Abstract
The effect of a rotating magnetic field (RMF) on the distribution of Al2O3 particles with an Al melt was studied by means of simulation and experiment. The results show that Al2O3 particles (diameter of 1–10 µm, 1wt.%) are significantly agglomerated at the top of ingots when subjected to an RMF, and their distribution is influenced by both the intensity and the duration of RMF application. The optimal separation efficiency is achieved with the magnetic intensity of 12 mT for 120 s. The number of the particles at the bottom and the middle decreases by 64.5% and 69.7%, respectively, while that at the top increases by 242.5% compared to the condition without an RMF. However, if further increase the intensity or the duration of RMF, it can induce turbulent flows that draw some of the separated Al2O3 particles back into the melt, reducing separation efficiency. The calculation results show that as the magnetic intensity increases from 6 mT to 18 mT, the velocity difference between the particles and the Al melt flow quadruples, increasing from 0.013 m·s−1 to 0.066 m·s−1. Driven by this velocity difference, centrifugal motion, and secondary circulation, Al2O3 particles tend to migrate upwards within the melt, facilitating the separation of impurity particles and enhancing the purity of the melt.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Fan C, Tang Q, Li F. Technologies for removing inclusions in molten aluminium. Light Metals, 2012, 12: 61–64.
Kolin A. An electromagnetokinetic phenomenon involving migration of neutral particles. Science, 1953, 117(3032): 134–137.
Leenov D, Kolin A. Theory of electromagnetophoresis. I. Magnetohydrodynamic forces experienced by spherical and symmetrically oriented cylindrical particles. Journal of Chemical Physics, 1954, 22(4): 683–688.
Zhong Y B, Qiang L I, Fang Y P, et al. Effect of transverse static magnetic field on microstructure and properties of GCr15 bearing steel in electroslag continuous casting process. Materials Science and Engineering: A, 2016, 660: 118–126.
Taniguchi S, Brimacombe J K. Numerical analysis on the separation of inclusion particles by pinch force from liquid steel flowing in a rectangular pipe. Tetsu to Hagane-Journal of the Iron and Steel Institute of Japan, 1994, 80(4): 312–317. (In Japanese)
Miki Y, Kitaoka H, Bessho N, et al. Inclusion separation from molten steel in tundish with rotating electromagnetic field. Tetsu to Hagane-Journal of the Iron and Steel Institute of Japan, 2009, 82(6): 498–503. (In Japanese)
Tanaka Y, Sassa K, Iwai K, et al. Separation of non-metallic inclusions from molten metal using traveling magnetic field. Magnetohydrodynamics, 2010, 81(12): 1120–1125.
Wang Y, Zhong Y, Wang B, et al. Numerical and experimental analysis of flow phenomenon in centrifugal flow tundish. ISIJ International, 2009, 49(10): 1542–1550.
Asai S. Recent development and prospect of electromagnetic processing of materials. Science and Technology of Advanced Materials, 2000, 1(4): 191–200.
Ren Z M, Lei Z S, Li C J, et al. New study and development on electromagnetic field technology in metallurgical processes. Acta Metallurgica Sinica, 2020, 56(4): 583–600. (In Chinese)
Gao G, Xu L. Spiral magnet–Revision on Maxwell equations. Frontier Science, 2014, 8(4): 41–44.
Huang J T, Wang E G, He J C. Numerical simulation of linear electromagnetic stirring in secondary cooling region of slab caster. Journal of Iron and Steel Research International, 2003, 10(3): 16–21.
Jie J C, Zou Q C, Sun J L, et al. Separation mechanism of the primary Si phase from the hypereutectic Al-Si alloy using a rotating magnetic field during solidification. Magnetohydrodynamics, 2014, 72: 57–66.
Noeppel A, Ciobanas A, Wang X D, et al. Influence of forced/natural convection on segregation during the directional solidification of Al-based binary alloys. Metallurgical and Materials Transactions B, 2010, 41(1): 193–208.
Grants I, Gerbeth G. Stability of axially symmetric flow driven by a rotating magnetic field in a cylindrical cavity. Journal of Fluid Mechanics, 2001, 431: 407–426.
Lee C Y, Lin C S, Jian R Q, et al. Simulation and experimentation on the contact width and pressure distribution of lip seals. Tribology International, 2006, 39(9): 915–920.
Raebiger D, Eckert S, Gerbeth G. Measurements of an unsteady liquid metal flow during spin-up driven by a rotating magnetic field. Experiments in Fluids, 2010, 48(2): 233–244.
Zou Q C, Jie J C, Sun J L, et al. Effect of Si content on separation and purification of the primary Si phase from hypereutectic Al-Si alloy using rotating magnetic field. Separation and Purification Technology, 2015, 142: 101–107.
Jebava M, Nemec L. Numerical study of glass fining in a pot melting space with different melt-flow patterns. Journal of Non-Crystalline Solids, 2013, 361: 47–56.
Klekovkin A Y, Basharimov N T. Melt circulation in a mold. Doklady Akademii Nauk Belarusi, 1991, 35(10): 907–910.
Park Y G, Yi K W, Ahn S B. The effect of operating parameters and dimensions of the RH system on melt circulation using numerical calculations. ISIJ International, 2001, 41(5): 403–409.
Acknowledgments
The authors gratefully acknowledge the support of the National Natural Science Foundation of China (Nos. 52171135 and 51971048).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Prof. Ting-ju Li is an EBM of CHINA FOUNDRY. He was not involved in the peer-review or handling of the manuscript. The authors have no other competing interests to disclose.
Additional information
Yu-bo Zhang Associate Professor, doctoral supervisor. His research interests mainly focus on the structural design and preparation technology of metal matrix composites. He has published more than 50 papers in journals, authorized 18 Chinese invention patents and 4 international patents.
Rights and permissions
About this article
Cite this article
Du, Sh., Shen, Yt., Zhang, Yb. et al. Movement behavior and separation of Al2O3 from Al melt under rotating magnetic field. China Foundry (2024). https://doi.org/10.1007/s41230-024-3140-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s41230-024-3140-8