Process simulation and microstructure analysis of low carbon Si-Mn quenched and partitioned steel

  • Cai Zhao
  • Di Tang
  • Hai-tao Jiang
  • Song-shan Zhao
  • Hui Li
Article

Abstract

The quenching and partitioning (Q&P) process was experimentally investigated on the thermomechanical simulator (Gleeble3800). The microstructure and fracture mechanism of the sheets were investigated by means of TEM. It was found that the microstructure of quenched and partitioned steel consists of fine lath martensite and thin inter-lath austenite films. The optimum quenching temperature of producing the maximum amount of retained austenite after final quenching at room temperature was predicted by Matlab software package. It was found that the calculations by Matlab software can provide guidance for experimental processing design reliably. The volume fraction of retained austenite at room temperature was approximately 8%, which was measured easily by the software VC6.0++ programming. The results verified that quenched and partitioned steel possesses a good combination of strength and plasticity due to its fine microstructure. This steel exhibited high ultimate tensile strength (exceeding 1000 MPa) and good elongation of 25%. The results showed that the fracture mechanism of the sheets is typical tough fracture under the condition of tensile failure.

Key words

Q&P Matlab software microstructures mechanical property 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    MI Zhen-li, TANG Di, YAN Ling, et al. High-Strength and High-Plasticity TWIP Steel for Modern Vehicle [J]. Material Science and Technology, 2005, 21(4): 451.CrossRefGoogle Scholar
  2. 2.
    Speer J G, Streicher A M, Matlock D K, et al. Quenching and Partitioning: a Fundamentally New Process to Create High Strength TRIP Sheet Microstructures [A]. The Thermodynamics, Kinetics, Characterization and Modeling of Austenite Formation and Decomposition [C]. Chicago: Minerals Metals and Mater, 2003. 502.Google Scholar
  3. 3.
    Gerdemann F L H, Speer J G, Matlock D K. Microstructure and Hardness of Steel Grade 9260 Heat-Treated by the Quenching and Partitioning (Q&P) Process [A]. Materials Science and Technology [C]. New Orleans: Association for Iron and Steel Technology, 2004. 439.Google Scholar
  4. 4.
    Speer J G, Edmonds D V, Rizzo F C. Partitioning of Carbon From Supersaturated Plates of Ferrite, With Application to Steel Processing and Fundamentals of the Bainite Transformation [J]. Current Opinion in Solid State and Materials Science, 2004, 8(3): 219.CrossRefGoogle Scholar
  5. 5.
    Clarke A, Speer J G, Matlock D K, et al. Microstructure and Carbon Partitioning in a 0.19% C-1.59% Mn-1. 63% Si Trip Sheet Steel Subjected to Quenching and Partitioning [A]. Proceedings of an International Conference on Solid-Solid Phase Transformations in Inorganic Materials [C]. Phoenix: TMS, 2005. 99.Google Scholar
  6. 6.
    Matlock D K, Bräutigam V E, Speer J G. Application of the Quenching and Partitioning (Q&P) Process to a Medium-Carbon, High-Si Micro-Alloyed Bar Steel [J]. Materials Science Forum, 2003, 426–432(2): 1089.CrossRefGoogle Scholar
  7. 7.
    Speer J G, Rizzo F C, Matlock D K, et al. The “Quenching and Partitioning” Process: Background and Recent Progress [J]. Materials Research, 2005, 8(4): 417.CrossRefGoogle Scholar
  8. 8.
    Matlock D K, De Cooman B C, Schroth J G, et al. Carbon Partitioning Into Austenite After Martensite Transformation [J]. Acta Materialia, 2003, 51(9): 2611.CrossRefGoogle Scholar

Copyright information

© China Iron and Steel Research Institute Group 2008

Authors and Affiliations

  • Cai Zhao
    • 1
    • 2
  • Di Tang
    • 1
  • Hai-tao Jiang
    • 1
  • Song-shan Zhao
    • 1
  • Hui Li
    • 1
  1. 1.National Engineering Research Center for Advanced Rolling TechnologyUniversity of Science and Technology BeijingBeijingChina
  2. 2.College of Materials Science and EngineeringTaiyuan University of Science and TechnologyTaiyuan, ShanxiChina

Personalised recommendations