Principle and practice of high nitrogen steel melting by blowing ammonia gas
During the high nitrogen steel (HNS) melting process, the absorption reaction of nitrogen in the liquid steel by blowing NH3 and N2 was investigated respectively. In order to obtain higher content of nitrogen in steel, the liquid steel should be deoxidized and desulfurized because the oxygen and sulfur as surface activity element are not favorable to the absorption of nitrogen in melting process. Based on the metallurgical thermodynamics, the coupling reaction of NH3 with oxygen can improve the generation of activity nitrogen atom in liquid steel. Nitrogen atom is easier to be absorbed than nitrogen molecule. At the same time, blowing ammonia gas can remove the oxygen from liquid steel and decrease the inclusion in the steel. Experiments of HNS melting were carried out in a 10kg induction furnace. and the results indicated that for liquid steel containing the same content of alloys and blowing the same mole of nitrogen, the absorption effect of nitrogen by blowing NH3 is obviously higher than that of blowing N2. The technical process of melting HNS by blowing NH3 under normal pressure is feasible in industrial production.
Key wordshigh nitrogen steel blowing NH3 couple reaction
Unable to display preview. Download preview PDF.
- Rashev T. High Nitrogen Steels-Metallurgy Under Pressure [M]. New York: Academic Publishing House, 1995.Google Scholar
- Gaviljuk V G, Berus H. High Nitrogen Steel: Structure, Properties, Manufacture, Applications [M]. Berlin: Heidberg Press, 1990.Google Scholar
- Lula R A. Manganese Stainless Steels [M]. Paris: The Manganese Centre, 1986.Google Scholar
- Simmons Overbiew. High-Nitrogen Alloying of Stainless Steel [J]. Materials Science and Engineering, 1996(207): 159.Google Scholar
- Delong W B. Effect of Nitrogen in Stabilizing Austenite Phase [J]. Metal Process, 1960(11): 98.Google Scholar
- Kamachi Mudali, Baldev Raj. High Nitrogen Steels and Stainless Steels Manufacturing Properties and Applications [M]. New Delhi: Narosa Publishing House, 2004.Google Scholar
- Uggowitzer P J, Harzenmoser M. Strengthening of Austenitic Steels by Nitrogen [M]. London: The Institute of Metals, 1989.Google Scholar
- ZHANG Ming-ke. Research of Process of Containing Nitrogen Stainless Steelmaking [D]. Beijing: University of Science and Technology Beijing, 2006.Google Scholar
- JIANG Zhou-hua. Calculation and Measurements of Nitrogen Contents in Austenitic Stainless Steel Melts by Bubbling Nitrogen Gas [C] // Proceedings of Second International Conference on Advanced Structural Steels. Shanghai: The Chinese Society for Metals, 2004: 852.Google Scholar
- Rawers J C, Dunning J S, Asai G. Characterization of Stainless Steels Melted and High Nitrogen Pressure [J]. Metall Trans A, 1992(23): 2061.Google Scholar