Abstract
For high strength interstitial free (IF) steel containing P element, the salt and pepper (SP) defects exist on the strip surface and could not be eliminated effectively by optimizing the hot rolling process, such as temperature and cooling water. The combination effect of Si and P on the characteristic of tertiary scale has been studied comprehensively by scanning electron microscopy (SEM) and electron probe microanalysis (EPMA), and the concept is proposed firstly that Si and P are of combination effect which can be utilized to eliminate the SP defect. The results show that the SP defects were induced by the rolled-in scale during finish rolling. P can be enriched at the interface between substrate and tertiary scale, which is easy to decrease the adhesion of tertiary scale. However, Si enrichment at the interface between substrate and tertiary scale can increase the adhesion. The SP defects can be eliminated completely, which is attributed to the accompanying enrichment of Si and P.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
X. J. Liu, G. M. Cao, Y. Q. He, T. Jia, Z. Y. Liu, J. Iron Steel Res. Int. 20 (2013) No. 11, 73–78.
X. J. Hu, B. M. Zhang, S. H. Chen, F. Fang, J. Q. Jiang, J. Iron Steel Res. Int. 20 (2013) No. 1, 47–52.
X. J. Liu, G. M. Cao, Y. Q. He, M. Yang, Z. Y. Liu, J. Iron Steel Res. Int. 21 (2014) No. 1, 24–29.
S. Liu, H. B. Wu, X. Li, H. T. Jiang, D. Tang, J. Iron Steel Res. Int. 21 (2014) No. 2, 215–221.
W. H. Zhou, F. S. Du, J. Iron Steel Res. Int. 9 (2002) No. 2, 21–23.
V. V. Basabe, J. A. Szpunar, ISIJ Int. 44 (2004) 1554–1559.
J. Kennedy, M. Evans, F. Robinson, J. Mater. Process. Technol. 212 (2012) 1622–1630.
K. Min, K. Kim, S. K. Kim, D. J. Lee, Met. Mater. Int. 18 (2012) 341–348.
M. Zhang, G. Shao, Mater. Sci. Eng. A 452–453 (2007) 189–193.
X. J. Liu, G. M. Cao, D. M. Nie, Z. Y. Liu, J. Iron Steel Res. Int. 20 (2013) No. 8, 54–59.
Y. L. Yang, C. H. Yang, S. N. Lin, C. H. Chen, W. T. Tsai, Mater. Chem. Phys. 112 (2008) 566–571.
G. M. Cao, X. J. Liu, B. Sun, Z. Y. Liu, J. Iron Steel Res. Int. 21 (2014) No. 3, 335–341.
H. Okada, T. Fukagawa, H. Ishihara, A. Okamoto, M. Azuma, Y. Matsuda, ISIJ Int. 35 (1995) 886–891.
C. H. Zhou, H. T. Ma, L. Wang, J. Iron Steel Res. Int. 17 (2010) No. 2, 27–30.
S. J. Seo, K. Asakura, K. Shibata, ISIJ Int. 37 (1997) 240–249.
S. Taniguchi, K. Yamamoto, D. Megumi, T. Shibata, Mater. Sci. Eng. A 308 (2001) 250–257.
T. Fukagawa, H. Okada, Y. Maehara, ISIJ Int. 34 (1994) 906–911.
E. El-kashif, K. Asakura, K. Shibata, ISIJ Int. 43 (2003) 2007–2014.
Z. M. Cao, K. P. Wu, Z. Y. Qiao, G. W. Du, Acta Phys. Chim. Sin. 28 (2012) 37–43.
T. Kizu, Y. Nagataki, T. Inazumi, Y. Hosoya, ISIJ Int. 41 (2001) 1494–1501.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yu, Y., Wang, C., Wang, L. et al. Combination Effect of Si and P on Tertiary Scale Characteristic of Hot Rolled Strip. J. Iron Steel Res. Int. 22, 232–237 (2015). https://doi.org/10.1016/S1006-706X(15)60035-8
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(15)60035-8