Copper distribution and oxidation states near corroded fasteners in treated wood
- 220 Downloads
Metal fasteners are used to hold wood structures together. In outdoor applications, these fasteners are subject to corrosion when the wood is treated with certain preservative treatments. Typically, these treatments contain copper. Prior work has hypothesized that the mechanism of corrosion in treated wood involves reduction of copper ions from the wood treatments. However, copper was rarely detected in the corrosion products of metals embedded in treated wood, which contradicts the hypothesized mechanism. This present work utilizes synchrotron based X-ray fluorescence microscopy (XFM) and X-ray absorption near edge spectroscopy to examine the corrosion mechanism in treated wood by looking at the spatial distribution and oxidation states of copper in the treated wood near the fastener and in the corrosion products removed from the fastener surface. The samples were obtained after a 1-year corrosion test. In the wood cell walls, the oxidation state of the copper treatment did not change in the immediate vicinity of the fastener, although there was a depletion of copper near the fastener. Furthermore, copper was detected in the corrosion products in trace amounts using XFM. Together, these techniques confirm that the corrosion mechanism involves transport of the cupric ions to the fastener surface, where they are reduced and suggest that previous attempts to detect copper were unsuccessful because the concentration of copper in the corrosion products was below the level of detection of the previously used techniques.
KeywordsX-ray fluorescence microscopy (XFM) X-ray absorption near edge spectroscopy (XANES) Preservative treated wood Corrosion Copper
Metal fasteners are frequently used to hold wood structures together. While in general wood is not a corrosive material, in certain situations wood can cause corrosion of metal fasteners which can lead to structural failures [1, 2]. Copper based waterborne wood preservatives are frequently used in the United States to protect the wood from fungal and insect attack [3, 4]. These wood preservatives have been shown to increase the corrosion of metal fasteners [5, 6, 7, 8, 9, 10, 11, 12, 13].
However, despite thermodynamic and kinetic evidence that the corrosion mechanism involves the reduction of cupric ions, copper was not detected in the corrosion products, as expected, in previous studies. Zelinka et al.  utilized energy dispersive X-ray spectroscopy (EDS), scanning electron microscopy (SEM), and powder X-ray diffraction (XRD) to examine the corrosion products of fasteners embedded in treated wood. They found no evidence of copper in the corrosion products using these techniques. This then raised questions about whether the proposed corrosion mechanism was correct and if it was, what was happening to the reduced copper. Possible alternative hypotheses may include (1) that the copper was migrating to the fastener surface but was being reduced in the wood near the metal surface, (2) that the copper was being reduced at the fastener surface but reoxidized in a further reaction step, or (3) that the proposed mechanism was wrong entirely.
In this study, synchrotron based X-ray fluorescence microscopy (XFM) and X-ray absorption near edge spectroscopy (XANES) are employed to better understand the corrosion mechanism of metal fasteners in treated wood. XFM has been used to map out the distribution of ions in wood cell walls down to trace levels with a resolution of approximately 400–600 nm [19, 20, 21, 22, 23], while XANES facilitates the determination of the oxidation state of the metal ions with a similar spatial resolution to XFM. Preliminary studies have shown the possibility of visualizing copper from wood treatments in cell walls as well as determine the oxidation state of copper ions within the cell walls [24, 25]. This present study investigates the distribution and oxidation states of copper ions near the wood-metal interface for wood exposed to steel and hot-dip galvanized steel fasteners and put the findings in context of the broader understanding of corrosion of metals in treated wood.
2 Materials and methods
2.1 Sample preparation
The samples examined came from previous corrosion tests examining the corrosion of metals embedded in treated southern pine (Pinus spp.) [17, 18]. In these experiments, steel and hot-dip galvanized steel fasteners were driven into southern pine and exposed for 1 year at 27 °C (80 °F) close to saturation pressure by placing the wood-metal assemblies over a reservoir of liquid water. The composition of the hot dip galvanized steel coating was found to be over 95 wt% zinc . After the tests were completed, the wood was split using the fasteners as a fulcrum; this allowed the fasteners to be removed from the wood without damaging the corrosion products. The wood was stored under dry (< 50% RH) conditions and the corrosion products were stored in sealed glass vials for several years until they could be examined with XFM.
Preservative treatments examined with their compositions, copper concentrations, and corresponding corrosion rates 
Nominal retention (kg of preservative per m3 of wood)
Actual retention (kg of preservative per m3 of wood)a
Bulk copper concentration (kg of copper per m3 of wood)
Corrosion Rate (µm year−1)b
MCQ Micronized copper quaternary
66.7 wt% CuO
33.3 wt% DDACc
ACQ Alkaline copper quaternary (type D)
66.7 wt% CuO
33.3 wt% DDAC
CA Copper azole (type C)
96.1 wt% CuO
1.95 wt% Tebuconazole
1.95 wt% Propiconazole
CCA Chromated copper arsenate (type C)
47.5 wt% CrO3
18.5 wt% CuO
34.0 wt% As2O5
To examine the wood using XFM and XANES, the samples were cut into 2 µm thick sections. This was accomplished by first taking the blocks of wood that had been in contact with the fastener and then cutting them into small cubes. These cubes were then placed into a Leica EM UC7 ultramicrotome (Wetzlar, Germany) fitted with a diamond knife and cross sections (transverse sections) were cut dry at room temperature. The sections were then held between two 200 nm–thick low stress Norcada (Edmonton, AB, Canada) silicon nitride windows for the experiments.
The corrosion products were also examined with XFM. These corrosion products were obtained from brushing the surface of the fastener after the corrosion experiment and collecting the debris that was removed in this process. This powder was then spread onto Kapton™ tape (DuPont, Wilmington, DE) and the corrosion products were imaged on the tape.
2.2 Testing methods
XFM was performed at beamline 2-ID-E at the Advanced Photon Source at Argonne National Laboratory with a beam energy of 10.15 keV and a focused beam diameter of 0.6 µm (FWHM). Elemental maps of the wood cell walls were built in 0.5 µm step sizes and a 5 ms dwell time for each step in fly scan mode. Maps of the corrosion products were taken with a beam focused to 0.6 µm diameter, 1 µm steps, and 5 ms dwell times using an aluminum filter to attenuate the beam to prevent X-ray fluorescence detector overload. Data analysis was carried out by the MAPS software package where the full spectra were fit to modified Guassian peaks, the background was iteratively calculated and subtracted, and the elemental quantification is calibrated by a standard reference (RF4-100-S1749, AXO DRESDEN GmbH, Heidenau, Germany) . One section of each sample type was examined due to time limitations of XFM beamtime.
The copper XANES scans were collected at beamline 2-ID-D at the Advanced Photon Source at Argonne National Laboratory and scanned over the copper K-edge (8980 eV) from 8960 to 9040 eV with a step size of 0.5 eV and a beam spot size of 0.2 µm. The dwell time at each energy depended on the relative signal (amount of copper) and ranged from 2 to 10 s per energy step. The dwell time was chosen by the operator prior to each scan. The data were analyzed by exporting the copper fluorescence signal and the upstream ion current from the MAPS software package . The data were then imported into ATHENA (version 0.9.22) where the fluorescence signal was divided by the upstream ion current to create the X-ray absorption coefficient, “µ(E)”, as a function of energy . The µ(E) signal was then baseline corrected in ATHENA to create the normalized µ(E) plots that are presented in the paper. XANES scans were taken in different anatomical features such as the secondary cell wall and the middle lamella. However, the curves taken in these regions showed no differences beyond noise. Therefore, individual scans were merged to form a single curve within Athena to reduce noise.
3 Results and discussion
A range of behaviors can be observed across the different wood preservatives. The interaction of iron and copper is easiest to observe from the composite image. For example, the MCQ sample has red, purple, and blue regions. The cells in the red region show the copper in the cell walls from the preservative treatment. In the purple region, these cells still have most or all of the copper from the wood preservative, but iron from the fastener had diffused in as well. Finally, in the blue region, these cell walls are depleted in copper so only the iron signal is visible. While in the MCQ sample, all three regions are all visible, in the ACQ sample, however, the iron only appears in parts of the cell walls (less than 5 µm from the edge). The majority of this iron rich region also contains copper but there is a small zone on the very edge of the cells that is depleted in copper. For the CA treatment, there is a large copper depleted and iron rich region; there does not appear to be an appreciable overlap between the iron and copper rich regions. For the CCA sample, there is iron throughout the sample, although there is an even higher concentration of iron in the upper right corner of the image. At the same time, the entire section has less copper than the other treatments shown, likely because the CCA treatment uses less copper than the other wood preservative systems examined [3, 14]. The high amount of iron uniformly distributed throughout the sample may be a result of trace impurities in the industrial grade treatment chemicals. In previous work using XFM, cell walls of copper treated wood were found to be uniformly higher in iron and this was attributed to impurities in the treatment . Regardless of the reason for the high iron concentration, the differences in the relative amounts of iron and copper make it difficult to directly compare this image to the other wood preservative treatments. However, when examining the region closest to the chevron, it appears that there are regions of cell wall material that only contain iron and are copper depleted, similar to the other wood preservative systems.
While Figs. 4 and 5 are helpful in visualizing the interplay between the corrosion products in the wood cell wall and the copper concentration from the preservative in the corrosion affected zone, they have several limitations. Firstly, the sections were cut from the wood near the fastener after a corrosion test after the fasteners had been removed. While every effort was made to preserve the wood surface directly adjacent to the fastener, some cells may have been removed during fastener extraction or sectioning of the wood for the microscopy. Because of this, it is impossible to say how far any given image was from the fastener surface and whether differences in copper concentration between treatments represent a quantitative difference between the treatments or whether it was related to from where the sections were cut. These sample preparation issues are in part caused by the fact that the study examined samples from a long term corrosion test using real fasteners. More quantitative results may be possible in a future study by placing prepared wood samples in contact with metal. Furthermore, because of beamline constraints, only one sample could be examined for each condition. Therefore, it is unclear if the observations can be generalized to the wood preservative treatment, or represent only one position along the length of the fastener.
Even with these limitations, Figs. 4 and 5 give an idea of the range of copper and iron interactions that are happening near the fastener surface. In all cases, iron and zinc corrosion products diffused into the wood cell walls. The range of diffusion distances ranged from as small as approximately 10 µm for ACQ treated wood, to over 100 µm in CCA treated wood. Furthermore, in nearly every case, there was a region near the fastener surface that was depleted in copper and these cells were only visible in the XFM maps of iron or zinc. The depth of this copper depleted zone again had a range of observed behaviors from less than or equal to 1 µm in ACQ treated wood to as much as 50 µm for CA treated wood.
The XFM maps in Figs. 4 and 5 are some of the first experimental evidence that test hypothesized mechanism for corrosion in treated wood; namely that the corrosion mechanism involves migration and reduction of copper in the wood preservatives (Fig. 1). From these data it appears that copper from the cell walls immediately adjacent to the fastener has been depleted. It follows that copper should indeed be present in the corrosion products as there is a zone near the fastener surface depleted in copper. Previous measurements on the corrosion products using EDS and powder X-ray diffraction did not detect any copper in the corrosion products . However, from Figs. 4 and 5, the total amount of reduced copper can be estimated and the amount of reduced copper would be too small to measure with those techniques. For example, the CA sample next to the steel fastener had one of the largest zones of copper depletion, 50 µm and the copper in this region was decreased from 0.26 to 0.05 µg cm−2. Assuming that this section was taken directly from the edge of the fastener (radius 1.5 mm) the amount of copper in the corrosion products would be approximately 1 ng per 2 µm of fastener length, which equates to 32 µg for the entire length of the 64 mm fastener . This small amount of copper would likely be undetectable with EDS with a minimum level of detection of 0.1–1 wt%  or powder XRD whose minimum level of detection is approximate 5 wt% .
Figure 7 shows the corrosion products from the galvanized fasteners; again, the shape of the particles can be easily seen from the zinc maps. In Fig. 7, the particles of corrosion products can most clearly be seen in the maps of zinc. Similar to Fig. 6, the scale for the map of copper is 1000 times smaller than that of the zinc concentration. However, in general, there appears to be more copper in the zinc corrosion products (Fig. 7) than in the steel corrosion products (Fig. 6). This can also be seen in the combined images in Fig. 7 where the corrosion products appear as purple objects, meaning that the copper is distributed throughout the zinc particles in the corrosion products.
In almost all cases, the copper oxidation state in the cell walls near the corrosion surface does not change.
Wood cell walls closest to the fastener surface are depleted in copper. Furthermore, iron and zinc corrosion products are able to diffuse into the cell walls.
Based off of the examination of the cell walls, the expected amount of copper in the corrosion products is below the level of detection of commonly used tools to examine corrosion products.
XFM images of the corrosion products confirm the presence of small amounts of copper in the corrosion products collected from steel and galvanized steel fasteners embedded in treated wood.
The use of Advanced Photon Source facilities was supported by the US Department of Energy, Basic Energy Sciences, Office of Science, under Contract Number W-31-109-Eng-38.
This study was funded by the USDA Forest Service, Forest Products Laboratory. The use of Advanced Photon Source facilities was supported by the US Department of Energy, Basic Energy Sciences, Office of Science, under Contract Number W-31-109-Eng-38. This article was written and prepared by US Government employees on official time, and it is therefore in the public domain and not subject to copyright.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 1.Burkholder M (2004) CCA, NFBA, and the post-frame building industry. Frame Build News 16(5):6–12Google Scholar
- 2.Rush FA (2015) Deck collapse-4403 ocean drive. Town of Emerald Isle, Emerald Isle, NCGoogle Scholar
- 3.Lebow S (2004) Alternatives to chromated copper arsenate for residential construction. Res. Pap. FPL-RP-618. U.S.D.A. Forest Service, Forest Products Laboratory, Madison, WIGoogle Scholar
- 4.Lebow S (2010) Wood preservation. In: Ross RJ (ed) Wood handbook—wood as an engineering material. U.S. Department of Agriculture, Forest Service, Forest Products Laboratory, Madison, WI, p 508Google Scholar
- 5.Baker AJ (1988) Corrosion of metals in preservative-treated wood. In: Hamel M (ed) Wood protection techniques and the use of treated wood in construction. Forest Products Society, Madison, pp 99–101Google Scholar
- 6.Baker AJ (1992) Corrosion of nails in CCA- and ACA-treated wood in two environments. For Prod J 42(9):39–41Google Scholar
- 7.Cross JN (1990) Evaluation of metal fastener performance in CCA treated timber. In: Baker JM (ed) Durability of building materials and components. E & FN Spon, LondonGoogle Scholar
- 8.Zelinka SL, Rammer DR (2005) Review of test methods used to determine the corrosion rate of metals in contact with treated wood. Gen. Tech. Rp. FPL-GTR-156. U.S. Department of Agriculture, Forest Service, Forest Products LaboratoryGoogle Scholar
- 13.Zelinka SL, Rammer DR (2011) Synthesis of published and unpublished corrosion data from long term tests of fasteners embedded in wood: calculation of corrosion rates and the effect of corrosion on lateral joint strength. Paper presented at the CORROSION 2011, Houston, TXGoogle Scholar
- 14.Zelinka SL (2014) Chapter 23. corrosion of metals in wood products. In: Aliofkhazraei M (ed) Developments in corrosion protection. InTech, Rijeka, pp 568–592Google Scholar
- 17.Zelinka SL (2009) Mechanism of corrosion in treated wood. University of Wisconsin, MadisonGoogle Scholar
- 20.Jakes JE, Gleber S-C, Vogt S, Hunt CG, Yelle DJ, Grigsby W, Frihart CR (2013) New syncrotron-based technique to map adhesive infiltration in wood cell walls. In: Proceedings of the 36th annual meeting of the Adhesion Society, Datona Beach, FL, March 3–6, 2013Google Scholar
- 22.Kirker G, Zelinka S, Gleber S-C, Vine D, Finney L, Chen S, Hong YP, Uyarte O, Vogt S, Jellison J, Goodell B, Jakes JE (2017) Synchrotron-based X-ray fluorescence microscopy enables multiscale spatial visualization of ions involved in fungal lignocellulose deconstruction. Sci Rep 7:41798. https://doi.org/10.1038/srep41798 CrossRefGoogle Scholar
- 23.Hunt CG, Zelinka SL, Frihart CR, Lorenz L, Yelle D, Gleber S-C, Vogt S, Jakes JE (2018) Acetylation increases relative humidity threshold for ion transport in wood cell walls–a means to understanding decay resistance. Int Biodeterior Biodegrad 133(1):230–237. https://doi.org/10.1016/j.ibiod.2018.06.014 CrossRefGoogle Scholar
- 24.Zelinka SL, Kirker GT, Jakes JE, Passarini L, Lai B (2016) Distribution and oxidation state of copper in the cell walls of treated wood examined by synchrotron based XANES and XFM. In: Proceedings of the 112th annual meeting of the American Wood Protection Association San Juan, PR, 2016. American Wood Protection Association, pp 172–178Google Scholar
- 25.Zelinka SL, Jakes JE, Kirker GT, Passarini L, Lai B (2016) Corrosion of metals in treated wood examined by synchrotron based XANES and XFM. Paper No. 7038. Paper presented at the CORROSION 2016, Vancouver BC, March 6–10, 2016Google Scholar
- 26.Vogt S (2003) MAPS: a set of software tools for analysis and visualization of 3D X-ray fluorescence data sets. J Phys IV 104:635–638Google Scholar
- 28.Zelinka SL, Jakes JE, Tang J, Ohno KM, Bishell AB, Finney L, Maxey ER, Vogt S, Kirker GT (2018) Fungal-copper interactions in wood examined with large field of view synchrotron based X-ray fluorescence microscopy. Wood Mater Sci Eng. https://doi.org/10.1080/17480272.2018.1458049 CrossRefGoogle Scholar
- 30.Williams TJ (2007) A needle in the X-ray haystack: detection limits in powder X-ray diffraction of geolocial materials. In: 2007 GSA denver annual meetingGoogle Scholar