Abstract
The hot deformation characteristics of ductile iron are studied in the temperature range of 973 to 1273K and strain rate range of 0. 001 to 1 s−1 by using hot compression tests. Processing maps for hot working are developed on the basis of the variations of efficiency of power dissipation with temperature and strain rate. The results reveal that the flow stress of ductile iron is sensitive to strain rate. In the processing map under strain of 0.7, a domain is centered at 1 273 K and 1 s−1, and the maximum efficiency is more than 36%. According to the maps, the zone with the temperature range of 1173 to 1 273 K and strain rate range of 0. 1 to 1 s−1 may be considered as the optimum region for hot working.
Similar content being viewed by others
References
Labrecque C, Gagne M. Ductile Iron: Fifty Years of Continuous Development [J]. Canadian Metallurgical Quarterly, 1998, 26: 232.
EL-Bitar T, EL-Banna E. Contribution of Forming Parameters on the Properties of Hot Rolled Ductile Cast Iron Alloys [J]. Mater Lett, 1997, 31: 145.
Zhao X, Jing T F. Morphology of Graphite in Hot-Compressed Nodular Iron [J]. J Mater Sci, 2004, 39: 6093.
Raj Rishi. Development of a Processing Map for Use in Warm-Forming and Hot Forming Processes [J]. Metall Trans, 1981, 12A: 1089.
Prasad Y V R K, Sasidhara S. Hot Working Guide: a Compendium of Processing Maps [M]. Materials Park: ASM International, 1997.
XIONG Yi, CAI Da-yong, ZHAO Sheng-li, et al. Hot Deformation Behavior of Low Carbon Steel [J]. Hot Working Tech, 2008, 37(18): 14 (in Chinese).
Al Omar A, Cabrera J M, Prado J M. Characterization of the Hot Deformation in a Microalloyed Medium Carbon Steel Using Processing Maps [J]. Scripta Materialia, 1996, 34(8): 1301.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by National Natural Science Foundation of China and Baosteel (50271061, 50371074)
Rights and permissions
About this article
Cite this article
Zhao, X., Yang, Xl. & Jing, Tf. Processing Maps for Use in Hot Working of Ductile Iron. J. Iron Steel Res. Int. 18, 48–51 (2011). https://doi.org/10.1016/S1006-706X(11)60049-6
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(11)60049-6