Textures and properties of hot rolled high strength Ti-IF steels

  • Yan-hui Guo
  • Zhao-dong Wang
  • Wen-wen Zou
  • Xiang-hua Liu
  • Guo-dong Wang
Article

Abstract

The texture evolution in a high strength Ti-IF steel during the processing of hot rolling, cold rolling, and annealing is studied. For comparison, both ferrite rolling and austenite rolling are employed. It is found that the texture type is the. same after ferrite rolling and austenite rolling, but the texture intensity is much higher in the ferrite rolled sample. Furthermore, texture characteristics at the surface are absolutely different from those at the mid-section in both ferrite rolled and austenite rolled samples, as well as under the cold rolled and annealed conditions. The shear texture {110}<001> disappears and orientation rotates along {110}<001<→{554}<225>→{111}<112>→ {111}<110>→{223}<110> during cold rolling. Compared to the austenite rolled sample, the properties of the cold rolled and annealed sheet which is subjected to ferrite rolling are higher.

Key words

high strength Ti-IF steel ferrite rolling austenite rolling texture 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    KANG Yong-lin. Quality Control and Formability of Modern Automobile Sheet [M]. Beijing: Metallurgical Industry Process, 1999 (in Chinese).Google Scholar
  2. 2.
    WANG Zuo-cheng. Stuy on the Effect of Metallurgical Factors on the Microstructure and Properties of Ultra-Low Carbon High Strength IF Steel [D]. Beijing: University of Science and Technology Beijing, 1994 (in Chinese).Google Scholar
  3. 3.
    Juntunen P, Raabe D, Karjalainen P, et al. Optimizing Continuous Annealing of Interstitial-Free Steels for Improving Deep Drawability [J]. Metallurgical and Materials Transactions: Physical Metallurgy and Materials Science, 2001, 32A(8): 1989.CrossRefGoogle Scholar
  4. 4.
    Tung Lam Kai, Quadir M Z, Duggan B J. A Novel Rolling-Annealing Cycle for Enhanced Deep Drawing Properties in IF Steels [J]. Key Engineering Materials, 2002, 233–236(I): 437.Google Scholar
  5. 5.
    Tomitz Andreas, Kaspar Radko. Deep-Drawable Thin-Gauge Hot Strip of Steel as a Substitution for Cold Strip [J]. ISIJ International, 2000, 40(9): 927.CrossRefGoogle Scholar
  6. 6.
    WANG Zhao-dong, GUO Yan-hui, ZHAO Zhong, et al. Developing an Ultra-Low Carbon Deep-Drawing Sheet Steel by Ferritic Hot Rolling Process [J]. Journal of Northeastern University, 2005, 26(8): 747 (in Chinese).Google Scholar
  7. 7.
    Zhao H, Rama S C, Barber G C, et al. Experimental Study of Deep Drawability of Hot Rolled IF Steel [J]. Journal of Materials Processing Technology, 2002, 128(1–3): 73.CrossRefGoogle Scholar
  8. 8.
    Saitoh H, Ushtoda K, Senuma T, et al. Structural and Textural Evolution During Subsequent Annealing of Steel Sheet Hot-Rolling in α Phase [A]. Tamura I, eds. THERMEC’ 88 [C]. Tokyo: The Iron and Steel Institute of Japan, 1988. 628.Google Scholar
  9. 9.
    Senuma T, Yada H. Texture and Deep Drawability of Low and Ultra Low Carbon Steel Sheet Hot Rolled Below Ar3 Temperature [A]. Tamura I, eds. THERMEC’ 88 [C]. Tokyo: The Iron and Steel Institute of Japan, 1988. 636.Google Scholar
  10. 10.
    ZHANG Hong-mei, LIU Ying-yi, JIANG Qi-wu. Effect of Deformation Temperature on Strain-Stress Curve and Micro-structure for High Strength IF Steel [J]. Hot Working Technology, 2006, 35(1): 75 (in Chinese).Google Scholar
  11. 11.
    Yong-Joon Roe R. Description of Crystallite Orientation in Polycrystalline Materials. III General Solution to Pole Figure Inversion [J]. Journal of Applied Physics, 1965, 36(6): 2024.CrossRefGoogle Scholar
  12. 12.
    Ray R K, Jonas J J, Hook R E. Cold Rolling and Annealing Textures in Low Carbon and Extra Low Carbon Steels [J]. International Materials Reviews, 1994, 39(4): 129.CrossRefGoogle Scholar
  13. 13.
    MAO Wei-min. Crystallography Texture and Anisotropy of Metal Materials [M]. Beijing: Science Process, 2002 (in Chinese).Google Scholar
  14. 14.
    Toth L S, Jonas J J, Dnaiel D, et al. Development of Ferrite Rolling Textures in Low- and Extra Low-Carbon Steels [J]. Metall Trans, 1990, 21A(11): 2985.CrossRefGoogle Scholar
  15. 15.
    Raphanel J L, van Houtte P. Simulation of the Rolling Textures of BCC Metals by Means of the Relaxed Taylor Theory [J]. Acta Metallurgica, 1985, 33(8): 1481.CrossRefGoogle Scholar
  16. 16.
    Arminjon M. Theory of a Class of Heterogeneous Taylor Models. Application to Deformation Textures of Steels [J]. Acta Metallurgica, 1987, 35(3)a: 615.CrossRefGoogle Scholar
  17. 17.
    Gilormini P. The Theory of Rate Sensitive Pencil Glide Application to Rolling Textures [J]. Acta Metallurgica, 1989, 37 (7): 2093.CrossRefGoogle Scholar

Copyright information

© China Iron and Steel Research Institute Group 2008

Authors and Affiliations

  • Yan-hui Guo
    • 1
  • Zhao-dong Wang
    • 1
  • Wen-wen Zou
    • 1
  • Xiang-hua Liu
    • 1
  • Guo-dong Wang
    • 1
  1. 1.State Key Laboratory of Rolling and AutomationNortheastern UniversityShenyang, LiaoningChina

Personalised recommendations