High temperature deformation behavior and processing map of hot isostatically pressed Ti-47. 5Al-2Cr-2Nb-0. 2W-0. 2B alloy using gas atomization powders

  • Published:
Journal of Iron and Steel Research International Aims and scope Submit manuscript

Abstract

The hot compressive deformation behavior of hot isostatically pressed Ti-47. 5Al-2Cr-2Nb-0. 2W-0. 2B alloy using gas atomization powders was systematically investigated and the processing map was obtained in the temperature range of 1323–1473 K and strain rate range of 0.001–0.5 s−1. The calculated activation energy in the above variational ranges of temperature and strain rate possesses a low activation energy value of approximately 365.6 kj/mol based on the constitutive relationship models developed with the Arrhenius-type constitutive model respectively considering the strain rate and deformation temperature. The hot working flow behavior during the deformation process was analyzed combined with the microstructural evolution. Meanwhile, the processing maps during the deformation process were established based on the dynamic material model and Prasad instability criterion under different deformation conditions. Finally, the optimal hot processing window of this alloy corresponding to the wide temperature range of 1353– 1453 K and the low strain rate of 0.001–0.1 s−1 was obtained.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Y. W. Kim, JOM 46 (1994) 30–39.

    Article  Google Scholar 

  2. G. E. Fuchs, Metall. Mater. Trans. A 29 (1998) 27–36.

    Article  Google Scholar 

  3. L. I. Hui-Zhong, M. Zeng, X. P. Liang, L. I. Zhou, Y. Liu, Trans. Nonferrous Met. Soc. China 22 (2012) 754–760.

    Article  Google Scholar 

  4. J. Qiao, H. Jia, P. K. Liaw, Mater. Sci. Eng. R 100 (2016) 1–69.

    Article  Google Scholar 

  5. X. P. Liang, Y. Liu, H. Z. Li, C. X. Zhou, G. F. Xu, Mater. Des. 37 (2012) 40–47.

    Article  Google Scholar 

  6. Y. Y. Luo, Z. P. Xi, W. D. Zeng, X. N. Mao, Y. L. Yang, H. Z. Niu, J. Mater. Eng. Perform. 23 (2014) 3577–3585.

    Article  Google Scholar 

  7. C. Qiu, Y. Liu, W. Zhang, B. Liu, X. Liang, Intermetallics 27 (2012) 46–51.

    Article  Google Scholar 

  8. D. Y. Zhang, H. Z. Li, X. P. Liang, Z. W. Wei, Y. Liu, Mater. Des. 59 (2014) 415–420.

    Article  Google Scholar 

  9. G. Wang, L. Xu, Y. Tian, Z. Zheng, Y. Cui, R. Yang, Mater. Sci. Eng. A 528 (2011) 6754–6763.

    Article  Google Scholar 

  10. T. Yan, E. L. Yu, Y. Q. Zhao, J. Iron Steel Res. Int. 20 (2013) No. 11, 125–130.

    Article  Google Scholar 

  11. K. P. Rao, Y. V. R. K. Prasad, Mater. Sci. Eng. A 527 (2010) 6589–6595.

    Article  Google Scholar 

  12. G. V. S. S. Prasad, M. Goerdeler, G. Gottstein, Mater. Sci. Eng. A 400 (2005) 231–233.

    Article  Google Scholar 

  13. P. Mathur, D. Apelian, A. Lawley, Acta Metall. 37 (1989) 429–443.

    Article  Google Scholar 

  14. B. S. Murty, S. Ranganathan, Int. Mater. Rev. 43 (1998) 101–141.

    Article  Google Scholar 

  15. Z. A. Munir, U. Anselmi-Tamburini, Mater. Sci. Rep. 3 (1989) 277–365.

    Article  Google Scholar 

  16. P. Saravanan, V. Selvarajan, S. V. Joshi, G. Sundararajan, J. Phys. D: Appl. Phys. 34 (2000) 131–140.

    Article  Google Scholar 

  17. D. Y. Yang, H. X. Peng, Y. Q. Fu, F. Y. Cao, Z. L. Ning, S. Guo, Y. D. Jia, N. Liu, J. F. Sun, Nanosci. Nanotechnol. Lett. 7 (2015) 603–610.

    Article  Google Scholar 

  18. K. L. Wang, S. Q. Lu, X. J. Dong, X. Li, D. L. Ouyang, J. Iron Steel Res. Int. 23 (2016) 1297–1302.

    Article  Google Scholar 

  19. A. V. Bakulin, S. E. Kulkova, Q. M. Hu, R. Yang, J. Exp. Theoret. Phys. 120 (2015) 257–267.

    Article  Google Scholar 

  20. Y. Huang, Y. Wang, H. Fan, J. Shen, Intermetallics 31 (2012) 202–207.

    Article  Google Scholar 

  21. Y. Sun, K. Kulkarni, A. K. Sachdev, E. J. Lavernia, Metall. Mater. Trans. A 45 (2014) 2759–2767.

    Article  Google Scholar 

  22. Y. Sun, Z. Wan, L. Hu, J. Ren, Mater. Des. 86 (2015) 922–932.

    Article  Google Scholar 

  23. F. Warchomicka, C. Poletti, M. Stockinger, Mater. Sci. Eng. A 528 (2011) 8277–8285.

    Article  Google Scholar 

  24. S. L. Zhu, H. Z. Cao, J. S. Ye, W. H. Hu, G. Q. Zheng, J. Iron Steel Res. Int. 22 (2015) 264–271.

    Article  Google Scholar 

  25. F. Warchomicka, C. Poletti, M. Stockinger, T. Henke, Int. J. Mater. Form. 3 (2010) 215–218.

    Article  Google Scholar 

  26. A. Arifin, A. B. Sulong, N. Muhamad, J. Syarif, M. I. Ramli, Mater. Des. 55 (2014) 165–175.

    Article  Google Scholar 

  27. Z. Y. Gao, T. Pan, Z. Wang, G. Q. Liu, H. Su, J. Iron Steel Res. Int. 22 (2015) 818–826.

    Article  Google Scholar 

  28. Y. M. Han, Z. Wang, X. H. Che, X. G. Chen, W. R. Li, Y. L. Li, Mater. Sci. Eng. B 156 (2009) 57–61.

    Article  Google Scholar 

  29. Y. Dong, C. Zhang, G. Zhao, Y. Guan, A. Gao, W. Sun, Mater. Des. 92 (2015) 983–997.

    Article  Google Scholar 

  30. Z. Y. Jiang, X. J. Gao, S. L. Li, H. M. Zhang, D. F. Chen, J. Z. Xu, J. Iron Steel Res. Int. 22 (2015) 438–445.

    Article  Google Scholar 

  31. N. Liu, Z. D. Liu, X. K. He, Z. Q. Yang, L. T. Ma, J. Iron Steel Res. Int. 23 (2016) 1342–1348.

    Article  Google Scholar 

  32. Y. Liu, Y. Ning, X. Yang, Z. Yao, H. Guo, Mater. Des. 95 (2016) 669–676.

    Article  Google Scholar 

  33. M. Ma, H. Ding, Z. Y. Tang, J. W. Zhao, Z. H. Jiang, G. W. Fan, J. Iron Steel Res. Int. 23 (2016) 244–252.

    Article  Google Scholar 

  34. X. Xiao, G. Q. Liu, B. F. Hu, X. Zheng, L. N. Wang, S. J. Chen, A. Ullah, Comput. Mater. Sci. 62 (2012) 227–234.

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. School of Materials Science and Engineering, Harbin Institute of Technology, 150001, Harbin, Heilongjiang, China

    Ying Bao, Dong-ye Yang, Fu-yang Cao Ph.D. (Assoc. Prof.) & Jian-fei Sun Ph.D. (Assoc. Prof.)

  2. School of Materials Science and Engineering, Harbin University of Science and Technology, 150000, Harbin, Heilongjiang, China

    Ying Bao

  3. Science and Technology on Advanced High Temperature Structural Materials Laboratory, Beijing Institute of Aeronautical Materials, 100095, Beijing, China

    Na Liu, Guo-qing Zhang & Zhou Li

Authors
  1. Ying Bao
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Dong-ye Yang
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Na Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Guo-qing Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Zhou Li
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Fu-yang Cao Ph.D.
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Jian-fei Sun Ph.D.
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding authors

Correspondence to Fu-yang Cao Ph.D. or Jian-fei Sun Ph.D..

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Bao, Y., Yang, Dy., Liu, N. et al. High temperature deformation behavior and processing map of hot isostatically pressed Ti-47. 5Al-2Cr-2Nb-0. 2W-0. 2B alloy using gas atomization powders. J. Iron Steel Res. Int. 24, 435–441 (2017). https://doi.org/10.1016/S1006-706X(17)30066-3

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1016/S1006-706X(17)30066-3

Key words

Search

Navigation