Journal of Materials Science Letters

, Volume 19, Issue 20, pp 1825–1828 | Cite as

Effect of cooling rate on the microstructure of hypereutectic Al-Mg2Si alloys

  • J. Zhang
  • Z. Fan
  • Y. Q. Wang
  • B. L. Zhou
Article

References

  1. 1.
    E. E Schimid, K. V Oldenbrug and G. Frommeyer, Z.Metallkde. 81 (1990) 809.Google Scholar
  2. 2.
    G. Frommeyer, S. Beer and K. V. Oldenbrug,ibid. 85 (1994) 372.Google Scholar
  3. 3.
    M. Mabuchi and K. Higashi, Acta Mater. 44 (1996) 4611.Google Scholar
  4. 4.
    M. Mabuchi, K. Kubota and K. Higashi, Mater.Letters 19 (1994) 247.Google Scholar
  5. 5.
    J. Zhang, Z. Fan, Y. Wang and B. Zhou, Mater.Sci.Eng. 281A (2000) 104.Google Scholar
  6. 6.
    Idem, J.Mater.Sci., submitted.Google Scholar
  7. 7.
    J. Zhang, Y. Wang, B. Yang and B. Zhou, J.Mater.Res. 1 (1999) 68.Google Scholar
  8. 8.
    J. Zhang, Y. Wang and B. Zhou, Mater.Sci.Tech. 11 (1999) 1236.Google Scholar
  9. 9.
    F. Norman, P. B Pranghell and R. S. Mcewen, Acta Mater. 46 (1998) 5715.Google Scholar
  10. 10.
    J. Zhang, Z. Fan, Y. Wang and B. Zhou, J.Mater.Sci.Letters 18 (1999) 783.Google Scholar
  11. 11.
    J. Lipton, W. Kurz and R. Trivedi, Acta Metall. 35 (1987) 957.Google Scholar
  12. 12.
    B. Chalmers, “Principles of Solidification” (John Wiley & Sons, Inc., 1964) p. 158.Google Scholar
  13. 13.
    W. D. Fei and S. B. Kang, J.Mater.Sci.Letters 14 (1995) 1795.Google Scholar
  14. 14.
    J. Chang, Z. Fan, Y. Wang and B. Zhou, Scripta Mater., in press.Google Scholar
  15. 15.
    G. Levi and R. Mehrabian, Metall.Mater.Trans. 13A (1982) 13.Google Scholar
  16. 16.
    M. C. Flemings and Y. Shiohara, Mater.Sci.Eng.A 65 (1984) 157.Google Scholar

Copyright information

© Kluwer Academic Publishers 2000

Authors and Affiliations

  • J. Zhang
    • 1
    • 2
  • Z. Fan
    • 3
  • Y. Q. Wang
    • 3
  • B. L. Zhou
    • 3
  1. 1.Institute of Metal ResearchChinese Academy of SciencesShenyangPeople's Republic of China
  2. 2.Department of Materials EngineeringBrunel UniversityUxbridgeUK
  3. 3.Department of Materials EngineeringBrunel UniversityUxbridgeUK

Personalised recommendations