Physical simulation of hot deformation and microstructural evolution for 42CrMo4 steel prior to direct quenching

  • A H Meysami
  • R Ghasemzadeh
  • S H Seyedein
  • M R Aboutalebi
  • R Ebrahimi
  • M Javidani
Article

Abstract

Direct quenching and tempering (DQ-T) of hot rolled steel section has been widely used in steel mill for the sake of improvement of mechanical properties and energy saving. Temperature history and microstructural evolution during hot rolling plays a major role in the properties of direct quenched and tempered products. The mathematical and physical modeling of hot forming processes is becoming a very important tool for design and development of required products as well as predicting the microstructure and the properties of the components. These models were mostly used to predict austenite grain size (AGS), dynamic, meta-dynamic and static recrystallization in the rods immediately after hot rolling and prior to DQ process. The hot compression tests were carried out on 42CrMo4 steel in the temperature range of 900–1100 °C and the strain rate range of 0.05–1 s−1 in order to study the high temperature softening behavior of the steel. For the exact prediction of flow stress, the effective stress-effective strain curves were obtained from experiments under various conditions. On the basis of experimental results, the dynamic recrystallization fraction (DRX), AGS, hot deformation and activation energy behavior were investigated. It was found that the calculated results were in good agreement with the experimental flow stress and microstructure of the steel for different conditions of hot deformation.

Key words

42CrMo4 steel hot compression test dynamic recrystallization hot deformation direct quenching physical simulation 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Chang W S. Microstructure and Mechanical Properties of 780 MPa High Strength Steels Produced by Direct-Quenching and Tempering Process [J]. Journal of Material Sscience, 2002, 37 (4): 1973.CrossRefGoogle Scholar
  2. [2]
    Wang F, Zhu Q, Lin J, et al. Prediction of Microstructural Evolution in Hot Rolling [J]. Journal of Materials Processing Technology, 2006, 177(3): 530.CrossRefGoogle Scholar
  3. [3]
    Bontcheva N, Petrov P, Petzov G, et al. Finite Element Simulation of Strain Induced Austenite-Martensite Transformation and Fine Grain Production in Stainless Steel [J]. Computational Materials Science, 2006, 40(1): 90.CrossRefGoogle Scholar
  4. [4]
    Lee H-W, Kwon H-C, Im Y-T, et al. Numerical Investigation of Austenite Grain Size Distribution in Square-Diamond Pass Hot Bar Rolling [J]. Journal of Materials Processing Technology, 2007, 191(3): 114.CrossRefGoogle Scholar
  5. [5]
    Toloui M, Serajzadeh S. Modeling Recrystallization Kinetics During Hot Rolling of AA5083 [J]. Journal of Materials Processing Technology, 2007, 184(2): 345.CrossRefGoogle Scholar
  6. [6]
    Kim Sung-I, Lee Youngseog, Lee Duk-lak, et al. Modeling of AGS and Recrystallized Fraction of Microalloyed Medium Carbon Steel During Hot Deformation [J]. Materials Science and Engineering, 2003, 355A(1): 384.CrossRefGoogle Scholar
  7. [7]
    Grass H, Krempaszky C, Reip T, et al. 3-D Simulation of Hot Forming and Microstructure Evolution [J]. Computational Materials Science, 2003, 28(3): 469.CrossRefGoogle Scholar
  8. [8]
    Liu Z Y, Wang W D, Gao W. Prediction of the Mechanical Properties of Hot-Rolled C-Mn Using Artificial Neural Networks [J]. Journal of Materials Processing Technology, 1996, 57(4): 332.CrossRefGoogle Scholar
  9. [9]
    Dyja H, Korczak P. The Thermal-Mechanical and Microstructural Model for the FEM Simulation of Hot Plate Rolling [J]. Journal of Materials Processing Technology, 1999, 93(3): 463.CrossRefGoogle Scholar
  10. [10]
    Kim S T, Yoo Y-C. Prediction of Dynamic Recrystallization Behavior of AISI Type 4130 Medium Carbon Steel [J]. Materials Science and Technology, 2002, 18(3): 160.CrossRefGoogle Scholar
  11. [11]
    Hodgson P D. Mathematical Modeling of Recrystallization Process During Hot Rolling of Steels [D]. Queensland: University of Queensland, 1993.Google Scholar
  12. [12]
    Hodgson P D, Gibbs R K. A Mathematical Model to Predict the Mechanical Properties of Hot Rolled C-Mn and Microalloyed Steels [J]. ISIJ Int, 1992, 32(6): 1329.CrossRefGoogle Scholar

Copyright information

© China Iron and Steel Research Institute Group 2009

Authors and Affiliations

  • A H Meysami
    • 1
  • R Ghasemzadeh
    • 1
  • S H Seyedein
    • 1
  • M R Aboutalebi
    • 1
  • R Ebrahimi
    • 2
  • M Javidani
    • 2
  1. 1.Department of Material Science and EngineeringIran University of Science and TechnologyTehranIran
  2. 2.Department of Material Science and EngineeringSabzevar Tarbiat-Moallem UniversitySabzevarIran

Personalised recommendations