Experimental investigation into the fragment size of tempered glass

  • N. Pourmoghaddam
  • J. Schneider
SI: Challenging Glass paper

Abstract

This work presents the relation between the fragment density and the permanent residual stress in fragmented tempered glasses of various thicknesses. Therefore, fracture tests were carried out on tempered glass plates and the fragments in observation fields of 50 mm \(\times \) 50 mm were counted. The average fragment density in the observation fields was set in correlation with the average measured residual stress of each specimen. Furthermore, the average particle weight of 130 particles per specimen chosen by random was determined. The relation between the average particle weight and the measured residual stress is given. The volume and the base surface as well as the radius of the particles are calculated assuming cylindrical fragments with approximately unchanged thicknesses. The relation between the residual stress and the particle base surface of regular polygonal shapes \(n=3\)–8 edges in addition to the cylindrical fragment \((n\rightarrow \infty )\) is also determined. The glass used for the fracture tests was commercial soda-lime-silica glass with three different thicknesses 4, 8 and 12 mm. The results in this work are a basis for the establishment of a theoretical model to predict macro-scale fracture patterns from elastic strain energy in tempered glass.

Keywords

Fragmentation Particle count Particle weight Residual stress Tempered glass Elastic strain energy Heat transfer coefficient 

Notes

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

References

  1. Acloque, P.: Deferred processes in the fragmentation of tempered glass. In: Proceedings of the 4th International Glass Congress, vol. 6, pp. 79–291 (1956)Google Scholar
  2. Akeyoshi, K., Kanai, E.: Mechanical properties of tempered glass. In: Proceedings of the 7th International Glass Congress, vol. 14, pp. 80–85 (1965)Google Scholar
  3. Aronen, A.: Modelling of deformations and stresses in glass tempering. Ph.D. thesis, Julkaisu-Tampere University of Technology, Publication 1036 (2012)Google Scholar
  4. Aronen, A., Karvinen, R.: Effect of glass temperature before cooling and cooling rate on residual stresses in tempering. Glass Struct. Eng. (2017).  https://doi.org/10.1007/s40940-017-0053-6
  5. Barsom, J.M.: Fracture of tempered glass. J. Am. Ceram. Soc. 51(2), 75–78 (1968).  https://doi.org/10.1111/j.1151-2916.1968.tb11840.x CrossRefGoogle Scholar
  6. CulletScanner: Version 17.4 (r40671) SoftSolution GmbH (2017)Google Scholar
  7. EN 12150-1: Glass in building – Thermally toughened soda lime silicate safety glass – Part 1: definition and description; German version EN 12150-1 (2015)Google Scholar
  8. Fineberg, J.: The dynamics of rapidly moving tensile cracks in brittle amorphous material. In: Shukla, A. (ed.) Dynamic Fracture Mechanics. World Scientific, Singapore, pp. 104–146 (2006)Google Scholar
  9. Gulati, S.T.: Frangibility of tempered soda-lime glass sheet. Glass Performance Days, pp. 13–15 (1997)Google Scholar
  10. Lee, H., Cho, S., Yoon, K., Lee, J.: Glass thickness and fragmentation behavior in stressed glasses. New J. Glass Ceram. 2, 138–143 (2012)CrossRefGoogle Scholar
  11. Martin, H.: Heat and mass transfer between impinging gas jets and solid surfaces. Adv. Heat Transf. 13, 1–60 (1977).  https://doi.org/10.1016/S0065-2717(08)70221-1 CrossRefGoogle Scholar
  12. Mognato, E., Brocca, S., Barbieri, A.: Thermally processed glass: correlation between surface compression, mechanical and fragmentation test. Glass Performance Days, pp. 8–11 (2017)Google Scholar
  13. Narayanaswamy, O.S.: A model of structural relaxation in glass. J. Am. Ceram. Soc. 54(10), 491–498 (1971).  https://doi.org/10.1111/j.1151-2916.1971.tb12186.x CrossRefGoogle Scholar
  14. Nielsen, J.H., Olesen, J.F., Stang, H.: The fracture process of tempered soda-lime-silica glass. Exp. Mech. 49(6), 855–870 (2009a).  https://doi.org/10.1007/s11340-008-9200-y CrossRefGoogle Scholar
  15. Nielsen, J.H.: Tempered glass: bolted connections and related problems. Ph.D. thesis, Technical University of Denmark, Department of Civil Engineeing (2009b)Google Scholar
  16. Nielsen, J.H.: Remaining stress-state and strain-energy in tempered glass fragments. Glass Struct. Eng. 2, 45–56 (2017).  https://doi.org/10.1007/s40940-016-0036-z CrossRefGoogle Scholar
  17. Nielsen, J.H., Olesen, J.F., Poulsen, P.N., Stang, H.: Finite element implementation of a glass tempering model in three dimensions. Comput. Struct. 88(17–18), 963–972 (2010).  https://doi.org/10.1016/j.compstruc.2010.05.004 CrossRefGoogle Scholar
  18. Pourmoghaddam, N., Nielsen, J.H., Schneider, J.: Numerical simulation of residual stresses at holes near edges and corners in tempered glass? A parametric study. In: Engineered Transparency International Conference at Glasstec, pp. 513–525 (2016)Google Scholar
  19. Pourmoghaddam, N., Schneider, J.: Finite-element analysis of the residual stresses in tempered glass plates with holes or cut-outs. Glass Struct. Eng. [Online].  https://doi.org/10.1007/s40940-018-0055-z (2018)
  20. Schneider, J.: Festigkeit und Bemessung punktgelagerter Gläser und stoßbeanspruchter Gläser. Ph.D. thesis, Technische Universität Darmstadt (2001)Google Scholar
  21. Shutov, A.I., Popov, P.B., Bubeev, A.B.: Prediction of the character of tempered glass fracture. Glass Ceram. 55(1–2), 8–10 (1998).  https://doi.org/10.1007/BF03180135 CrossRefGoogle Scholar
  22. Tandon, R., Glass, S.J.: Fracture Mechanics of Ceramics; Active Materials, Nanoscale Materials, Composites, Glass, and Fundamentals, vol. 14, pp. 77–92. Springer, Berlin (2005)Google Scholar
  23. Warren, P.D.: Fragmentation of Thermally Strengthened Glass. Fractography of Glasses and Ceramics IV, pp. 389–402. The American Ceramic Society, Westerville (2001)Google Scholar

Copyright information

© Springer International Publishing AG, part of Springer Nature 2018

Authors and Affiliations

  1. 1.Technical University of DarmstadtDarmstadtGermany

Personalised recommendations