Abstract
Transparent heating film was fabricated with the conductive coating solution including silver nanowire and graphene oxide. Visible transmittance, electric resistance, and heating temperature were analyzed on the as-prepared film. Transparent heating film was fabricated with a resistance value of 100 Ω or less, and the visible transmittance was adjusted at a level of 90% or less according to the loading of Ag nanowire. The heating temperature was stably increased throughout the film up to 100 °C or more in proportion to the applied DC voltage.
Similar content being viewed by others
References
J. Kang, H. Kim, K.S. Kim, S.K. Lee, S. Bae, J.H. Ahn, B.H. Hong, NanoLett. 11(12), 5154 (2011)
Y.-H. Yoon, J.-W. Song, D. Kim, J. Kim, J.-K. Park, S.-K. Oh, C.-S. Han, Adv. Mater. 19, 4284 (2007)
M. Izaki, Electrochem. Solid-State Lett. 1, 215 (1998)
B.E. Aufderheide, M.J. Robrecht, W.R. Kelley, US Patent 4,952,783 (1990)
Y. Li, T. Yang, T. Yu, L. Zheng, K. Liao, J. Mater. Chem. 21(29), 10844 (2011)
M. Erol, E. Celik, Mater. Technol. 47, 25 (2013)
J.E. An, Y.G. Jeong, Eur. Polym. J. 49(6), 1322 (2013)
J.R. Potts, D.R. Dreyer, C.W. Bielawski, R.S. Ruoff, Polymer 52(1), 5 (2011)
B. Krause, R. Boldt, L. Häußler, P. Pötschke, Compos. Sci. Technol. 114, 119 (2015)
W.B. Zhang, Z.X. Zhang, J.H. Yang, T. Huang, N. Zhang, X.T. Zheng, Z.W. Zhou, Carbon 90, 242 (2015)
S.-Y. Park, J.-S. Bae, J.-G. Kim, M.-W. Oh, J. Kim, D.-G. Nam, J.H. Yeum, W. Oh, Polym. Polym. Comp. 24, 315 (2016)
J. Kim, D.-G. Nam, J.H. Yeum, S. Suh, W. Oh, Trans. Electr. Electron. Mater. 16, 274 (2015)
D. Kim, W. Oh, J. Kim, D.-G. Nam, J. Jang, J.-S. Bae, J. Korean Phys. Soc. 65, L429 (2014)
W.S. Hummers, R.E. Offeman, J. Am. Chem. Soc. 80, 1339 (1958)
S. Kim, W. Oh, J.-S. Bae, S.B. Yang, J.H. Yeum, J. Park, C. Sung, J. Kim, J.-C. Shin, Int. J. Polym. Sci. 2019, 3478325 (2019)
Acknowledgements
This work was supported by Dong-Eui University Grant (202003450001). This work was also supported by the Korea Basic Science Institute (KBSI) National Research Facilities and Equipment Center (NFEC) grant funded by the Korean government (Ministry of Education) (No. 2019R1A6C1010045).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Choi, YH., Oh, W. Heating Characteristics of Transparent Films Prepared with Conductive Composite Materials. Trans. Electr. Electron. Mater. 22, 97–102 (2021). https://doi.org/10.1007/s42341-020-00267-z
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s42341-020-00267-z