Factors Affecting Kinetics and Gel Composition of Alkali–Silica Reaction in Alkali-Activated Slag Mortars

  • Research paper
  • Published:
International Journal of Civil Engineering Aims and scope Submit manuscript

Abstract

Alkali activation of metallurgical slags produces low-carbon cementitious binders for sustainable concrete production. However, the potential deleterious reaction of internal alkalis in alkali-activated slag (AAS) with siliceous aggregates is a serious durability concern. In this work, the alkali–silica reaction (ASR) in alkali-activated ground granulated blast furnace slag mortars with various activator dosages and types, aggregate reactivity, as well as incorporation of pulverized fly ash or silica fume is studied. The ASR-induced length expansion and microstructural damage in AAS mortars are studied by a modified accelerated mortar bar test and scanning electron microscopy with X-ray energy-dispersive spectroscopy. The results show that the kinetics of ASR-induced damage, as well as the gel composition and spatial distribution, in AAS mortars is highly dependent on the alkali dosage, activator type, and aggregate reactivity. The ASR-induced length expansion is approximately proportional to the volumetric fraction of dissolved glassy aggregates. However, AAS mortars show noticeable autogenous shrinkage at the initial stage of immersion, making the conventional judgment of ASR risks using length expansion as the sole indicator invalid. The dissolution kinetics of aggregate, which is influenced by the level of alkalinity and availability of reactive silica, seems to be the rate-limiting reaction of ASR-induced damage in AAS mortars under accelerated testing conditions.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9

Similar content being viewed by others

References

  1. Thomas RJ, Ye H, Radlinska A, Peethamparan S (2016) Alkali-activated slag cement concrete. Concr Int 38:33–38

    Google Scholar 

  2. Juenger MCG, Winnefeld F, Provis JL, Ideker JH (2011) Advances in alternative cementitious binders. Cem Concr Res 41:1232–1243

    Article  Google Scholar 

  3. Provis JL, Palomo A, Shi C (2015) Advances in understanding alkali-activated materials. Cem Concr Res 78:110–125

    Article  Google Scholar 

  4. Wang S-D, Pu X-C, Scrivener KL, Pratt PL (1995) Alkali-activated slag cement and concrete: a review of properties and problems. Adv Cem Res 7:93–102

    Article  Google Scholar 

  5. Aiken TA, Kwasny J, Sha W, Soutsos MN (2018) Effect of slag content and activator dosage on the resistance of fly ash geopolymer binders to sulfuric acid attack. Cem Concr Res 111:23–40

    Article  Google Scholar 

  6. Behfarnia K, Rostami M (2018) The effect of alkaline solution-to-slag ratio on permeability of alkali activated slag concrete. Int J Civ Eng 16:897–904

    Article  Google Scholar 

  7. Bernal SA, San Nicolas R, Myers RJ, de Gutiérrez RM, Puertas F, van Deventer JSJ, Provis JL (2014) MgO content of slag controls phase evolution and structural changes induced by accelerated carbonation in alkali-activated binders. Cem Concr Res 57:33–43

    Article  Google Scholar 

  8. Ye H, Cai R, Tian Z (2020) Natural carbonation-induced phase and molecular evolution of alkali-activated slag: effect of activator composition and curing temperature. Constr Build Mater 248:118726

    Article  Google Scholar 

  9. Palacios M, Puertas F (2006) Effect of carbonation on alkali-activated slag paste. J Am Ceram Soc 89:3211–3221

    Article  Google Scholar 

  10. Nedeljković M, Zuo Y, Arbi K, Ye G (2018) Carbonation resistance of alkali-activated slag under natural and accelerated conditions. J Sustain Metall 4:33–49

    Article  Google Scholar 

  11. Ye H, Radlińska A (2017) Shrinkage mitigation strategies in alkali-activated slag. Cem Concr Res 101:131–143

    Article  Google Scholar 

  12. Ye H, Radlinska A (2016) Shrinkage mechanisms of alkali-activated slag. Cem Concr Res 88:126–135

    Article  Google Scholar 

  13. Melo Neto AA, Cincotto MA, Repette W (2008) Drying and autogenous shrinkage of pastes and mortars with activated slag cement. Cem Concr Res 38:565–574

    Article  Google Scholar 

  14. Cartwright C, Rajabipour F, Radlińska A (2014) Shrinkage characteristics of alkali-activated slag cements. J Mater Civ Eng 27:B4014007

    Google Scholar 

  15. Sakulich AR, Bentz DP (2013) Mitigation of autogenous shrinkage in alkali activated slag mortars by internal curing. Mater Struct 46:1355–1367

    Article  Google Scholar 

  16. Fernández-Jiménez A, Puertas F (2001) Setting of alkali-activated slag cement. Influence of activator nature. Adv Cem Res 13:115–121

    Article  Google Scholar 

  17. Fernández-Jiménez A, Puertas F (2002) The alkali–silica reaction in alkali-activated granulated slag mortars with reactive aggregate. Cem Concr Res 32:1019–1024

    Article  Google Scholar 

  18. Bakharev T, Sanjayan JG, Cheng Y-B (2001) Resistance of alkali-activated slag concrete to alkali–aggregate reaction. Cem Concr Res 31:331–334

    Article  Google Scholar 

  19. Rajabipour F, Giannini E, Dunant C, Ideker JH, Thomas MDA (2015) Alkali–silica reaction: current understanding of the reaction mechanisms and the knowledge gaps. Cem Concr Res 76:130–146

    Article  Google Scholar 

  20. Saha AK, Khan MNN, Sarker PK, Shaikh FA, Pramanik A (2018) The ASR mechanism of reactive aggregates in concrete and its mitigation by fly ash: a critical review. Constr Build Mater 171:743–758

    Article  Google Scholar 

  21. Vayghan AG, Rajabipour F, Rosenberger JL (2016) Composition–rheology relationships in alkali–silica reaction gels and the impact on the gel’s deleterious behavior. Cem Concr Res 83:45–56

    Article  Google Scholar 

  22. Shafaatian SMH, Akhavan A, Maraghechi H, Rajabipour F (2013) How does fly ash mitigate alkali–silica reaction (ASR) in accelerated mortar bar test (ASTM C1567)? Cem Concr Compos 37:143–153

    Article  Google Scholar 

  23. Shi C, Shi Z, Hu X, Zhao R, Chong L (2015) A review on alkali-aggregate reactions in alkali-activated mortars/concretes made with alkali-reactive aggregates. Mater Struct 48:621–628

    Article  Google Scholar 

  24. Wang W, Noguchi T (2020) Alkali-–silica reaction (ASR) in the alkali-activated cement (AAC) system: A state-of-the-art review. Constr Build Mater 252:119105

    Article  Google Scholar 

  25. Maraghechi H, Rajabipour F, Pantano CG, Burgos WD (2016) Effect of calcium on dissolution and precipitation reactions of amorphous silica at high alkalinity. Cem Concr Res 87:1–13

    Article  Google Scholar 

  26. Chen Y, Pu X, Yang C, Ding Q (2002) Alkali aggregate reaction in alkali slag cement mortars. J Wuhan Univ Technol Sci Ed 17:60–62

    Article  Google Scholar 

  27. Shi Z, Shi C, Wan S, Li N, Zhang Z (2018) Effect of alkali dosage and silicate modulus on carbonation of alkali-activated slag mortars. Cem Concr Res 113:55–64

    Article  Google Scholar 

  28. Gifford PM, Gillott JE (1996) Alkali–silica reaction (ASR) and alkali-carbonate reaction (ACR) in activated blast furnace slag cement (ABFSC) concrete. Cem Concr Res 26:21–26

    Article  Google Scholar 

  29. Al-Otaibi S (2008) Durability of concrete incorporating GGBS activated by water-glass. Constr Build Mater 22:2059–2067

    Article  Google Scholar 

  30. Puertas F, Palacios M, Gil-Maroto A, Vázquez T (2009) Alkali-aggregate behaviour of alkali-activated slag mortars: effect of aggregate type. Cem Concr Compos 31:277–284

    Article  Google Scholar 

  31. ASTM Standard C1567 (2011) Standard test method for determining the potential alkali–silica reactivity of combinations of cementitious materials and aggregate (accelerated mortar-bar method). ASTM International, USA

  32. Tarnopol MS, Junge AE (1946) Resistance of plate glass to alkaline solutions. J Am Ceram Soc 29:36–39

    Article  Google Scholar 

  33. Li Z (2017) Acid leaching resistance and alkali silica reaction (ASR) of alkali-activated cement free binders. Ph.D. Dissertation, Clarkson University, Potsdam, USA

  34. Ben Haha M, Gallucci E, Guidoum A, Scrivener KL (2007) Relation of expansion due to alkali silica reaction to the degree of reaction measured by SEM image analysis. Cem Concr Res 37:1206–1214

    Article  Google Scholar 

  35. Kim T, Olek J (2014) Chemical sequence and kinetics of alkali-silica reaction part I e222xperiments. J Am Ceram Soc 97:2195–2203

    Article  Google Scholar 

  36. Maraghechi H, Maraghechi M, Rajabipour F, Pantano CG (2014) Pozzolanic reactivity of recycled glass powder at elevated temperatures: reaction stoichiometry, reaction products and effect of alkali activation. Cem Concr Compos 53:105–114

    Article  Google Scholar 

  37. Ye H, Chen Z, Huang L (2019) Mechanism of sulfate attack on alkali-activated slag: the role of activator composition. Cem Concr Res 125:105868

    Article  Google Scholar 

  38. Sanchez LFM, Fournier B, Jolin M, Mitchell D, Bastien J (2017) Overall assessment of alkali-aggregate reaction (AAR) in concretes presenting different strengths and incorporating a wide range of reactive aggregate types and natures. Cem Concr Res 93:17–31

    Article  Google Scholar 

  39. Ponce JM, Batic OR (2006) Different manifestations of the alkali–silica reaction in concrete according to the reaction kinetics of the reactive aggregate. Cem Concr Res 36:1148–1156

    Article  Google Scholar 

  40. Tänzer R, Jin Y, Stephan D (2017) Effect of the inherent alkalis of alkali activated slag on the risk of alkali silica reaction. Cem Concr Res 98:82–90

    Article  Google Scholar 

  41. Maas AJ, Ideker JH, Juenger MCG (2007) Alkali silica reactivity of agglomerated silica fume. Cem Concr Res 37:166–174

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Hailong Ye.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Huang, L., Ye, H. Factors Affecting Kinetics and Gel Composition of Alkali–Silica Reaction in Alkali-Activated Slag Mortars. Int J Civ Eng 19, 453–462 (2021). https://doi.org/10.1007/s40999-020-00589-2

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s40999-020-00589-2

Keywords

Navigation