Simulation and Experimental Investigation of a Combined Control Method for Stray Grain During Single Crystal Blade Solidification

  • Technical Paper
  • Published:
International Journal of Metalcasting Aims and scope Submit manuscript

Abstract

It is of great significance to effectively prevent the stray grain defect at the edge plate of nickel-based superalloy single crystal blades. In this study, the evolution of the mushy zone and the growth of grain adjacent to the edge plate was first simulated by the temperature field and cellular automaton-finite element (CAFÉ) model, combined with a single crystal blade solidification experiment; it was proved that modifying the withdrawal rate alone was insufficient to prevent the stray grain formation. Then, the formation reason of the heat barrier zone and the irregular distribution pattern of the mold shell thickness were revealed by quantifying the present mold shell thickness near the edge plate through an industrial conical beam computed tomography. Based on these results, a combined control method for stray grain was proposed, which involves the use of precise measures such as non-uniform mold design, exact addition of process bars, and variable withdrawal rate. Simulation analysis demonstrated that this method can substantially reduce the undercooling range and average undercooling at the edge plate by 45.5% and 31.6%, respectively, and then eliminate the isolated undercooling zone. The macrostructure and microstructure of the blade cast by this method verified the effectiveness in inhibiting stray grain, and it will be a promising approach to manufacturing single crystal blades.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Figure 1
Figure 2
Figure 3
Figure 4
Figure 5
Figure 6
Figure 7
Figure 8
Figure 9
Figure 10
Figure 11
Figure 12
Figure 13
Figure 14
Figure 15

Similar content being viewed by others

References

  1. G. Gudivada, A.K. Pandey, Recent developments in nickel-based superalloys for gas turbine applications: Review. J. Alloys Compd. 963, 14 (2023)

    Article  Google Scholar 

  2. Y.F. He, S.G. Wang, J. Shen, D. Wang, Y.Z. Lu, L.H. Lou, J. Zhang, Evolution of micro-pores in a single crystal nickel-based superalloy during 980 °C creep. Acta Metall. Sin.-Engl. Lett. 35(8), 1397–1406 (2022)

  3. B.Q. Wang, L. Zeng, M.X. Xia, N. Ren, J.G. Li, Substrate stimulating technique for ni-based single crystal superalloy preparation during direction solidification. Mater. Des. 224, 9 (2022)

    Article  Google Scholar 

  4. M. Huo, C.Y. Chen, H.Y. Jian, W.C. Yang, L. Liu, M. Motyka, C.Y. Jo, The stray grains from fragments in the rejoined platforms of ni-based single-crystal superalloy. Metals. 13(8), 10 (2023)

    Article  Google Scholar 

  5. D. Szeliga, Eliminating equiaxed grain defects in a ni-based single-crystal blade platform by flattening the liquidus isotherm. Adv. Eng. Mater. 13 (2023)

  6. W. Tan, X. Xue, T. Yu, W. Li, P. Yan, Q. Zeng, Formation mechanism of stray grain in the transition zone between airfoil and platform of nickel-based single crystal blade. Rare Met. Mater. Eng. 51(4), 1348–1355 (2022)

    CAS  Google Scholar 

  7. Z. Shang, H.J. Niu, X.P. Wei, D.Z. Song, J.T. Zou, G. Liu, S.H. Liang, L.P. Nie, X.F. Gong, Microstructure and tensile behavior of nickel-based single crystal superalloys with different Re contents. J. Mater. Res. Technol. JMRT 18, 2458–2469 (2022)

    Article  CAS  Google Scholar 

  8. N. Ren, J. Li, B.Q. Wang, L. Zeng, M.X. Xia, J.G. Li, Design of variable withdrawal rate for superalloy single-crystal blade fabrication. Mater. Des. 198, (2021)

  9. L. Qin, J. Shen, G.X. Yang, Q.D. Li, Z. Shang, A design of non-uniform thickness mould for controlling temperature gradient and S/L interface shape in directionally solidified superalloy blade. Mater. Des. 116, 565–576 (2017)

    Article  CAS  Google Scholar 

  10. D. Szeliga, K. Kubiak, J. Sieniawski, Control of liquidus isotherm shape during solidification of Ni-based superalloy of single crystal platforms. J. Mater. Process. Tech. 234, 18–26 (2016)

    Article  CAS  Google Scholar 

  11. D.X. Ma, Development of single crystal solidification technology for production of superalloy turbine blades. Acta Metall. Sin. 51(10), 1179–1190 (2015)

    CAS  Google Scholar 

  12. M. Meyer, D. Dedecke, U. Paul, S. Kwu, Undercooling related casting defects in single crystal turbine blades. Superalloys 471–479 (1996)

  13. F. Qiu, K. Bu, B.J. Zheng, G.L. Tian, Control of edge plate stray grain of single-crystal turbine blade by using process bar method. Int. J. Metalcast. 14(1), 144–154 (2020). https://doi.org/10.1007/s40962-019-00338-9

    Article  Google Scholar 

  14. S.J. Ren, K. Bu, S. Mou, R.Y. Zhang, B.X. Bai, Control of dimensional accuracy of hollow turbine blades during investment casting. J. Manuf. Process. 99, 548 (2023)

    Article  Google Scholar 

  15. M.Z. Xu, S.N. Lekakh, V.L. Richards, Thermal property database for investment casting shells. Int. J. Metalcast. 10(3), 329–337 (2016). https://doi.org/10.1007/s40962-016-0052-4

    Article  Google Scholar 

  16. X. Liu, Y. Wang, H. Zheng, Z. Guo, G.H. Liu, Z.D. Wang, Investigation and application of inverse determination of interfacial heat transfer coefficient in vacuum investment casting. Int. J. Metalcast. (2024). https://doi.org/10.1007/s40962-023-01240-1

    Article  Google Scholar 

  17. S. Mou, K. Bu, S.J. Ren, J. Liu, H.Y. Zhao, Z.X. Li, Digital twin modeling for stress prediction of single-crystal turbine blades based on graph convolutional network. J. Manuf. Process. 116, 210–223 (2024)

    Article  Google Scholar 

  18. M.S. Varfolomeev, G.I. Shcherbakova, Interaction of a ceramic casting mold material of the Al2O3–Al2O3 composition with a nickel-based superalloy. Int. J. Metalcast. 15(4), 1309–1316 (2021)

    Article  CAS  Google Scholar 

  19. F. Qiu, K. Bu, J.H. Song, G.L. Tian, X.D. Zhang, Dimensional control of nickel-based single crystal turbine blade investment casting by process control optimization. Int. J. Metalcast. 12(3), 469–479 (2018)

    Article  CAS  Google Scholar 

  20. X. Guo, A.T. Yang, D.Y. Zhao, J. He, F. Tao, Q.Y. Zhang, Z.H. Yang, Research on displacement and wall thickness evolution of gas turbine blade during casting process based on cantilever structure core. J. Chin. Soc. Power Eng. 41(6), 452–459 (2021)

    Google Scholar 

  21. J.X. Wu, Y.Y. Chen, Z.M. Du, H.Y. Jiang, Modeling of investment casting of Ti48Al48Cr2Nb2 (at%) alloy air rudder skeleton. Int. J. Metalcast. 17(3), 2002–2016 (2023). https://doi.org/10.1007/s40962-022-00907-5

    Article  CAS  Google Scholar 

  22. C.A. Gandin, M. Rappaz, D. West, B.L. Adams, Grain texture evolution during the columnar growth of dendritic alloys. Metall. Mater. Trans. A 26(6), 1543–1551 (1995)

    Article  Google Scholar 

  23. C.A. Gandin, J.L. Desbiolles, M. Rappaz, P. Thevoz, A three-dimensional cellular automation-finite element model for the prediction of solidification grain structures. Metall. Mater. Trans. A 30(12), 3153–3165 (1999)

    Article  Google Scholar 

  24. A. Kermanpur, N. Varahram, P. Davami, M. Rappaz, Thermal and grain-structure simulation in a land-based turbine blade directionally solidified with the liquid metal cooling process. Metall. Mater. Trans. B 31(6), 1293–1304 (2000)

    Article  Google Scholar 

  25. H.X. Xia, Y.H. Yang, Q.S. Feng, Q.Y. Xu, H.B. Dong, B.C. Liu, Generation mechanism and motion behavior of sliver defect in single crystal ni-based superalloy. J. Mater. Sci. Technol. 137, 232–246 (2023)

    Article  Google Scholar 

  26. W. Kurz, B. Giovanola, R. Trivedi, Theory of microstructural development during rapid solidification. Acta Metall. 34(5), 823–830 (1986)

    Article  CAS  Google Scholar 

  27. B.Q. Wang, L. Zeng, N. Ren, M.X. Xia, J.G. Li, A comprehensive understanding of grain selection in spiral grain selector during directional solidification. J. Mater. Sci. Technol. 102, 204–212 (2022)

    Article  CAS  Google Scholar 

  28. Z.F. Liu, K. Miao, W.B. Lian, Z.L. Lu, D.C. Li, Elimination of the stray grain defects of single crystal blade by variable wall thickness based on integral ceramic mold. Metals 12(11), 11 (2022)

    Article  CAS  Google Scholar 

  29. K. Cui, W.H. Wang, R.S. Jiang, D.Z. Zhao, A wall-thickness compensation strategy for wax pattern of hollow turbine blade. Chinese. J. Aeronaut. 32(8), 1982–1993 (2019)

    Article  Google Scholar 

  30. F.Q. Yang, D.H. Zhang, K.D. Huang, Y. Yang, Iterative excitation with noise rejection techniques for x-ray computed tomography of hollow turbine blades. Nondestruct. Test. Eva. 38(1), 172–188 (2023)

    Article  CAS  Google Scholar 

  31. D.X. Ma, Y.X. Zhao, W.T. Xu, F.Z. Xu, J.H. Wei, H.J. Zhang, Comparative investigation of the undercooling capacity and single-crystal castability of some ni-based superalloys. Crystals 13(1), 11 (2023)

    Google Scholar 

  32. X.W. Yan, Q.Y. Xu, G.Q. Tian, Q.W. Liu, J.X. Hou, B.C. Liu, Multi-scale modeling of liquid-metal cooling directional solidification and solidification behavior of nickel-based superalloy casting. J. Mater. Sci. Technol. 67, 36–49 (2021)

    Article  Google Scholar 

  33. M.M. Franke, R.M. Hilbinger, A. Lohmuller, R.F. Singer, The effect of liquid metal cooling on thermal gradients in directional solidification of superalloys: Thermal analysis. J. Mater. Process. Tech. 213(12), 2081–2088 (2013)

    Article  CAS  Google Scholar 

  34. Y.L. Jia, L.L. He, Y.S. Zhao, H.M. Guo, X. Fang, J. Zhang, Determination of undercooling time for stray grain formation of dd11 single crystal superalloy. J. Aeronaut. Mater. 35(4), 8–15 (2015)

    CAS  Google Scholar 

  35. H. Jafari, M.H. Idris, A. Ourdjini, Effect of thickness and permeability of ceramic shell mould on in-situ melted AZ91D investment casting. Appl. Mech. Mater. 465, 1087 (2013)

    Article  Google Scholar 

  36. A. Wall, M.J. Benoit, A review of existing solidification crack tests and analysis of their transferability to additive manufacturing. J. Mater. Process. Tech. 320, 118090 (2023)

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This work was sponsored by National Science and Technology Major Project (J2019-VII-0013-0153) and Postdoctoral Fellowship Program of CPSF (GZC20233515).

Author information

Authors and Affiliations

  1. Key Laboratory of High Performance Manufacturing for Aero Engine, Ministry of Industry and Information Technology, School of Mechanical Engineering, Northwestern Polytechnical University, Xi’an, 710072, Shannxi, People’s Republic of China

    Haoyu Zhao, Kun Bu, Binqiang Wang & Sheng Mou

  2. Avic Xi’an Aero-Engine (Group) Ltd., Xi’an, 710100, People’s Republic of China

    Pengguo Duan

Authors
  1. Haoyu Zhao
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Kun Bu
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Binqiang Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Sheng Mou
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Pengguo Duan
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding authors

Correspondence to Kun Bu or Binqiang Wang.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Zhao, H., Bu, K., Wang, B. et al. Simulation and Experimental Investigation of a Combined Control Method for Stray Grain During Single Crystal Blade Solidification. Inter Metalcast (2024). https://doi.org/10.1007/s40962-024-01357-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s40962-024-01357-x

Keywords

Search

Navigation