Abstract
The FeSiBC amorphous powder cores were fabricated using powders of the FeSiBC amorphous ribbons which were mechanically crushed for a short time, and the relationship between magnetic properties and powder particle sizes was evaluated. The saturation magnetization Bs of the amorphous Fe82Si2B15C1 alloy was 1.62 T, which provided a superior dc-bias property for the powder cores. Meanwhile, a stable permeability up to high frequency range over 10 MHz and the low core loss of 400 kW/m3 at f = 50 kHz and Bm = 0.1 T were obtained. These excellent high-frequency magnetic properties of the FeSiBC amorphous powder cores could be attributed to the effective electrical insulation between the FeSiBC amorphous powders made by mechanical crushing.
Similar content being viewed by others
References
K. Suzuki, N. Kataoka, A. Inoue, Mater. Trans. JIM. 31 (1990) 743–746.
K. Suzuki, A. Makino, A. Inoue, J. Appl. Phys. 70 (1991) 6232–6237.
M. A. Willard, D. E. Laughlin, M. E. Mchenry, J. Appl. Phys. 84 (1998) 6773–6777.
Y. Kawamura, A. Inoue, T. Masumoto, Jpn. J. Appl. Phys. 35 (1996) 828–830.
S. Yoshida, T. Mizushima, T. Hatanai, IEEE Trans. Magn. 36 (2000) 3424–3426.
G. H. Kim, T. H. Noh, G. B. Choi, J. Appl. Phys. 93 (2003) 7211–7213.
Y. Ogawa, M. Naoe, Y. Yoshizawa, J. Magn. Magn. Mater. 304 (2006) 675–678.
A. Makino, H. Men, T. Kubota, IEEE. Trans. Magn. 45 (2009) 4302–4305.
M. Yagi, I. Endo, I. Otsuka, H. Yamamoto, J. Magn. Magn. Mater. 215–216 (2000) 84–87.
S. Yoshida, T. Mizushima, T. Hatanai, A. Inoue, IEEE Trans. Magn. 36 (2000) 3424–3426.
I. Otsuka, K. Wada, Y. Maeta, IEEE Trans. Magn. 44 (2008) 3891–3893.
S. Tang, H. Wang, Z. Wang, Metallic Functional Materials 17 (2010) No. 3, 9–12.
X. Wang, C. Lu, F. Guo, J. Magn. Magn. Mater. 324 (2012) 2727–2730.
J. Sort, D. C. Ile, A. P. Zhilyaev, Scripta Mater. 50 (2004) 1221–1224.
R. Nowosielski, J. J. Wyslocki, I. Wnuk, J. Mater. Process. Technol. 175 (2006) 324–326.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by National Natural Science Foundation of China (51071050)
Rights and permissions
About this article
Cite this article
Wang, Xy., Lu, Zc., Lu, Cw. et al. Magnetic Properties of FeSiBC Amorphous Alloy Powder Cores Using Mechanical-Crushed Powder. J. Iron Steel Res. Int. 21, 1055–1058 (2014). https://doi.org/10.1016/S1006-706X(14)60183-7
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(14)60183-7