Abstract
Investment Casting (IC), using the wax pattern, produces metal parts with a high surface finish and complex geometries within acceptable tolerances. However, removing the wax patterns can have processing challenges, such as thermal expansion during wax melting for pattern removal leading to shell cracking defects, the release of hydrocarbons from melting wax, and the burnt residue from this process. To overcome these challenges, it has been proposed to replace wax with ice as a pattern material. Ice has an inherent benefit of reduction of volume during its phase change from solid to liquid. It helps to reduce cracking due to expansion. Rapid Freeze Prototyping (RFP) and Freeze Cast Process (FCP) can produce the ice pattern. In the process of Rapid Ice Investment Casting (RIIC), the ice pattern is invested with a low-temperature ceramic slurry to make ceramic shells for metal casting. Sublimation is used for ice pattern evacuation at sub-zero conditions using a vacuum. Estimating various properties like time for total sublimation, concentration gradient, and energy usage are vital for process characterization and optimization. A diffusion-based mathematical model has been proposed and experimentally verified to sublimate the ice patterns in this research. Experimental results show a close correlation (96.74%) with the theoretical model. The demonstration of ice investment casting has been carried out, and it reported close dimensional accuracy.
Similar content being viewed by others
Availability of data and material
Not applicable.
Code availability
Not applicable.
References
S. Kumar, D.B. Karunakar, Int. J. Met. 15, 98–107 (2021). https://doi.org/10.1007/s40962-020-00421-6
M.P. Groover, Fundamentals of Modern Manufacturing, 4th edn. (Wiley, Hoboken, 2010), pp. 225–253
D. Almonti, N. Ucciardello, Materials 12, 2261–2274 (2019). https://doi.org/10.3390/ma12142261
D. Almonti, G. Baiocco, V. Tagliaferri, N. Ucciardello, Materials 13, 1085–1096 (2020). https://doi.org/10.3390/ma13051085
D. Almonti, G. Baiocco, E. Mingione, N. Ucciardello, Int. J. Adv. Manuf. Technol. 111, 1157–1172 (2020). https://doi.org/10.1007/s00170-020-06092-1
C. Liu, F. Wang, S. Jin, F. Li, X. Lai, Int. J. Met. 13, 953–968 (2019). https://doi.org/10.1007/s40962-019-00317-0
Druschitz EA. Investment shell cracking. Missouri University of Science and Technology; 2009. https://scholarsmine.mst.edu/masters_theses/5003. Accessed 20 June 2020
H. Zhao, P.K. Nam, V.L. Richards, S.N. Lekakh, Int. J. Met. 13, 18–25 (2019). https://doi.org/10.1007/s40962-018-0240-5
W. Everhart, S. Lekakh, V. Richards, J. Chen, H. Li, K. Chandrashekhara, Int. J. Met. 7, 21–27 (2013). https://doi.org/10.1007/BF03355541
Yodice DB. U. S. Patent 5,072,770, 17 Dec 1991
Q. Liu, M.C. Leu, Int. J. Adv. Manuf. Technol. 29, 317–335 (2006). https://doi.org/10.1007/s00170-005-2523-2
Liu Q, Leu MC. In: International solid freeform fabrication symposium, 2004. https://doi.org/10.26153/tsw/7025
Q.B. Liu, M.C. Leu, V.L. Richards, Int. J. Cast Met. Res. 20, 14–24 (2007). https://doi.org/10.1179/136404607X202708
M.C. Leu, Q. Liu, F.D. Bryant, CIRP Ann. 12, 185–188 (2003). https://doi.org/10.1016/S0007-8506(07)60561-7
L. Qingbin, G. Sui, M.C. Leu, Comput. Ind. 48, 181–197 (2002). https://doi.org/10.1016/S0166-3615(02)00042-8
P. Kamble, S. Chavan, K.P. Karunakaran, J. Emerg. Technol. 5, 119–131 (2018)
J.C. Kasper, G. Winter, W. Friess, Eur. J. Pharm. Biopharm. 85, 162–169 (2013). https://doi.org/10.1016/j.ejpb.2013.05.019
M. Xu, S.N. Lekakh, V.L. Richards, Int. J. Met. 10, 329–337 (2016). https://doi.org/10.1007/s40962-016-0052-4
K.J. Kossacki, K. Misiura, L. Czechowski, Icarus 329, 72–78 (2019). https://doi.org/10.1016/j.icarus.2019.03.019
V. Chevrier, D.R. Ostrowski, D.W.G. Sears, Icarus 196, 459–476 (2008). https://doi.org/10.1016/j.icarus.2008.03.009
V. Chevrier, D.W.G. Sears, J.D. Chittenden, L.A. Roe, R. Ulrich, K. Bryson, L. Billingsley, J. Hanley, Geophys. Res. Lett. 34, 3–7 (2007). https://doi.org/10.1029/2006GL028401
S. Kumar, D.B. Karunakar, Int. J. Met. 13, 588–596 (2019). https://doi.org/10.1007/s40962-018-00297-7
S. Kumar, D.B. Karunakar, Int. J. Met. 15, 98–107 (2020). https://doi.org/10.1007/s40962-020-00421-6
Z.H. Wang, J. Wang, B. Yu, J. Wu, M. Wang, B. Su, Int. J. Met. 13, 74–81 (2019). https://doi.org/10.1007/s40962-018-0228-1
G. Dietler, C. Aubert, D.S. Cannell, P. Wiltzius, Phys. Rev. Lett. 57, 3117–3121 (1986)
Q. Liu, M.C. Leu, V.L. Richards, S.M. Schmitt, Int. J. Adv. Manuf. Technol. 24, 485–495 (2004). https://doi.org/10.1007/s00170-003-1635-9
Y. Jing, L. Dehong, W. Zhao, J. Yehua, Int. J. Met. 9, 4 (2015). https://doi.org/10.1007/BF03356038
T. Watts, C. Derksen, C.C. Canada, M. Sandells, Cryosphere 9, 5979–6002 (2015). https://doi.org/10.5194/tcd-9-5979-2015
K. Goto, T. Hondoh, A. Higashi, Jpn. J. Appl. Phys. 25, 351–357 (1986). https://doi.org/10.1143/JJAP.25.351
S. Pattnaik, D.B. Karunakar, P.K. Jha, J. Mater. Process. Technol. 212, 2332–2348 (2012). https://doi.org/10.1016/j.jmatprotec.2012.06.003
Acknowledgements
The authors wish to acknowledge the help extended by the Department of Chemical Engineering, IIT Bombay, regarding experimental work.
Funding
There are no financial conflicts of interest to disclose.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflicts of interest
Not applicable.
Ethics approval
Not applicable.
Consent to participate
Not applicable.
Consent for publication
Not applicable.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Hodgir, R., Mittal, Y.G., Kamble, P. et al. Mathematical Modelling of Pattern Sublimation in Rapid Ice Investment Casting. Inter Metalcast 16, 1002–1009 (2022). https://doi.org/10.1007/s40962-021-00665-w
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40962-021-00665-w