Phase Degree of Response Voltage and Current Versus Excitation Voltage of the Accelerated Thermally Aged CSPE
- 5 Downloads
As the accelerated thermally aged years of CSPE samples increase, their resistivity and percent elongation decrease. On the other hand, their dissipation factors, glass transition temperatures, and apparent densities increase with increasing ageing times. The phase degree of response current versus excitation voltage of a CSPE sample decreased in agreement with the tendency of resistivity, while the phase degree of response voltage versus excitation voltage increased in agreement with the tendency of conductivity. The variations in temperature for an applied AC voltage are higher than those for a DC voltage.
KeywordsCSPE Percent elongation Dissipation factor Differential temperature between AC and DC voltages Phase degree of response current and response voltage versus excitation voltage Glass transition temperature
This work was supported by Wonkwang University in 2018.
- 3.http://www.lambient.com. The Handbook of Dielectric Analysis and Cur Monitoring, Version 1.0, Lambient Technologies™ L.L.C., 2014. Accessed 9 sept 2017
- 4.http://www.lambient.com. AN11-LT-451 and LCR Meter Comparison and LT-4203 Parallel Plate Test Fixture, Version 1.0, Lambient Technologies™ L.L.C., 2014. Accessed 9 sept 2017
- 5.http://www.lambient.com. Insight-Application Note 2.13 Dielectric Measurement Techniques, Version 1.0, Lambient Technologies™ L.L.C., 2014. Accessed 9 sept 2017
- 6.A.J. Dekker, Electrical Engineering Materials, 3rd edn. (Prentice-Hall Inc, Englewood Cliffs, 1973), pp. 62–78Google Scholar
- 7.http://www.yeonjin.com. TXA™ texture analyzer. Accessed 9 sept 2017
- 8.W.D. Callister Jr., Materials Science and Engineering—An Introduction, 5th edn. (Wiley, Hoboken, 2000), pp. 473–519Google Scholar
- 9.http://kor.mt.com/kr/ko/home/products/LaboratoryAnalyticsBrowse/TAFamilyBrowse.html. Accessed 9 sept 2017
- 10.http://www.aslltd.c.uk. CTH7000, Hand-Hand Thermometer, WIKA, UK. Accessed 9 sept 2017
- 11.J.I. Kim, B.H. Jeon, S.J. Lee, High Voltage Plasma Technology, 1st edn. (Jinsaem, Seoul, 2012), pp. 251–276Google Scholar