Long-term properties and microstructural characterization of natural clinoptilolite zeolite-based cementitious materials

  • Technical Paper
  • Published:
Innovative Infrastructure Solutions Aims and scope Submit manuscript

Abstract

The pozzolanic reaction of clinoptilolite zeolite is often considered a slow chemical process at early ages, and the interaction with portland cement can alter the chemical and microstructural condition due to the cation exchange capability of zeolite particles beyond the early ages. Therefore, the present study investigates the long-term properties and microstructural characterization of clinoptilolite zeolite-blended cementitious materials, replacing the portland cement up to 20% by mass. For this, pozzolanic activity via thermal gravimetric analysis, degree of hydration by non-evaporable water, estimated gel/space ratio, compressive strength, and drying shrinkage of mortar bars were conducted to assess the influence of zeolite addition up to 360 days. The volume of hydration reaction products for the cementitious pastes was measured by the chemical shrinkage. The microstructure and pore size distribution were observed by scanning electron microscopy and small-angle X-ray scattering, respectively. The chloride ion penetrability of concrete was measured via surface resistivity. Results revealed that the use of clinoptilolite zeolite decreased the compressive strength in the early ages likely due to the slow pozzolanic activity (i.e., particles were not properly reactive until 28 days), but the zeolite samples obtained a relatively higher compressive strength at later ages due to the continued pozzolanic action, increasing degree of hydration, and the gel/space ratio. Results also suggested that the zeolite particles attributed to the internal curing capacity in the later ages. The lower chemical shrinkage of zeolite samples indicated the lower hydration reaction products in the early ages, but the higher pozzolanic consumption of CH in the early ages produced more gel/space ratio of microstructure leading to an apparently increased fibrous C–S–H network in the long term. The finer pore size distribution of zeolite-blended samples led to lower drying shrinkage by up to 25% compared to the control sample in 360 days. Overall, the use of to 20% clinoptilolite zeolite substantially increased the surface resistivity (by up to 230% higher compared to the control) in 90 days and subsequent resistance to chloride ion penetrability by reducing the permeability due to the refinement of pore microstructure.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15
Fig. 16
Fig. 17
Fig. 18
Fig. 19

Similar content being viewed by others

Data availability

Available upon request to mislam46@tntech.edu.

References

  1. Bilim C (2011) Properties of cement mortars containing clinoptilolite as a supplementary cementitious material. Constr Build Mater 25(8):3175–3180. https://doi.org/10.1016/j.conbuildmat.2011.02.006

    Article  Google Scholar 

  2. Mertens G, Snellings R, Van Balen K et al (2009) Pozzolanic reactions of common natural zeolites with lime and parameter affecting their reactivity. Cem Concr Res 39(3):233–240. https://doi.org/10.1016/j.cemconres.2008.11.008

    Article  Google Scholar 

  3. Poon CS, Lam L, Kou SC, Lin ZS (1999) A study on the hydration rate of natural zeolite blended cement pastes. Constr Build Mater 13(8):427–432. https://doi.org/10.1016/S0950-0618(99)00048-3

    Article  Google Scholar 

  4. Ahmadi B, Shekarchi M (2010) Use of natural zeolite as a supplementary cementitious material. Cem Concr Compos 32(2):134–141. https://doi.org/10.1016/j.cemconcomp.2009.10.006

    Article  Google Scholar 

  5. Najimi M, Sobhani J, Ahmadi B, Shekarchi M (2012) An experimental study on durability properties of concrete containing zeolite as a highly reactive natural pozzolan. Constr Build Mater 35(2012):1023–1033. https://doi.org/10.1016/j.conbuildmat.2012.04.038

    Article  Google Scholar 

  6. Burris LE (2014) Increasing the reactivity of natural zeolites used as supplementary cementitious materials. Dissertation, University of Texas at Austin, Austin, TX

  7. Snellings R, Mertens G, Cizer Ö, Elsen J (2010) Early age hydration and pozzolanic reaction in natural zeolite blended cements: reaction kinetics and products by in situ synchrotron X-ray powder diffraction. Cem Concr Res 40(12):1704–1713. https://doi.org/10.1016/j.cemconres.2010.08.012

    Article  Google Scholar 

  8. Islam MS, Mohr BJ (2022) Early age properties and microstructural characterization of zeolite based cementitious materials. Adv Civ Eng Mater 11(1):1–21. https://doi.org/10.1520/ACEM20210131

    Article  Google Scholar 

  9. Krolo P, Krstulovic R, Dabic P, Bubic A (2005) Hydration and leaching of cement-zeolite composite. Ceram-Silik 49(3):213–219

    Google Scholar 

  10. Kocak Y, Tasci E, Kaya U (2013) The effect of using natural zeolite on the properties and hydration characteristics of blended cements. Constr Build Mater 47(2013):720–727. https://doi.org/10.1016/j.conbuildmat.2013.05.033

    Article  Google Scholar 

  11. Uzal B, Turanl L, Yücel H, Göncüoğlu MC, Çulfaz A (2010) Pozzolanic activity of clinoptilolite: a comparative study with silica fume, fly ash and a non-zeolitic natural pozzolan. Cem Concr Res 40(3):398–404. https://doi.org/10.1016/j.cemconres.2009.10.016

    Article  Google Scholar 

  12. Pabalan RT, Bertetti FP (2001) Cation-exchange properties of natural zeolites. Rev Miner Geochem 45(1):453–518. https://doi.org/10.2138/rmg.2001.45.14

    Article  Google Scholar 

  13. Boháč M, Kubátová D, Nečas R et al (2016) Properties of cement pastes with zeolite during early stage of hydration. Proc Eng 151(2016):2–9. https://doi.org/10.1016/j.proeng.2016.07.349

    Article  Google Scholar 

  14. Liu C, Chen D, Cheng ZQ (2020) Effect of zeolite powder on the hydration and microstructure evolution of hardened cement paste at low water-binder ratio. Rev Roman Mater 50(3):331–336

    Google Scholar 

  15. Markiv T, Sobol K, Franus M, Franus W (2016) Mechanical and durability properties of concretes incorporating natural zeolite. Arc Civ Mech Eng 16(4):554–562. https://doi.org/10.1016/j.acme.2016.03.013

    Article  Google Scholar 

  16. Fagerlund G (2009) Chemically bound water as measure of degree of hydration: method and potential errors. (Report TVBM; Vol. 3150). Division of Building Materials, LTH, Lund University

  17. Lam L, Wong YL, Poon CS (2000) Degree of hydration and gel/space ratio of high-volume fly ash/cement system. Cem Concr Res 30(5):747–756. https://doi.org/10.1016/S0008-8846(00)00213-1

    Article  Google Scholar 

  18. Copeland LE, Hayes JC (1953) The determination of non-evaporable water in hardened portland cement pastes. Portland Cem Assoc Res Bull 47:1–9

    Google Scholar 

  19. Molina L (1992) On predicting the influence of curing conditions on the degree of hydration. (CBI Report 5). Swedish Cement and Concrete Research Institute, Stockholm, Sweden, pp 96

  20. Mohr BJ, Hood K (2018) Factors influencing mitigation strategies for autogenous shrinkage. Adv Civ Engg Mater 7(4):672–690. https://doi.org/10.1520/ACEM20170139

    Article  Google Scholar 

  21. Ghrici M, Kenai S, Meziane S (2006) Mechanical and durability properties of cement mortar with Algerian natural pozzolana. J Mater Sci 41:6965–6972. https://doi.org/10.1007/s10853-006-0227-0

    Article  Google Scholar 

  22. Islam MS, Mohr BJ, VandenBerge D (2022) Performance of natural clinoptilolite zeolite in the cementitious materials: a comparative study with metakaolin, fly ash, and blast furnace slag. J Build Eng 53(2022):104535. https://doi.org/10.1016/j.jobe.2022.104535

    Article  Google Scholar 

  23. Jana D (2007) A new look to an old pozzolan, clinoptilolite-a promising pozzolan in concrete. In: Proceedings of the 29th ICMA conference on cement microscopy. Curran Associates Inc., Quebec, 168–206

  24. Renhe Y, Baoyuan L, Zhongwei W (1990) Study on the pore structure of hardened cement paste by SAXS. Cem Concr Res 20(3):385–393. https://doi.org/10.1016/0008-8846(90)90028-V

    Article  Google Scholar 

  25. Keaton DG (2012) Nano-scale pore analysis of cementitious mortars subject to delayed ettringite formation. MS Thesis, Tennessee Technological University, TN

  26. ASTM C618-19, Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete, ASTM International, West Conshohocken, PA, 2019, https://doi.org/10.1520/C0618-19

  27. AASHTO T 353 (2014) Standard method of test for particle size analysis of hydraulic cement and related materials by light scattering. Washington, DC

  28. ASTM C150/C150M-07 (2019) Standard specification for portland cement. ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C0150-07

  29. ASTM C33/C33M-18 (2018) Standard specification for concrete aggregates. ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C0033_C0033M-18

  30. ASTM C109/C109M-20b (2020) Standard test method for compressive strength of hydraulic cement mortars (using 2-in. or [50 mm] cube specimens). ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C0109_C0109M-20

  31. ASTM C1260-14 (2014) Standard test method for potential alkali reactivity of aggregates (Mortar-Bar Method). ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C1260-21

  32. ASTM C305-20 (2020) Standard practice for mechanical mixing of hydraulic cement pastes and mortars of plastic consistency. ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C0305-14

  33. Borges PHR, Costa JO, Milestone NB et al (2020) Carbonation of CH and C–S–H in composite cement pastes containing high amounts of BFS. Cem Concr Res 40(2):284–292. https://doi.org/10.1016/j.cemconres.2009.10.020

    Article  Google Scholar 

  34. ASTM C1608-17 (2017) standard test method for chemical shrinkage of hydraulic cement paste. ASTM International. West Conshohocken, PA. https://doi.org/10.1520/C1608-07

  35. Neville AM (1981) Properties of concrete, 3rd edn. ELBS with Longman, London, pp 257–279

    Google Scholar 

  36. Zhang MH, Gjorv OE (2014) Effect of silica fume on cement hydration in low porosity cement pastes. Cem Concr Res 21(6):1006–1014. https://doi.org/10.1016/0008-8846(91)90060-U

    Article  Google Scholar 

  37. Taylor HFW (1990) Cement chemistry. Academic Press, London, pp 298–299

    Google Scholar 

  38. Wu ZQ, Young JF (1984) The hydration of tricalcium silicate in the presence of colloidal silica. J Mater Sci 19:3477–3486. https://doi.org/10.1007/BF02396922

    Article  Google Scholar 

  39. Bentz DP, Garboczi EJ (1991) Simulation studies of the effects of mineral admixtures on the cement paste-aggregate interfacial zone. ACI Mater J 88(5):518–529. https://doi.org/10.14359/2179

    Article  Google Scholar 

  40. ASTM C596-18 (2018) Standard test method for drying shrinkage of mortar containing hydraulic cement. ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C0596-18

  41. ASTM C192/C192M-19 (2019) Standard practice for making and curing concrete test specimens in the laboratory. ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C0192_C0192M-14

  42. ASTM C31/C31M-19a (2019) Standard practice for making and curing concrete test specimens in the field. ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C0031_C0031M-22

  43. Millard SG, Wenner (1991) Reinforced concrete resistivity measurement techniques. Proc Inst Civil Eng Part 2 91(1):71-88. https://doi.org/10.1680/iicep.1991.13583

  44. Federal Highway Administration (FHWA) (2012) Surface resistivity test evaluation as an indicator of the chloride permeability of concrete. HRDI-10/12-12(500)E. FHWA-HRT-13-024, Georgetown Pike, VA. https://highways.dot.gov/research/

  45. AASHTO T358 (2019) Standard method of test for surface resistivity of concrete’s ability to resist chloride ion penetration. Washington, DC

  46. Sičáková A, Špak M, Kozlovská M, Kováč M (2017) Long-term properties of cement-based composites incorporating natural zeolite as a feature of progressive building material. Adv Mater Sci 2017:7139481. https://doi.org/10.1155/2017/7139481

    Article  Google Scholar 

  47. Pane I, Hansen W (2005) Investigation of blended cement hydration by isothermal calorimetry and thermal analysis. Cem Concr Res 35(6):1155–1164. https://doi.org/10.1016/j.cemconres.2004.10.027

  48. Berry EE, Hemmings RT, Zhang MH et al (1994) Hydration in high-volume fly ash binders. ACI Mater J 91:382–389

    Google Scholar 

  49. Justnes H, Hammer T, Ardoullie B et al (1998) Chemical shrinkage of cement paste, Mortar and Concrete. In: Tazawa E (ed) Proceedings of international workshop on autogenous shrinkage of concrete. JCI, Hiroshima, Japan, pp 201–211

  50. Justnes H, Van Gemert A, Verboven F, Sellevold EJ (1996) Total and external chemical shrinkage of low W/C ratio cement pastes. Adv Cem Res 8(31):121–126. https://doi.org/10.1680/adcr.1996.8.31.121

    Article  Google Scholar 

  51. Taylor HFW (1997) Cement chemistry, 2nd edn. Thomas Telford, London. https://doi.org/10.1680/cc.25929

    Book  Google Scholar 

  52. Feldman RF, Carette GG, Malhotra VM (1990) Studies on of development of physical and mechanical properties of high-volume fly ash-cement pastes. Cem Concr Compos 12(4):245–251. https://doi.org/10.1016/0958-9465(90)90003-G

    Article  Google Scholar 

  53. Young JF, Hansen W (1987) Volume relationships for CSH formation based on hydration stoichiometry. MRS Online Proc Libr 85:313–332. https://doi.org/10.1557/PROC-85-313

    Article  Google Scholar 

  54. Mengxue W, Li C, Yao W (2017) Gel/space ratio evolution in ternary composite system consisting of portland cement, silica fume, and fly ash. Materials 10(1):59. https://doi.org/10.3390/ma10010059

    Article  Google Scholar 

  55. Yu Z, Yang W, Zhan P, Liu X, Chen D. Strengths, microstructures and nanomechanical properties of concrete containing high volume of zeolite powder. Materials 13(18):4191. https://doi.org/10.3390/ma13184191

  56. Ghourchian S, Wyrzykowski M, Lura P et al (2013) An investigation on the use of zeolite aggregates for internal curing of concrete. Constr Build Mater 40:135–144. https://doi.org/10.1016/j.conbuildmat.2012.10.009

    Article  Google Scholar 

  57. Snelson DG, Wild S, O’Farrell M (2008) Heat of hydration of portland cement-metakaolin-fly ash (PC-MK-PFA) blends. Cem Concr Res 38(6):832–840. https://doi.org/10.1016/j.cemconres.2008.01.004

    Article  Google Scholar 

  58. Naiqian F, Tingyu H (1998) Mechanism of natural zeolite powder in preventing alkali-silica reaction in concrete. Adv Cem Res 10(3):101–108. https://doi.org/10.1680/adcr.1998.10.3.101

    Article  Google Scholar 

  59. Islam MS, Mohr BJ (2023) Resistance to freeze-thaw of concrete made with natural clinoptilolite zeolite. J Cold Reg Eng 37(4):04023016. https://doi.org/10.1061/JCRGEI/CRENG-681

    Article  Google Scholar 

Download references

Acknowledgements

The authors express their gratitude to Mr. Wayne Hawkins and Mr. Brian Bates, Tennessee Tech Center for Manufacturing Research (CMR) for the technical assistance, and the alignment set up for small-angle X-ray scattering.

Funding

The authors did not receive any external funding for this study.

Author information

Authors and Affiliations

  1. Department of Civil and Environmental Engineering, Tennessee Tech University, 1020 Stadium Drive, Box 5015, Cookeville, TN, 38505-0001, USA

    M. Shariful Islam & Benjamin J. Mohr

Authors
  1. M. Shariful Islam
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Benjamin J. Mohr
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

M. Shariful Islam contributed to conceptualization, methodology, data curation, formal analysis, investigation, writing—original draft. Benjamin J. Mohr contributed to supervision, visualization, funding acquisition, project administration, writing—review & editing.

Corresponding author

Correspondence to M. Shariful Islam.

Ethics declarations

Competing interests

The authors have no relevant financial or non-financial interests to disclose.

Ethical approval

This research does not contain any experiments with human participants or animals performed by the authors.

Informed consent

For this study, formal consent is not required.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Islam, M.S., Mohr, B.J. Long-term properties and microstructural characterization of natural clinoptilolite zeolite-based cementitious materials. Innov. Infrastruct. Solut. 8, 325 (2023). https://doi.org/10.1007/s41062-023-01278-4

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s41062-023-01278-4

Keywords

Search

Navigation