Analysis of microstructure characteristics and precipitation behavior of automobile beam steels produced by compact strip production
The microstructure characteristics and precipitation behavior of automobile beam steels produced by compact strip production (CSP) were investigated by use of scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray energy dispersive spectroscopy. The result shows that the final microstructure is mainly composed of polygonal ferrite and small amount of pearlite, and the average ferrite grain size is about 3–6 μm. Small amount addition Ti to aluminium-killed steel can help to refine (the microstructure and improve the mechanical properties. A large number of fine precipitates have been observed in automobile beam steels. The mean particle size is about 10—30 nm. Remarkable strengthening and grain refinement can be obtained by these nano-particles.
Key wordscompact strip production microstructure precipitation behavior
Unable to display preview. Download preview PDF.
- Flemming G, Hensger K. Extension of Product Range and Perspectives of CSP Technology [J]. MPT Inter, 2000(1): 54.Google Scholar
- Yu H, Ren H, Kang Y L. Carbon Diffusion in Hot Strips of Low Carbon Steel Produced by CSP Line Under Different Thermal Histories [J]. J Mater Sci Technol, 2005, 21(1): 21.Google Scholar
- Kang Y L, Yu H, Fu J. Morphology and Precipitation Kinetics of A1N in Hot Strip of Low Carbon Steel Produced by Compact Strip Production [J]. Mater Sci Eng, 2003(351): 265.Google Scholar
- Yu H, Kang Y L, Wang K L. Study of Mechanism on Micro-structure Refinement During Compact Strip Production Process [J]. Mater Sci Eng, 2003(363): 86.Google Scholar
- Gardiola B, Humbert M, Esling C. Determination and Prediction of the Inherited Ferrite Texture in a HSLA Steel Produced by Compact Strip Production [J]. Mater Sci Eng, 2001(303): 60.Google Scholar
- Yu H, Kang Y L, Xiong X Y. Quantitative Analysis on Strengthening Mechanism of Ultra-Thin Hot Strip of Low Carbon Steel Produced by CSP Technique [J]. J Univ Sci Technol Beijing, 2004, 11(5): 425.Google Scholar
- Kang Y L, Wang K L, Yu H. Microstructure Evolution and Precipitation Behavior of Low Carbon Steel Hot Strips Produced by CSP [J]. J Univ Sci Technol Beijing, 2004, 11(4): 364.Google Scholar
- Zhang L, Yang W Y, Zheng W W. Carbides/Nitrides Precipitates in a C-Mn Strip by CSP Technology [J]. J Univ Sci Technol Beijing, 2005, 12(6): 517.Google Scholar