Abstract
Weak light imaging has drawn more and more attention because of its promising potential for practical applications in security monitoring and space exploration. In this work, all-inorganic Cs2AgBiBr6 double perovskite-based self-powered photodetectors containing inorganic copper thiocyanate (CuSCN) as hole-transport layers (HTLs) are successfully fabricated and applied for weak light imaging, which is the first report on the weak light imaging application of all-inorganic lead-free perovskite photodetectors. CuSCN films with favorable optical property and hole extraction capability are prepared via a cost efficient and fast solvent removal method, demonstrating the potential for high-performance perovskite-based devices as transparent components. It is revealed that the band alignment of the device is effectively optimized with the presence of CuSCN HTLs, which can availably transport holes while block electrons at the Cs2AgBiBr6/CuSCN interface, resulting in remarkable improvement of photoresponse performance. The responsivity and detectivity are 0.34 A W−1 and 1.03×1013 Jones, respectively. In particular, the light current has a boost of almost 10 times. Furthermore, the photodetectors are integrated into a self built light detection imaging system uti lizing the focused laser scanning imaging mode. With illumination of as low as 5 nW cm−2 (405 nm), the image involving graphics and words with a size of 5 cm×5 cm can still be distinctly recognized. These results suggest the promising potential of all-inorganic perovskite-based devices for weak light detection and imaging applications.
摘要
弱光成像技术在安全监测、 空间勘探、 医疗成像及通讯领域有着广泛的应用. 光电探测器是弱光成像技术的核心元件, 决定了成像系统的质量. 本工作首次将硫氰酸亚铜(CuSCN)薄膜作为无机空穴传输层(HTLs)与全无机Cs2AgBiBr6双钙钛矿薄膜相结合, 获得了具有优良弱光探测能力的光电探测器. CuSCN薄膜具有优异的空穴提取能力, 可以有效地传输空穴并调节能带排列, 从而减少载流子在Cs2AgBiBr6/CuSCN界面处的复合, 使器件的光电流提升近10倍. 该器件在~1 nW cm−2的弱光下的响应度和探测率分别达到了0.34 A W−1和1.03×1013 Jones. CuSCN薄膜还具有优异的光透过率, 保证了器件的半透明特性. 我们搭建了基于聚焦激光扫描成像模式的弱光成像系统, 并将Cs2AgBiBr6/CuSCN异质结光电探测器集成于该系统中. 采用一幅包含图形和文字的图案(尺寸为5 cm×5 cm)为成像对象. 在低至5 nW cm−2(405 nm)的辐照下, 该系统依然能够输出清晰的图像. 这些研究结果显示了基于Cs2Ag-BiBr6/CuSCN结构的全无机光电探测器在弱光探测和成像领域的巨大潜力.
Article PDF
Similar content being viewed by others
References
Wang L, Jie J, Shao Z, et al. MoS2/Si heterojunction with vertically standing layered structure for ultrafast, high-detectivity, self-driven visible-near infrared photodetectors. Adv Funct Mater, 2015, 25: 2910–2919
Leung SF, Ho KT, Kung PK, et al. A self-powered and flexible organometallic halide perovskite photodetector with very high detectivity. Adv Mater, 2018, 30: 1704611
Zhang Y, Du J, Wu X, et al. Ultrasensitive photodetectors based on island-structured CH3NH3PbI3 thin films. ACS Appl Mater Interfaces, 2015, 7: 21634–21638
Wang A, Fu L, Zhang Y, et al. High-sensitivity photon-counting imaging detector. In: Proceedings of SPIE. Beijing, 2004. 439–442
Ding L, Li YQ, Liu XY, et al. Weak light characteristics of potential biosensor unit. Micro-Nano Lett, 2013, 8: 594–597
Dong Q, Fang Y, Shao Y, et al. Electron-hole diffusion lengths >175 µm in solution-grown CH3NH3PbI3 single crystals. Science, 2015, 347: 967–970
Stranks SD, Eperon GE, Grancini G, et al. Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science, 2013, 342: 341–344
Yang WS, Park BW, Jung EH, et al. Iodide management in formamidinium-lead-halide-based perovskite layers for efficient solar cells. Science, 2017, 356: 1376–1379
Jeon NJ, Na H, Jung EH, et al. A fluorene-terminated holetransporting material for highly efficient and stable perovskite solar cells. Nat Energy, 2018, 3: 682–689
Cho H, Jeong SH, Park MH, et al. Overcoming the electroluminescence efficiency limitations of perovskite light-emitting diodes. Science, 2015, 350: 1222–1225
Lin K, Xing J, Quan LN, et al. Perovskite light-emitting diodes with external quantum efficiency exceeding 20 percent. Nature, 2018, 562: 245–248
Yang T, Zheng Y, Du Z, et al. Superior photodetectors based on all-inorganic perovskite CsPbI3 nanorods with ultrafast response and high stability. ACS Nano, 2018, 12: 1611–1617
Saidaminov MI, Adinolfi V, Comin R, et al. Planar-integrated single-crystalline perovskite photodetectors. Nat Commun, 2015, 6: 8724
Tan Z, Wu Y, Hong H, et al. Two-dimensional (C4H9NH3)2PbBr4 perovskite crystals for high-performance photodetector. J Am Chem Soc, 2016, 138: 16612–16615
Ji C, Wang P, Wu Z, et al. Inch-size single crystal of a lead-free organic-inorganic hybrid perovskite for high-performance photo-detector. Adv Funct Mater, 2018, 28: 1705467
Tong XW, Kong WY, Wang YY, et al. High-performance red-light photodetector based on lead-free bismuth halide perovskite film. ACS Appl Mater Interfaces, 2017, 9: 18977–18985
Zhou J, Luo J, Rong X, et al. Lead-free perovskite derivative Cs2SnCl6−xBrx single crystals for narrowband photodetectors. Adv Opt Mater, 2019, 7: 1900139
Luo J, Li S, Wu H, et al. Cs2AgInCl6 double perovskite single crystals: Parity forbidden transitions and their application for sensitive and fast UV photodetectors. ACS Photonics, 2017, 5: 398–405
Lei LZ, Shi ZF, Li Y, et al. High-efficiency and air-stable photo-detectors based on lead-free double perovskite Cs2AgBiBr6 thin films. J Mater Chem C, 2018, 6: 7982–7988
Wang A, Yan X, Zhang M, et al. Controlled synthesis of lead-free and stable perovskite derivative Cs2SnI6 nanocrystals via a facile hot-injection process. Chem Mater, 2016, 28: 8132–8140
Jung JW, Chueh CC, Jen AKY. High-performance semitransparent perovskite solar cells with 10% power conversion efficiency and 25% average visible transmittance based on transparent CuSCN as the hole-transporting material. Adv Energy Mater, 2015, 5: 1500486
Liu D, Kelly TL. Perovskite solar cells with a planar heterojunction structure prepared using room-temperature solution processing techniques. Nat Photon, 2013, 8: 133–138
Cao J, Wu B, Chen R, et al. Efficient, hysteresis-free, and stable perovskite solar cells with ZnO as electron-transport layer: effect of surface passivation. Adv Mater, 2018, 30: 1705596
Jiang Q, Zhang L, Wang H, et al. Enhanced electron extraction using SnO2 for high-efficiency planar-structure HC(NH2)2PbI3-based perovskite solar cells. Nat Energy, 2016, 2: 16177
Zhou H, Chen Q, Li G, et al. Interface engineering of highly efficient perovskite solar cells. Science, 2014, 345: 542–546
Zhang P, Yu Q, Min X, et al. Fabrication of Cu2ZnSn(S,Se)4 photovoltaic devices with 10% efficiency by optimizing the annealing temperature of precursor films. RSC Adv, 2018, 8: 4119–4124
Arora N, Dar MI, Hinderhofer A, et al. Perovskite solar cells with CuSCN hole extraction layers yield stabilized efficiencies greater than 20%. Science, 2017, 358: 768–771
Qin P, Tanaka S, Ito S, et al. Inorganic hole conductor-based lead halide perovskite solar cells with 12.4% conversion efficiency. Nat Commun, 2014, 5: 3834
Wijeyasinghe N, Regoutz A, Eisner F, et al. Copper(I) thiocyanate (CuSCN) hole-transport layers processed from aqueous precursor solutions and their application in thin-film transistors and highly efficient organic and organometal halide perovskite solar cells. Adv Funct Mater, 2017, 27: 1701818
Zhao Z, Yang H, Zhu Y, et al. Interfacial N-Cu-S coordination mode of CuSCN/C3N4 with enhanced electrocatalytic activity for hydrogen evolution. Nanoscale, 2019, 11: 12938–12945
Jaffe JE, Kaspar TC, Droubay TC, et al. Electronic and defect structures of CuSCN. J Phys Chem C, 2010, 114: 9111–9117
Aldakov D, Chappaz-Gillot C, Salazar R, et al. Properties of electrodeposited CuSCN 2D Layers and nanowires influenced by their mixed domain structure. J Phys Chem C, 2014, 118: 16095–16103
Liang Z, Zeng P, Liu P, et al. Interface engineering to boost photoresponse performance of self-powered, broad-bandwidth PED-OT:PSS/Si heterojunction photodetector. ACS Appl Mater Interfaces, 2016, 8: 19158–19167
Wu C, Du B, Luo W, et al. Highly efficient and stable self-powered ultraviolet and deep-blue photodetector based on Cs2AgBiBr6/SnO2 heterojunction. Adv Opt Mater, 2018, 6: 1800811
Yang J, Bao C, Ning W, et al. Stable, high-sensitivity and fast-response photodetectors based on lead-free Cs2AgBiBr6 double perovskite films. Adv Opt Mater, 2019, 7: 1801732
Li Y, Shi Z, Lei L, et al. Ultrastable lead-free double perovskite photodetectors with imaging capability. Adv Mater Interfaces, 2019, 6: 1900188
Zhou X, Hobbs MJ, White BS, et al. An InGaAlAs-InGaAs two-color photodetector for ratio thermometry. IEEE Trans Electron Devices, 2014, 61: 838–843
Kulkarni M, Gruev V. Integrated spectral-polarization imaging sensor with aluminum nanowire polarization filters. Opt Express, 2012, 20: 22997–23012
Acknowledgements
This work was supported by the National Natural Science Foundation of China (51772135), the Ministry of Education of China (6141A02022516), the Fundamental Research Funds for the Central Universities (11619103), China Postdoctoral Science Foundation (2019M663376), Guangdong Province Higher Vocational Colleges & Schools Pearl River Scholar Funded Scheme (2017), the Natural Science Foundation of Guangdong Province, China (2017A020215135 and 2018A030310659) and the Science and Technology Program of Guangzhou, China (201804010432).
Author information
Authors and Affiliations
Contributions
Author contributions Yan G designed and engineered the device samples and wrote the paper; Ji Z designed and engineered the imaging system; Li Z and Jiang B performed the chemical experiments; Yan G, Kuang M and Cai X accomplished the characterizations; Yuan Y proposed the idea and analyzed the data. This work was guided and supported by Mai W. All authors contributed to the general discussion.
Corresponding authors
Ethics declarations
Conflict of interest The authors declare that they have no conflict of interest.
Additional information
Genghua Yan received her BSc degree in applied physics from Central South University in 2013 and PhD degree in materials physics and chemistry from Sun Yat-Sen University (SYSU) in 2018. She joined the College of Science and Engineering, Jinan University as a postdoctor since the middle of 2018. Her main research interest focuses on advanced thin film materials and photoelectric devices.
Ye Yuan received his BSc degree in optical information science and technology from SYSU in 2013 and PhD degree in materials physics and chemistry from SYSU in 2018. He now is an assistant research fellow at the Department of Physics, Jinan University. His research interests are thin-film photoelectric materials and devices, especially heterojunction photodetectors and solar cells.
Wenjie Mai is a professor as well as head of the Deparment of Physics, Jinan University. He received his BSc degree from Peking University in 2002 and PhD degree from Georgia Institute of Technology (GIT) in 2009. He joined Jinan University in 2009. He was a visiting fellow at GIT from 2012 to 2013. His research areas include photoelectric materials, energy materials and the related flexible devices. He currently focuses on supercapacitors, photodetectors and solar cells.
Supporting Information
Rights and permissions
About this article
Cite this article
Yan, G., Ji, Z., Li, Z. et al. All-inorganic Cs2AgBiBr6/CuSCN-based photodetectors for weak light imaging. Sci. China Mater. 64, 198–208 (2021). https://doi.org/10.1007/s40843-020-1358-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40843-020-1358-5