Austenite grain growth behavior of X80 pipeline steel in heating process
- 2 Downloads
Through changing soaking temperature and soaking time, austenite grain growth behavior of X80 pipeline steel under different heating conditions was studied. Relationships of average grain size to soaking temperature and time were obtained respectively. The results show that the prior austenite grains grow with the increase of soaking temperature and time. When soaking temperature is lower than 1180 °C, austenite grain size and growth rate are small; when it higher than 1200 °C, austenite grains grow rapidly and abnormal grain growth appears. For soaking at 1180 °C. austenite grain growth rate is initially high and then decreases when soaking time exceeds 1 h.
Key wordssoaking temperature soaking time grain growth grain size
Unable to display preview. Download preview PDF.
- REN Ji-tang, ZHU Li-guang. Theory and Experience of Continuous Casting and Rolling [M]. Beijing: Metallurgical Industry Press, 2002 (in Chinese).Google Scholar
- Tamura I, Ouchi C, Tanaka T, et al. Thermomechanical Processing of High Strength Low Alloy Steels [M]. London: Butthrtworth & Co Ltd, 1988.Google Scholar
- SU De-da. Influence of Original Structures on Austenitic Grain Growth of T10A Steel [J]. Steel Wire Products, 2004, 30(4): 45.Google Scholar
- Sellars C M, Whiteman J A. Recrystallization and Grain Growth in Hot Rolling [J]. Metal Science, 1979(3–4): 87.Google Scholar
- ZHONG Yun-long, LIN Guo-quan, and LIU Sheng-xin. Austenite Grain Growth Behavior of Steel 33Mn2V Designed for Oil-Well Tubes [J]. Acta Metallurgica Sinica, 2003, 39(7): 699.Google Scholar
- YONG Qi-long. Secondary Phases in Steels [M]. Beijing: Metallurgical Industry Press, 2006 (in Chinese).Google Scholar