Abstract
To improve the straight edge seam defect on hot-rolled steel plates, the deformation and temperature distribution of rectangular slabs and chamfered slabs during rolling in a pilot rolling experiment were analyzed in detail using the finite element method. The results showed that the crease formed on the lateral side near the edge of the plate as a result of uneven stress during broadside rolling. The creases rose to the surface with unrestricted spread and evolved into a straight edge seam during the subsequent straight rolling. To eliminate the straight edge seam defect, chamfered slabs were developed and investigated for rolling. The use of the chamfered slabs provided two advantages for rolling: the distribution of the temperature near the edge was ameliorated, and the deformation shape was improved by the chamfered shape. As a result, the risk of forming a straight edge seam defect was reduced by the use of a chamfered slab.
Similar content being viewed by others
References
G. Krauss, S. W. Thompson, ISIJ Int. 35 (1995) 937–945.
P. Hu, H. Zhang, M. L. Wang, Mater. Trans. 56 (2015) 2095–2097.
Z. W. Ma, H. Zhang, P. Hu, Chinese J. Eng. 37 (2015) 1630–1636.
K. Kohno, Tetsu-to-Hagané 73 (1987) S1062–S1062.
S. J. Lee, J. W. Choi, Metall. Res. Technol. 5 (2008) 127–135.
S. Moir, J. Preston, J. Mater. Process. Technol. 125 (2002) 720–724.
C. G. Sun, G. S. Lee, ISIJ Int. 461 (2006) 93–99.
H. Yamaguchi, Y. Kusaba, Tetsu-to-Hagané 82 (1996) 58–63.
Y. X. Wang, H. L. Yu, X. H. Liu, J. Iron Steel Res. 21 (2009) No. 12, 14–16.
G. R. Johnson, W. H. Cook, Eng. Fract. Mech. 21 (1985) 31–43.
P. Hu, H. Zhang, M. L. Wang, Metall. Res. Technol. 508 (2015) 1–10.
T. Altan, H. L. Gegel, Metal Forming: Fundamentals and Application, American Society for Metals, Metals Park, OH, 1983.
A. Silvonen, M. Mahnen, A. S. Korhonen, Scand. J. Metall. 16 (1987) 103–109.
S. Serajzadeh, Mater. Sci. Technol. 21 (2005) 93–97.
I. Tadanobu, Y. Akira, Y. Jun, Mater. Lett. 106 (2013) 37–40.
N. Yukawa, Y. Yoshida, Tetsu-to-Hagané 92 (2006) 661–666.
H. Zhang, C. Z. Yang, M. L. Wang, H. B. Tao, H. P. Liu, X. B. Wang, J. Iron Steel Res. Int. 22 (2015) No. 2, 99–105.
P. Hu, H. Zhang, M. L. Wang, Metall. Res. Technol. 104 (2015) 1–10.
M. L. Wang, C. Z. Yang, H. B. Tao, H. Zhang, J. H. Liu, Y. M. Wu, Iron and Steel 47 (2012) No. 10, 27–33.
J. X. Cao, H. B. Tao, H. Zhang, M. W. Zhou, L. Z. Zhang, M. Y. Peng, Iron and Steel 48 (2013) No. 11, 4347.
F. F. Ren, H. Zhang, W. N. Wang, M. L. Wang, Iron and Steel 50 (2015) No. 4, 27–33.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by National Natural Science Foundation of China (51204059)
Rights and permissions
About this article
Cite this article
Zhang, H., Hu, P. & Wang, Ml. Mechanism and Improvement of Straight Edge Seam Defect on Hot-rolled Plate Surfaces through Use of Chamfered Slabs. J. Iron Steel Res. Int. 23, 539–546 (2016). https://doi.org/10.1016/S1006-706X(16)30085-1
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(16)30085-1