Investigation of injection molding parameters on the uniformity of porous array of polymer microfluidic chip
- 13 Downloads
The uniformity of the porous array seriously affects the performance of the injection-molded parts. In this study, a uniform hole array chip constituted by 384 holes whose radiuses are 1.30 mm is fabricated by precision injection molding technology. To capture the relevance between the uniform dimension of the porous array and the injection molding process parameters, single factor experiment was adopted. Besides, the condensed state of the hole array was studied to give a further explanation of the inner relationship between the hole array and the most sensitive injection process. As for the measurement, the diameter of the hole which next to the gate and away from the gate was investigated by means of universal tool-measuring microscope, and the standard deviation of the hole diameter was chosen to estimate the uniformity of the hole array. Furthermore, the crystal state and interface state were characterized by polarized light microscopy (PLM), used to explain why the difference of those holes appeared. The results reveal that the impact of process parameters on the uniformity of the hole array was ranked as follows: melt temperature, cooling time, mold temperature, injection pressure, injection speed and packing pressure. Besides, the analysis of the condensed state on different melt temperature indicates that the larger grain size is less favorable to the uniform molding, as the melt temperature increases, the difference of cortical thickness between the dynamic template and fixed template sides decreases, product uniformity is improved.
KeywordsUniformity Porous array Injection molding Single factor experiment Condensed state
The authors gratefully acknowledge the support given by the National Key Research and Development Plan of China under Grant No. 2016YFC1202503.
- 2.Song M, Liu Y (2013) Research on incorporate injection molding of the cover sheet and the substrate sheet for microfluidic chip. Mater Sci Technol 21:13–17Google Scholar
- 6.Hong S-Z (2005) Precision injection molding and factor of mold designing. Die Mould Technol 4:24–33Google Scholar
- 7.ManCang S, Hui Z, Shan LJ (2016) Replication of large scale micro pillar array with different diameters by micro injection molding. Microsyst Technol 10:1007–1016Google Scholar
- 9.Chen X, Leary TF, Maldarelli C (2017) Transport of biomolecules to binding partners displayed on the surface of microbeads arrayed in traps in a microfluidic cell. Biomicrofluidics 11:1–23Google Scholar
- 10.Lee F-W, Hung W-H, Ma C-W, Yang Y-J (2016) Polymer-based disposable microneedle array with insertion assisted by vibratingmotion. Biomicrofluidics 10:1–11Google Scholar
- 13.Lihong N, Xiaohong J, Yaolong Z (2016) Large-area, size-tunable Si nanopillar arrays with enhanced antireflective and plasmonic properties. Nanotechnology 31:1–9Google Scholar
- 14.Wenggang W, Haiyang M, Xiang H (2016) Fabrication and characterization of SiO2/Si heterogeneous nanopillar arrays. Nanotechnology 30:1–9Google Scholar
- 15.Lixia W, Bei W (2003) Research on the influence of process parameters on quality of injection molding products. J Zhengzhou Univ 24:62–66Google Scholar
- 16.Group of Mathematical Statistics in Institutes of China (1977) Analysis of standard deviation. Science Press, Beijing, ChinaGoogle Scholar