRefGoogle Scholar
  12. 12.
    K. NAKAMOTO, “Infrared and Raman Spectra of Inorganic and Coordination Compounds”, 3rd Edn (Wiley, New York, 1978).Google Scholar
  13. 13.
    A. LEAUSTIC, F. BABONNEAU and J. LIVAGE,Chem. Mater. 1 (1989) 240.CrossRefGoogle Scholar

Copyright information

© Chapman and Hall 1997

Authors and Affiliations

  • JUN ZHANG
    • 1
  • SHENGCHENG LUO
    • 1
  • LINLIN GUI
    • 1
  1. 1.Institute of Physical ChemistryPeking UniversityBeijingPeople’s Republic of China

Personalised recommendations